Pressure-induced transparency of MgO,Al2O3, AlN,and cBN ceramics at room temperature

The in situ axial X-ray diffraction patterns of four ceramic powder samples (MgO, Al₂O₃, AlN, and cBN) that were compressed in a diamond anvil cell under uniaxial non-hydrostatic conditions were recorded. The microscopic deviatoric stress as a function of the pressure was determined from the X-ray diffraction peak broadening analysis: the curves increased approximately linearly with the pressure at the initial compression stage and then levelled off under further compression. Pressure-induced transparency was observed in all of the samples under compression, and the pressure at the turning point on the curves of the microscopic deviatoric stress versus pressure corresponded to the pressure at which the samples became transparent. Analysis of the microstructural features of the pressure-induced transparent samples indicated that the compression caused the grains to fracture, and the broken grains bonded with each other. We demonstrated that the ceramics’ pressure-induced transparency was a process during which the grains were squeezed and broken, the pores were close between the grains, and the broken grains were re-bonded under compression.     

水杨酸处理诱导采后甜瓜抗坏血酸-还原型谷胱甘肽循环代谢清除过氧化氢的作用及机制

目的：研究抗坏血酸（ascorbic acid，AsA）-还原型谷胱甘肽（reduced glutathione，GSH）循环代谢在水杨酸处理采后甜瓜诱导的过量H2O2清除过程中的作用。方法：用4 mmol/L水杨酸浸泡‘玉金香’厚皮甜瓜10 min，测定处理后果实常温贮藏过程中丙二醛（malondialdehyde，MDA）含量，分析活性氧的积累水平、超氧化物歧化酶（superoxide dismutase，SOD）和过氧化氢酶（catalase，CAT）活力，以及AsA-GSH循环过程相关酶活力及产物和底物含量。结果：水杨酸处理降低了果实MDA含量，第10天处理组MDA含量较对照组降低14.6%；显著提高了果实O2－·的产生速率和H2O2含量（P＜0.05），其中处理后第2天O2－·的产生速率高出同期对照组的1.9 倍，第6天H2O2含量高出对照组果实29.7%；提高了果实SOD活力，但抑制了CAT活力，说明H2O2的清除可能是依赖于除酶促系统外的其他系统。此外，水杨酸处理提高了果实抗坏血酸过氧化物酶、单脱氢抗坏血酸过氧化物酶、脱氢抗坏血酸还原酶和谷胱甘肽还原酶的活力，增加了AsA和氧化型谷胱甘肽的含量，降低了脱氢抗坏血酸和GSH的含量。结论：水杨酸处理诱导了厚皮甜瓜果实的氧爆，抑制了MDA产生，由水杨酸诱导产生的过量H2O2主要依靠AsA-GSH循环系统清除。     

Rheological phase reaction synthesis and electrochemical performance of LiFe2/3Mn1/3PO4/C cathode for lithium-ion batteries

LiFe_2/3Mn_1/3PO₄/C composite was prepared by the rheological phase reaction using LiH₂PO₄, Li₂CO₃, FePO₄, Mn(Ac)₂·4H₂O and ascorbic acid as starting materials. The crystal structure and morphology of as-synthesized sample were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The analysis of XRD results showed that the obtained sample was single-phase with orthorhombic olivine-type structure (Pnma space group). SEM micrographs revealed that the sample was aggregates, with an irregular morphology. The initial discharge capacity was 166.9, 149.1, 139.6, 112.8, 82.93 mAh g^??1 at the rate of 0.1, 0.5, 1, 2, and 10 C, respectively. And when the rate was 0.1, 0.5, 1, 2, and 10 C, the capacity retention was 92.2%, 90%, 92.9%, 97.6%, 91.5% after 50, 100, 200, 200, 500 cycles, respectively.

     

Reducing web latency with coding-based fast multi-path loss recovery

Wireless Networks - TCP latency is critical to the performance of Web services. However, packet loss greatly impairs the TCP performance due to its poor loss recovery mechanisms. Recent work FUSO...     

