The surface carboxyl group of carbonaceous microspheres effects on the synthesis and structure of SiOC ceramics

In this study, C/SiOC and C/SiO₂ composites were prepared by using carbonaceous microspheres with different surface functional groups. Carbonaceous microspheres based on hydrothermal reaction of glucose contains hydroxyl group, while the surface carboxyl group increases after NaOH etching. The hydroxyl group increases the oxygen-enriched structural units of SiOC ceramics, and the C spheres are closely enwrapped in SiOC matrix after pyrolysis at 900 °C. However, the interfacial reaction of surface carboxyl with Si–OH results in the formation of cristobalite SiO₂, and C spheres are not only encased inside the SiOC matrix, but also dispersed outside of SiOC ceramics. After removal of C via calcination at 500 °C for 5 h, C/SiOC and C/SiO₂ composites are transformed into amorphous SiO₂ and cristobalite SiO₂, respectively. The thermogravimetric analysis indicates the oxidation resistance of SiOC is superior to that of C and SiO₂.     

Novel TiC-based composites with enhanced mechanical properties

Novel TiC-based composites were synthesized by reactive hot-pressing at 1800 °C for 1 h with ZrB₂ addition as a sintering aid for the first time. The effects of ZrB₂ contents on the phase composition, microstructure evolution, and mechanical properties were reported. Based on the reaction and solid solution coupling effects between ZrB₂ and TiC, the product ZrC may be partially or completely dissolved into the TiC matrix, and then phase separation within the miscibility gap is observed to form lamellar nanostructured ZrC-rich (Zr, Ti)C. The TiC-10 mol.% ZrB₂ (starting batch composition) exhibits good comprehensive mechanical properties of hardness 27.7 ± 1.3 GPa, flexural strength 659 ± 48 MPa, and fracture toughness of 6.5 ± 0.6 MPa m^1/2, respectively, which reach or exceed most TiC-based composites using ceramics as sintering aids in the previous reports.     

Spatiotemporal Magnetocaloric Microenvironment for Guiding the Fate of Biodegradable Polymer Implants

The degradation behavior of implants is significantly important for bone repair. However, it is still unprocurable to spatiotemporally regulate the degradation of the implants to match bone ingrowth. In this paper, a magneto-controlled biodegradation model is established to explore the degradation behavior of magnetic scaffolds in a magnetothermal microenvironment generated by an alternating magnetic field (AMF). The results demonstrate that the scaffolds can be heated by magnetic nanoparticles (NPs) under AMF, which dramatically accelerated scaffold degradation. Especially, magnetic NPs modified by oleic acid with a better interface compatibility exhibit a greater heating efficiency to further facilitate the degradation. Furthermore, the molecular dynamics simulations reveal that the enhanced motion correlation between magnetic NPs and polymer matrix can accelerate the energy transfer. As a proof-of-concept, the feasibility of magneto-controlled degradation for implants is demonstrated, and an optimizing strategy for better heating efficiency of nanomaterials is provided, which may have great instructive significance for clinical medicine.     

Scallops as a new source of food protein: high-intensity ultrasonication improved stability of oil-in-water emulsion stabilised by myofibrillar protein

In this study, the effect of high-intensity ultrasound (HIUS) (200 and 400 W for 0, 5, 10 and 15 min respectively) on conformational changes, physicochemical, rheological and emulsifying properties of scallop (Patinopecten yessoensis) myofibrillar protein (SMP) was investigated. HIUS-treated SMP had lower α-helix content and higher β-sheet content compared with the native SMP. HIUS treatment induced the unfolding of SMP and increased the surface hydrophobicity. The particle size of SMP decreased and the absolute zeta-potential increased after ultrasonication, which in turn increased the solubility of SMP. The conformational changes and the improvement of physicochemical properties of SMP increased the ability for SMP to lower the interfacial tension at the oil–water interface and increased the percentage of adsorbed protein. As a result, the emulsifying properties, rheological properties of SMP and storage stability of emulsions were also improved. In conclusion, HIUS treatment has future potential for improving the emulsifying properties of SMP.     

Simultaneous fractionation of multiple classes of polyphenols from honeybush tea using solid-phase extraction

The structural diversity of polyphenols and the inherent limitations of current extraction techniques pose a challenge to extract polyphenols using a simple and green method. Hence, in this study, a method was developed to simultaneously fractionate multiple classes of polyphenols by only varying ethanol-water solutions. Honeybush tea, which is rich in polyphenols, was selected as a model for this study. Solvent extraction followed by solid-phase extraction (SPE) was developed to obtain a polyphenol-rich fraction from six honeybush samples. Based on a gradient elution programme (10%, 30%, 50%, 70% and 90% (v/v) ethanol-water solution) of SPE, the Strata X cartridge showed a better recovery of most targeted polyphenols under 0.9 mL of the drying volume and 1 mL min⁻¹ of the dispensing speed. The elution programme for fractionating most polyphenols was as follows: single elution with 50% ethanol, followed by twice elution with 70% ethanol. The antioxidant capacity was used to analyse the differences among the polyphenol-rich fractions from six honeybush samples. Principal component analysis (PCA) revealed that unfermented C. genistoides (GG) has the greatest antioxidant capacity among the honeybush species studied. Additionally, mangiferin, isomangiferin and vicenin-2 were the main contributors to the antioxidant capacity in six honeybush fractions according to the correlation study.     

