Ca-Mg-Al复合氧化物催化尿素与1,2-丙二醇制碳酸丙烯酯

采用共沉淀法制备了系列Ca-Mg-Al复合氧化物催化剂，通过对沉淀剂配比、沉淀液pH值及焙烧温度等制备条件的考察，得到以Na₂CO₃为沉淀剂、pH=9.5、850℃下焙烧4h制备的Ca-Mg-Al催化活性最高。在 n(PG)∶n(urea)=1.5∶1、反应温度为145℃、绝压20kPa、反应时间4h、催化剂用量为尿素质量的5%时，碳酸丙烯酯收率达到84.6%。采用XRF、XRD、NH₃-TPD、SEM及BET对催化剂的组成、晶型及酸性进行了表征，发现随着沉淀剂中Na₂CO₃的含量增加，催化剂中CaO∶MgO的比例增大，碳酸丙烯酯的收率亦升高；经850℃焙烧后，催化剂中存在CaO和MgO两种活性中心，起协同催化作用；随着焙烧温度由700℃升高到850℃，NH₃-TPD脱附曲线向低温方向偏移，且强酸中心NH₃脱附峰面积比由81.14%明显下降为0，中强酸中心NH₃脱附峰面积比由0增加到78.07%，而碳酸丙烯酯收率由68%增加到84.6%，这表明催化剂强酸性位的减少是催化活性增加的主要原因。     

CAN总线的输送控制系统集成化研究

针对现有技术中输送系统控制不稳定、控制能力低下等问题,本文提出基于工业CAN总线的输送系统集成化控制.在控制系统CAN通信节点利用代码进行数据的转化,通过emit关键字将数据绘制成显示曲线,由输入的代码不断对系统数据进行刷新,实现了输送系统的实时监控,提高了系统运行的安全性.通过时间同步技术将SAEAS6802时钟同步协议与时钟修正算法相结合,有效地对数据处理时间和接收时间进行校正,减少了数据接收误差,提高了时间同步精度.实验结果表明,本文研究方法提高了输送控制系统的运行安全性和可靠性.     

Fluoride-mediately solvothermal synthesis and tunable photocatalytic selectivity of urchin-like ZrO2 hollow microspheres

Photocatalysts often show excellent performances on the basis of their surface state of exposed faces with high reactivity, but unfortunately surfaces of this type are usually concealed into the interior of crystals for their high surface energy. We report here a possibility that for fluorine-terminated surfaces of monoclinic ZrO₂, these higher-energy surfaces could be retained and exposed. Urchin-like ZrO₂ hollow microspheres (UZHS) composed of nanoribbons with exposed (010) facets are obtained through a fluoride mediately solvothermal method. We prove the stabilization effect of fluorine adsorption on (010) facets by density functional theory calculations. More interestingly, UZHS exhibit tunable photocatalytic selectivity in dye degradation. The fluorinated UZHS exhibit good performances both on decomposing Congo red (CR) and methylene blue, while the surface-modified UZHS by calcination only favor decomposition of CR.     

Revisiting the Parallel Strategy for DOACROSS Loops

Journal of Computer Science and Technology - DOACROSS loops are significant parts in many important scientific and engineering applications, which are generally exploited pipeline/wave-front...     

Low-temperature synthesis of SiC nanowires with Ni catalyst

SiC nano wires were fabricated on the silicon substrate dipped with a layer of Ni catalyst at 900 ℃ by gas pressure annealing processing. The morphologies and crystal structures were determined by scanning electron microscopy(SEM), transmission electron microscopy(TEM)and X-ray diffraction(XRD). The results show that the assynthesized nanowires are β-SiC single crystalline with diameter range of 50-100 nm, and length of tens of micron by directly annealing at 900 ℃. The SiC nano wires grow along the [111] direction with highly uniform morphology. And the possible growth mechanism of SiC nano wires is proposed.The present work provides an efficient strategy for the production of high-quality SiC nano wires.     

Fabrication and characterizations of Cr3+-doped ZnGa2O4 transparent ceramics with persistent luminescence

0.5 at.% Cr:ZnGa₂O₄ precursor was synthesized by the co-precipitation method with nitrates as raw materials, using ammonium carbonate as the precipitant. Low-agglomerated Cr:ZnGa₂O₄ powders with an average particle size of 43 nm were obtained by calcining the precursor at 900℃ for 4 h. Using the powders as starting materials, 0.5 at.% Cr:ZnGa₂O₄ ceramics with an average grain size of about 515 nm were prepared by presintering at 1150℃ for 5 h in air and HIP post-treatment at 1100℃ for 3 h under 200 MPa Ar. The in-line transmittance of 0.5 at.% Cr:ZnGa₂O₄ ceramics with a thickness of 1.3 mm reaches 59.5% at the wavelength of 700 nm. The Cr:ZnGa₂O₄ ceramics can be effectively excited by visible light and produce persistent luminescence at 700 nm. For Cr:ZnGa₂O₄ transparent ceramics, the brightness of afterglow was larger than 0.32 mcd/m² after 30 min, which is far superior to that of Cr:ZnGa₂O₄ persistent luminescence powders.