Moisture adsorption characteristics of a thin bed of polycrystalline potash pellets: Part I. Experimental study

This study is an experimental investigation of heat and moisture transfer within a packed bed of polycrystalline, porous potash pellets. Experiments were first performed to determine the moisture uptake characteristics on individual pellets subject to a step-change in relative humidity. Then a bed of pellets was subjected to flows of humid air on the upper boundary and a cold impermeable surface on the lower boundary resulting in a temperature gradient across the bed. Temperature and moisture content were measured within the bed. It was found that moisture uptake is less for potash pellets and they are less likely to cake than granular and standard potash when subjected to the same ambient air conditions. This is due to the porous nature of the pellet and its nearly uniform size and spherical shape.     

水泥熟料质量指标的软测量建模研究

针对水泥熟料质量指标的测量,提出一种基于最小二乘支持向量机的软测量建模方法;对于建模数据,提出了基于模糊聚类的数据预处理方法.实验研究表明,该数据预处理方法明显优于传统的拉依达准则方法,能够有效地去除现场测量数据中存在的异常数据;最小二乘支持向量机建模相比于RBF神经网络也具有明显优势,建立的软测量模型对于整个窑系统优化控制具有重要意义.     

小型轴向槽道热管蒸发段的换热系数

通过试验的方法对直径为6mm、长为210mm的小型轴向槽道热管蒸发段换热系数进行研究,并得出计算模型.热管管内工作介质为水,蒸汽饱和温度分别为40℃、50℃和60℃.通过测定,得出在水平工作状况下,热管管内气化换热系数受传输功率.温度差和饱和蒸气压的影响不大.气化形式以蒸发为主.并且通过半理论分析和试验的方法得到在试验条件范围内,热管蒸发段换热系数基本稳定在30 500x(1±25%)W/(m2·℃).     

超支化含苯基聚硅氧烷亲二氧化碳特性及其分子模拟

通过水解缩聚法制备含有不同苯基含量的超支化聚硅氧烷，探究苯基的引入对超支化聚合物在CO2中溶解性能的影响。浊点压力测试得出苯基的引入在超支化结构中对聚合物在CO2中的溶解度影响不大，超支化聚合物中苯基含量的增加没有导致浊点压力的明显升高，有望实现作为CO2增稠剂兼具较好的溶解度和增稠性能。分子模拟计算分析了超支化聚硅氧烷和直链聚硅氧烷与CO2分子间的相互作用以及超支化聚硅氧烷分子间的相互作用，发现含苯基的超支化聚硅氧烷具有更低的内聚能密度（CED）和溶解度参数（δ），表现出更弱的聚合物分子间相互作用，有利于超支化有机硅氧烷在CO2体系中的溶解。     

防止氟化铝母液脱硅工艺中铝、氟消耗方法研究

在氟化铝母液中添加氯化铝等可溶性铝盐,可有效地阻止钠,氟,铝间冰晶石固体物质的形成,从而达到防止氟化铝脱硅工艺中铝,氟的损耗,确保氟硅酸钠的产品质量,同时提高母液利用的经济效益。     

Improving Dewaterability and Other Properties of Citric Acid Wastewater Treatment Sludge by Ozone and Peroxone

ABSTRACT

The efficacies of ozonation and peroxone (O₃/H₂O₂) pretreatments were compared for citric acid wastewater sludge conditioning with the objective of improving dewatering characteristics of the sludge. Treatment with 84 mg O₃/g dry solid (DS) and 12.5 mg/g DS H₂O₂ greatly enhanced the effectiveness of ozonation, providing sludge dewaterability similar to that obtained by ozonation at 250 mg O₃/g DS. Most importantly, treatment of citric acid wastewater sludge with 84 mg O₃/g DS and 12.5 mg/g DS H₂O₂ led to the preservation of the nutrient elements nitrogen, phosphorus, and potassium in the sludge with a minimal volatile suspended solids/total suspended solids reduction of 5.5%, which is much lower than that with ozonation at 250 mg O₃/g DS.     

我国汽车工业对塑料的需求

分析了国内外汽车工业对塑料的市场需求现状与趋势,提出了"十·五"期间塑料在我国汽车领域的应用方向与发展思路.     

N-十六烷基乙二胺二乙酸钠的合成及性能研究

采用大量无水乙二胺与1－Br－十六烷反应合成N－十六烷基乙二胺，然后与过量氯乙酸作用制备N－十六烷基乙二胺二乙酸，用NaOH中和，即得N－十六烷基乙二胺二乙酸钠。该产物在硬水中的差示稳定性为333，优于LAS。在相同测试条件下，产物的去污力高于LAS，发泡力明显低于LAS。     

凝胶法片状莫来石粉的制备及应用

采用拟薄水铝石和非晶态超细SiO_2微粉为原料。以溶胶-凝胶工艺制取莫来石凝胶,通过干燥、煅烧研制得片状结晶莫来石粉。初步研究了凝胶法莫来石粉在钛酸铝陶瓷和烧结刚玉砖中的应用。实验结果表明:凝胶粉起到了促进烧结、降低烧成温度的作用,并使钛酸铝——莫来石复相陶瓷和刚玉砖的强度得到了显著提高。     

改善高吸水树脂性能的主要技术方案

文章介绍了盐的存在对高吸水树脂吸水性能的影响，重点论述了提高高吸水树脂耐盐性、吸水速度和吸水后水凝胶强度的技术方案。