农村光棍成因及治理机制研究

以驻村扶贫点滇西南L县X村的光棍为研究对象,侧重个体精准性,强调个体因果性的特征,运用小数据分析该村光棍的贫困特征和生成原因,基于马斯洛需求层次理论探索光棍内生动力激发机制.研究表明:农村光棍趋于年轻化,形势严峻;光棍成因受到外部资源匮乏的限制,又受到自身资源缺陷的制约,内外因相互影响,但外因只有通过内因才能发挥作用.探讨通过需求原理激发光棍群体的内生动力,构建长效治理机制,让光棍群体最大限度实现人生价值,提升社会获得感和幸福感.     

基于蜻蜓翅脉结构的连续碳纤维增强树脂基复合材料仿生设计与增材制造

以具有轻质高强优异性能的蜻蜓翅脉结构为设计灵感，在分析翅脉网格结构抗冲击原理的基础上，设计了传统和仿生两类对比结构。采用熔融挤出3D打印机成功制备了具有不同结构的连续碳纤维增强聚乳酸复合材料试样，并对不同结构复合材料试样的拉伸性能和抗冲击性能进行了测试和对比分析。研究分析结果表明：由于拉伸力方向上的连续碳纤维含量相对较少，限制了仿生结构复合材料抗拉强度的提高，但仿生结构的平均抗拉强度为传统结构的1.18倍；当仿生结构复合材料试样受到冲击力时，其内部六边形结构的连接角度会发生变化，从而极大消耗冲击能量，同时具有六边形网格结构的连续碳纤维可以有效阻碍裂纹的扩展，因此仿生结构的平均冲击韧性可以达到传统结构的2.46倍；仿生蜻蜓翅脉结构可以显著提高增材制造复合材料的综合力学性能，且对于抗冲击性能的提高具体突出效果。连续碳纤维增强树脂基复合材料的有效可行的仿生蜻蜓翅脉结构设计和增材制造，可极大扩展其在高冲击载荷领域中的相应应用。     

Influence of CO2 inleakage on the slight-alkalization of generator internal cooling water

The slight-alkalization of generator internal cooling water (GICW) is widely used to inhibit the corrosion of hollow copper conductor and thereby ensure the safe operation of the generator. CO₂ inleakage is increasingly identified as a potential security risk for GICW system. In this paper, the influence of CO₂ inleakage on the slight-alkalization of GICW was theoretically discussed. Based on the equilibriums of the CO₂-NaOH-H₂O system, CO₂ inleakage saturation was derived to quantify the amount of the dissolved CO₂ in GICW. This parameter can be directly calculated with the measured conductivity and the [Na⁺] of GICW. The influence of CO₂ inleakage on the slight-alkalization conditioning of GICW and the measurement of its water quality parameters were then analyzed. The more severe the inleakage, the narrower the water quality operation ranges of GICW, resulting in the more difficult the slight-alkalization conditioning of GICW. The temperature calibrations of the conductivity and the pH value of GICW show non-linear correlations with the amount of CO₂ inleakage and the NaOH dosage. This study provides insights into the influence of CO₂ inleakage on the slight-alkalization of GICW, which can serve as the theoretical basis for the actual slight-alkalization when CO₂ inleakage occurs.     

Nacre-Inspired,Liquid Metal-Based Ultrasensitive Electronic Skin by Spatially Regulated Cracking Strategy

The realization of liquid metal-based wearable systems will be a milestone toward high-performance, integrated electronic skin. However, despite the revolutionary progress achieved in many other components of electronic skin, liquid metal-based flexible sensors still suffer from poor sensitivity due to the insufficient resistance change of liquid metal to deformation. Herein, a nacre-inspired architecture composed of a biphasic pattern (liquid metal with Cr/Cu underlayer) as “bricks” and strain-sensitive Ag film as “mortar” is developed, which breaks the long-standing sensitivity bottleneck of liquid metal-based electronic skin. With 2 orders of magnitude of sensitivity amplification while maintaining wide (>85%) working range, for the first time, liquid metal-based strain sensors rival the state-of-art counterparts. This liquid metal composite features spatially regulated cracking behavior. On the one hand, hard Cr cells locally modulate the strain distribution, which avoids premature cut-through cracks and prolongs the defect propagation in the adjacent Ag film. On the other hand, the separated liquid metal cells prevent unfavorable continuous liquid-metal paths and create crack-free regions during strain. Demonstrated in diverse scenarios, the proposed design concept may spark more applications of ultrasensitive liquid metal-based electronic skins, and reveals a pathway for sensor development via crack engineering.     

SIL验证与安全仪表系统的优化设计

安全仪表功能(SIF)回路是为了降低特定场景的安全风险而设置的,定级报告中SIF回路的功能描述是工艺设计的完整逻辑要求,包含关键动作及附件动作。安全完整性等级(SIL)验证属于概率学领域研究范畴,影响失效率的因素多且复杂。如果SIL验证无法通过,将造成大量的设计变更,浪费工程投资,影响工期。设计人员应关注SIL定级报告中关键动作的识别、要求平均失效概率以及SIF回路架构的约束。按照文中方法优化测量元件、逻辑控制器、执行元件及辅助元件的设计,可增加通过验证的概率。在没有预验证及安全要求规格书时,可以参考文中典型可通过SIL验证的SIF回路的经验架构进行优化设计,以减少工程变更。