Synthesis of nanopowders with low agglomeration by elaborating Φ values for producing Gd2O3-MgO nanocomposites with extremely fine grain sizes and high mid-infrared transparency

Refining ceramic microstructures to the nanometric range to minimize light scattering provides an interesting methodology for developing novel optical ceramic materials. In this work, we reported the fabrication and properties of a new nanocomposite optical ceramic of Gd₂O₃-MgO. The citric acid sol-gel combustion method was adopted to fabricate Gd₂O₃-MgO nanocomposites with fine-grain sizes, dense microstructures and homogeneous phase domains. Nanopowders with low agglomeration and improved sinterability can be obtained by elaborating Φ values. Further refining of the microstructure of the nanocomposites was achieved by elaborating the hot-pressing conditions. The sample sintered at 65 MPa and 1300 °C showed a quite high hardness value of 14.3 ± 0.2 GPa, a high transmittance of 80.3 %–84.7 % over the 3?6 μm wavelength range, due mainly to its extremely fine-grain size of Gd₂O₃ and MgO (93 and 78 nm, respectively) and high density.     

An index structure supporting rule activation in pervasive applications

World Wide Web - Rule mechanism has been widely used in many areas, such as databases, artificial intelligent and pervasive computing. In a rule mechanism, rule activation decides which rules are...     

喷油方式对斜齿轮齿面温度的影响

为探讨喷油方式对齿面温度的影响，以斜齿轮为研究对象，通过CFD仿真和试验研究不同喷油方式对斜齿轮齿面温度的影响。针对斜齿轮喷油润滑过程的特点，分析其齿面摩擦生热量，简化轮齿喷油润滑计算模型，并基于CFX进行齿面对流换热仿真研究，得到了不同喷油方式下的齿面温度；基于功率开放式斜齿轮试验平台，对不同喷油方式下的齿面温度进行了试验测量，与仿真计算结果进行对比分析。结果表明：在高速重载斜齿轮传动系统中，啮出侧喷油润滑的方式比啮入侧喷油润滑方式的冷却降温效果要好。     

面向医院建筑项目的IPD模式应用研究

医院建筑项目是非常复杂且具有挑战性的建设项目。传统的交付模式无法满足人们对医院建筑建设、运营方面的高要求,为此开展面向医院建筑项目的IPD模式应用研究。在对IPD模式发展现状整理的基础上,阐述医院建筑项目IPD模式的适用性。分析采用IPD模式的医院建筑项目特点,并以上海市某公立三甲专科医院项目为例,对IPD模式在国内的应用进行探索性研究。     

Synthesis of Ionic Ultramicroporous Polymers for Selective Separation of Acetylene from Ethylene

The design of highly stable and efficient porous materials is essential for developing breakthrough hydrocarbon separation methods based on physisorption to replace currently used energy-intensive distillation/absorption technologies. Efforts to develop advanced porous materials such as zeolites, coordination frameworks, and organic polymers have met with limited success. Here, a new class of ionic ultramicroporous polymers (IUPs) with high-density inorganic anions and narrowly distributed ultramicroporosity is reported, which are synthesized by a facile free-radical polymerization using branched and amphiphilic ionic compounds as reactive monomers. A covalent and ionic dual-crosslinking strategy is proposed to manipulate the pore structure of amorphous polymers at the ultramicroporous scale. The IUPs exhibit exceptional selectivity (286.1–474.4) for separating acetylene from ethylene along with high thermal and water stability, collaboratively demonstrated by gas adsorption isotherms and experimental breakthrough curves. Modeling studies unveil the specific binding sites for acetylene capture as well as the interconnected ultramicroporosity for size sieving. The porosity-engineering protocol used in this work can also be extended to the design of other ultramicroporous materials for the challenging separation of other key gas constituents.