Enhanced thermal shrinkage behavior of phenolic-derived carbon aerogel-reinforced by HNTs with superior compressive strength performance

A novel carbon/m-HNTs composite aerogel was synthesized by introducing the modified halloysite nanotubes (m-HNTs) into phenolic (PR) aerogels through chemical grafting, followed with carbonization treatment. In order to explore the best proportion of HNTs to phenolic, the micromorphology of PR/m-HNTs were investigated by SEM before carbonization, confirming 10 wt% of m-HNTs is most beneficial to the porous network of aerogels. The interaction between PR and HNTs was studied by FTIR spectra, and microstructure evolution of the target product-carbon/m-HNTs composite aerogel were illustrated by SEM and TEM techniques. SEM patterns indicated that the carbon/m-HNTs aerogels maintain a stable porous structure at 1000 °C (carbonization temperature), while a ~20 nm carbon layer was formed around m-HNTs generating an integral unit through TEM analysis. Specific surface area and pore size distribution of composite aerogels were analyzed based on mercury intrusion porosimetry and N₂ adsorption–desorption method, the obtained results stayed around 500 m²g^?1 and 1.00 cm³g^?1 (pore volume) without significant discrepancy, compared with pure aerogel, showing the uniformity of pore size. The weight loss rate (26.76%) decreased greatly compared with pure aerogel, at the same time, the best volumetric shrinkage rate was only 30.83%, contributed by the existence of HNTs supporting the neighbor structure to avoid over-shrinking. The highest compressive strength reached to 4.43 MPa, while the data of pure aerogel was only 1.52 MPa, demonstrating the excellent mechanical property of carbon/m-HNTs aerogels.     

深竖井大吨位提升机高比压高摩擦因数衬垫的研制

针对深竖井、大吨位的提升条件下,摩擦衬垫需要高比压和高摩擦因数的难题,在工况分析和参数设计的基础上,研制了比压为2.5 MPa、摩擦因数为0.28的摩擦衬垫,并分别对衬垫的稳定性、抗比压能力、硬度特性、压力特性和磨损情况进行试验.委托第三方检测验证,衬垫的比压试验值达到9.8 MPa,摩擦因数试验值达到0.381,满足实验室的指标要求.     

液滴撞击干燥倾斜壁面铺展实验研究

通过高速摄影技术及像素分析方法对液滴撞击干燥倾斜壁面进行实验研究，分析了不同倾斜角及韦伯数（We）对液滴飞溅及铺展的影响，结果表明，倾斜角的增加有利于抑制飞溅的产生；We一定时，液滴的前铺展因子随着倾斜角的增加而增加，后铺展因子随着倾斜角的增加而减小；液滴的前后初始铺展速度均大于液滴的撞击速度，且随着倾斜角的增加而减小。      

刮板输送机中板仿生耐磨优化试验研究

刮板输送机中板磨损失效已成为输送机运行故障的主要原因之一，为了提高中板耐磨性，基于蜣螂非光滑单元进行了仿生中板设计，以磨损量为响应值，进行了单因素和响应面法优化试验。根据响应面法试验结果得到的因素显著性影响顺序（从高至低）依次为：径向距离，深径比，直径，节距角。基于试验结果建立了磨损量与因素的回归预测模型，经试验对比发现，预测模型与真实试验的相对误差为3.2%。在特定工况（煤散料粒度为6~8 mm、载荷为20 N、刮板链速为0.65 m/s及试验时长为6 600 s）下，当深径比为1.41、直径为0.69 mm、节距角为6.55°和径向距离为4.66 mm时，磨损量最小，仿生中板的耐磨性提高了12.6%。分析其耐磨机理发现，与光滑板相比，仿生板的磨粒磨损及黏着磨损较轻。凹坑分布可破坏持续切削中板表面的煤粒运动状态。中板的仿生优化可为今后刮板输送机的设计提供一定参考。