环保型GSF胶结料水化硬化机理研究

GSF胶结料是利用石膏尾矿、高炉矿渣、粉煤灰等工业废渣与少量激发剂混合配制的一种新型胶凝材料。着重研究了GSF胶结料水化动力学特征、水化产物和硬化机理,研究表明GSF胶结料水化硬化机理有别于普通硅酸盐水泥。     

Investigation of Phosphate Cement-based Binder with Super High Early Strength for Repair of Concrete

Magnesium phosphate cement- based binder ( MPB ) for repair of concrete was prepared by proportionally mixing over burned MgO powder ( M) with NHH2 PO4 powder ( P) and set modifying admixtures . It is characteristic by excellent properties such as rapid setting, high strength and high bond strength to old concrete .. The study is focused on the key factors influencing the setting time and strength of MPB, the bond property of MPB to old concrete and the kinetic feature of the hydration of MPB,     

Mg2Si固相反应的热力学评估及工艺优化

固相反应法的引入,是为了解决采用传统方法制备Mg-Si基热电材料过程中带来的Mg的氧化及碳化等问题。从热力学角度对固相反应过程中涉及到的Mg-Si-O-C体系进行了评估,并探讨了制备工艺对材料组成的影响。     

利用石膏尾矿生产新型墙体材料的研究

本文对利用石膏尾矿矿渣等工业废弃物制备建筑砖、砌块等墙体材料的原材料组成、配合比、工艺参数、制品性能进行了试验研究。     

沸石、硅藻土孔结构及调湿性能的研究

调湿材料是能自动调节室内湿度的一种新型多功能材料,本文对两种多孔无机矿物:沸石和硅藻土孔径分布、比表面积以及吸湿、放湿性能进行了实验研究,作出其吸湿及放湿曲线,并分析微观形貌与其调湿性能差异的关系.     

低折射率疏水SiO_2薄膜的制备和表征

为了制备低折射率疏水SiO_2薄膜,将正硅酸乙酯(TEOS)和二甲基二乙氧基硅烷(DDS)在碱性条件下共水解缩聚,再以六甲基二氮硅烷(HMDS)做进一步的改性,采用提拉浸渍工艺在玻璃基底上制备单层增透膜。通过对溶胶粘度随老化时间的变化规律及HMDS添加对薄膜接触角影响等的分析与研究,制备了接触角最大的低折射率薄膜;同时对薄膜的红外特性、透过率、折射率进行了表征。结果表明:TEOS和DDS共水解缩聚提高了膜层疏水性,经HMDS改性后,薄膜的接触角为149°,折射率为1.12。     

Preparation and absorption/desorption performance of gypsum-based humidity controlling materials

Absorption/desorption properties of some humidity controlling materials which contain gypsum as basic cement materials and activated Sepiolite powder as humidity controlling media were tested. The kinetics curve of moisture adsorption/desorption were drawn and humidity controlling performance in nature environment was verified. The experimental results show that moisture absorption/desorption rates are increased, and the speed is also accelerated. These materials, which can adjust environmental humidity effectively, are new ones with good humidity controlling performance.     

改性海泡石粉体的孔结构与调湿性能

用CaCl2溶液改性海泡石粉,研制出一种具有较强吸附能力的调湿材料。用BET吸附测试仪测试样品的孔结构,静态吸附法测试其吸附性能。结果表明:改性后的海泡石粉孔结构发生明显改变,吸、放湿率增大,吸附速度加快,CaCl2的加入量对样品的调湿性能有显著影响。     

环保型GSF胶结材的研究

根据材料化学原理，利用石膏尾矿、高炉矿渣、粉煤灰等工业废渣研究了一种环保型胶凝材料GSF，重点研究了GSF胶结料的配合比等性能，结果表明将磨细的石膏尾矿、矿渣（粉煤灰）、碱性激发剂和早强剂按一定比例混合可以制备出抗压强度超过40MPa的胶结料。     

还原氧化石墨烯对水性无机富锌涂料防腐性能的影响

为提高水性无机富锌涂层的防腐性能，以高模数硅酸钾溶液和氟碳乳液为成膜物质，片状锌粉为主要功能填料，并添加适量还原氧化石墨烯分散液作为辅助填料，制备了硅酸盐水性无机富锌涂料。采用物理性能测试、电化学测试、盐雾试验等测试方法，探究了还原氧化石墨烯添加量对涂层防腐性能的影响。结果表明：加入适量还原氧化石墨烯，可以增强水性无机富锌涂料的防腐性能，当涂料中还原氧化石墨烯分散液添加量达到6%时，涂层的力学性能及耐腐蚀性最佳，经过腐蚀后的主要腐蚀产物为Zn₅(OH)₈Cl₂和ZnO。