Investigation of Nanometer- and Submicron-Size Dispersed Phases in Titanium Pseudo- β -Alloys using Scattering and Diffraction of Neutrons,Electrons, and X-Ray Radiation

Metal Science and Heat Treatment - The size and volume fraction of fine particles of secondary β -phase formed during hardening heat treatment of pseudo-β-titanium alloy VT22 are...     

Calorimetric study of ytterbium orthovanadate YbVO4 polycrystalline ceramics

The heat capacity of ytterbium orthovanadate was first measured by adiabatic calorimetry in the temperature range T?=?12.28–344.06?K. No obvious anomalies were observed on the curve obtained. The values of standard thermodynamic functions in the temperature range T?=?0–400 K were calculated. Based on low-temperature calorimetry data obtained, previously published data on the high-temperature heat capacity of ytterbium orthovanadate were corrected. The anomalous contribution to heat capacity for YbVO₄ was compared with the data known for YbPO₄.     

Molten salt synthesis of MAX phases in the Ti-Al-C system

The molten salt method was used to synthesise the MAX phase compounds Ti₂AlC and Ti₃AlC₂ from elemental powders. Between 900–1000?°C, Ti₂AlC was formed alongside ancillary phases TiC and TiAl, which decreased in abundance with increasing synthesis temperature. Changing the stoichiometry and increasing the synthesis temperature to 1300?°C resulted in formation of Ti₃AlC₂ alongside Ti₂AlC and TiC. The type of salt flux used had little effect on the product formation. The reaction pathway for Ti₂AlC was determined to be the initial formation of TiC_1-x templating on the graphite and titanium aluminides.     