Construction of multifunctional stimuli-responsive nanotherapeutics enabling improved intratumoral penetration of therapeutics and reversal of multiple-drug resistance (MDR) is potent to achieve effective cancer treatment. Herein, we report a general method to synthesize pH-dissociable calcium carbonate (CaCO3) hollow nanoparticles with amorphous CaCO3 as the template, gallic acid (GA) as the organic ligand, and ferrous ions as the metallic center via a one-pot coordination reaction. The obtained GA–Fe@CaCO3 exhibits high loading efficiencies to both oxidized cisplatin prodrug and doxorubicin, yielding drug loaded GA–Fe@CaCO3 nanotherapeutics featured in pH-responsive size shrinkage, drug release, and Fenton catalytic activity. Compared to nonresponsive GA–Fe@silica nanoparticles prepared with silica nanoparticles as the template, such GA–Fe@CaCO3 confers significantly improved intratumoral penetration capacity. Moreover, both types of drug-loaded GA–Fe@CaCO3 nanotherapeutics exhibit synergistic therapeutic efficacies to corresponding MDR cancer cells because of the GA–Fe mediated intracellular oxidative stress amplification that could reduce the efflux of engulfed drugs by impairing the mitochondrial-mediated production of adenosine triphosphate (ATP). As a result, it is found that the doxorubicin loaded GA–Fe@CaCO3 exhibits superior therapeutic effect towards doxorubicin-resistant 4T1 breast tumors via combined chemodynamic and chemo-therapies. This work highlights the preparation of pH-dissociable CaCO3-based nanotherapeutics to enable effective tumor penetration for enhanced treatment of drug-resistant tumors.
Journal of Computer Science and Technology - DOACROSS loops are significant parts in many important scientific and engineering applications, which are generally exploited pipeline/wave-front... 相似文献
SiC nano wires were fabricated on the silicon substrate dipped with a layer of Ni catalyst at 900 ℃ by gas pressure annealing processing. The morphologies and crystal structures were determined by scanning electron microscopy(SEM), transmission electron microscopy(TEM)and X-ray diffraction(XRD). The results show that the assynthesized nanowires are β-SiC single crystalline with diameter range of 50-100 nm, and length of tens of micron by directly annealing at 900 ℃. The SiC nano wires grow along the [111] direction with highly uniform morphology. And the possible growth mechanism of SiC nano wires is proposed.The present work provides an efficient strategy for the production of high-quality SiC nano wires. 相似文献
0.5 at.% Cr:ZnGa2O4 precursor was synthesized by the co-precipitation method with nitrates as raw materials, using ammonium carbonate as the precipitant. Low-agglomerated Cr:ZnGa2O4 powders with an average particle size of 43 nm were obtained by calcining the precursor at 900℃ for 4 h. Using the powders as starting materials, 0.5 at.% Cr:ZnGa2O4 ceramics with an average grain size of about 515 nm were prepared by presintering at 1150℃ for 5 h in air and HIP post-treatment at 1100℃ for 3 h under 200 MPa Ar. The in-line transmittance of 0.5 at.% Cr:ZnGa2O4 ceramics with a thickness of 1.3 mm reaches 59.5% at the wavelength of 700 nm. The Cr:ZnGa2O4 ceramics can be effectively excited by visible light and produce persistent luminescence at 700 nm. For Cr:ZnGa2O4 transparent ceramics, the brightness of afterglow was larger than 0.32 mcd/m2 after 30 min, which is far superior to that of Cr:ZnGa2O4 persistent luminescence powders. 相似文献