对浸矿后离子型稀土原地浸矿场采用清水进行淋洗，在184天的清水淋洗过程中，尾水氨氮值从最开始的507mg/L，降低至140mg/L，淋洗尾水pH4.52~3.10。淋洗尾水采用两级反渗透膜分离，既回收有价资源稀土，又能使出水氨氮达标。结果表明，产水氨氮浓度稳定低于15mg/L，对稀土的截留率高于98.25%，浓水中稀土离子平均浓度313.4mg/L，可进一步回收稀土资源。     

Dual effect synergistically triggered Ce:(Y,Tb)3(Al,Mn)5O12 transparent ceramics enabling a high color-rendering index and excellent thermal stability for white LEDs

Ce:Y₃Al₅O₁₂ transparent ceramics (TCs) with appropriate emission light proportion and high thermal stability are significant to construct white light emitting diode devices with excellent chromaticity parameters. In this work, strategies of controlling crystal-field splitting around Ce³⁺ ion and doping orange-red emitting ion, were adopted to fabricate Ce:(Y,Tb)₃(Al,Mn)₅O₁₂ TCs via vacuum sintering technique. Notably, 85.4 % of the room-temperature luminescence intensity of the TC was retained at 150 °C, and the color rendering index was as high as 79.8. Furthermore, a 12 nm red shift and a 16.2 % increase of full width at half maximum were achieved owing to the synergistic effects of Tb³⁺ and Mn²⁺ ions. By combining TCs with a 460 nm blue chip, a warm white light with a low correlated color temperature of 4155 K was acquired. Meanwhile, the action mechanism of Tb³⁺ ion and the energy transfer between Ce³⁺ and Mn²⁺ ions were verified in prepared TCs.     

Performance analysis of bit error rate of data link system under pulse LFM interference in time-varying rayleigh channel

Wireless Networks - In such mobile platforms as ships and aircraft, the detection and reconnaissance devices are near to the communication facilities. When working at the same time, they will...     

Understanding grain refining and anti Si-poisoning effect in Al-10Si/Al-5Nb-B system

Grain refinement is critical for fabricating high-quality Al-Si casting components in the application of automobile and aerospace industries,while the well-known Si-poisoning effect makes it difficult.Nbbased refiners offer an effective method to refine Al-Si casting alloys,but their anti Si-poisoning capability is far from being understood.In this work,the grain refining mechanism and the anti Si-poisoning effect in the Al-10 Si/Al-5 Nb-B system were systematically investigated by combining transmission electron microscope,first-principles calculations,and thermodynamic calculations.It is revealed that NbB₂provides the main nucleation site in the Al-10 Si ingot inoculated by 0.1 wt.%Nb Al-5 Nb-B refiner.The exposed Nb atoms on the(0001)NbB₂and(1-100)NbB₂surface can be substituted by Al to form(Al,Nb)B₂intermedia layers.In addition,a layer of NbAl₃-like compound(NbAl₃')can cover the surface of NbB₂with the orientation relation of(1-100)[11-20]NbB_2//(110)[110]NbAl₃'.Both of the(Al,Nb)B₂and NbAl₃'intermedia layers contribute to enhancing the nucleation potency of NbB₂particles.These discoveries provide fundamental insight to the grain refining mechanism of the Nb-B based refiners for Al-Si casting alloys and are expected to guide the future development of stronger refiners for Al-Si casting alloys.     

Theoretical study on a kind of cyclization mechanism of boron trichloride and hexamethyldisilazane to form the borazine ring for SiBCN ceramics precursor

Borazine rings act as a pivotal part in siliconboroncarbonitride ceramics (SiBCN) for high-temperature stability and great resistance to crystallization. A detailed investigation of the ring formation mechanism will guide the design and synthesis of SiBCN to meet application requirements under extreme conditions. Boron trichloride (BCl₃) and hexamethyldisilazane (HN(SiMe₃)₂) are common raw materials for the synthesis of precursors for SiBCN. In this paper, quantum chemical calculation was used to study the cyclization reaction mechanism between BCl₃ and HN(SiMe₃)₂ to form trichloroborazine (TCBZ) at the MP2/6-31G (d,p) level of theory. We discussed the structure properties, reaction pathways, energy barriers, reaction rates, and other aspects in detail. The results show that BCl₃ and HN(SiMe₃)₂ alternately participate in the reaction process, accompanied by the release of trimethylchlorosilane (TMCS), and that the entire reaction shows an absolute advantage in terms of energy. In the Step by step reaction, lower reaction barriers are formed due to the introduction of BCl₃ with more heat released compared to that for the introduction of HN(SiMe₃)₂. The final single-molecule cyclization and TMCS elimination steps are found to be faster compared to all previous bimolecular reactions.     

甲玛地区角岩矿微生物浸出的试验研究

介绍了西藏华泰龙矿业开发有限公司角岩的矿石性质,针对该低品位铜矿石进行了详细的微生物浸出试验研究,在原矿铜品位仅为0.12%、SiO_2含量高达69.12%的情况下,用接种量为10%的浸矿菌液,浸出1 d时,铜浸出率即为34.44%,浸出11 d时,浸出率达到70.02%,此时较无菌条件下的浸出率高出17.46个百分点。     

基于学习进程的学习评估在大学化学教学中的实践

高等教育质量提升的关键在于课程教学质量的不断完善。作为高等教育的重要环节,化学课程教学在非化学化工专业人才的知识体系构建、能力培养、素质养成方面有着不可或缺的作用。大学化学课程的教学实践表明,基于学习进程的评估有利于激发学生的学习积极性,显著提高教学班的整体成绩并实现课程教学质量的提升。     

Characterizations of friction welding joint interface for AISI 316

Because of heat amount is different from peripheral to central of friction welding interface, which is leaded to vary the characterizations along that interface. Current study, respectively, focused on the effect of different friction pressure on micro-structural and mechanical properties of that friction welding joint interface. Presently, these friction pressures are 110, 130, 150 and 170 MPa while kept all other conditions constant. The effects of different friction pressure on welding interface characterization were investigated by EDX, SEM, tensile, compression, impact and hardness tests. The tensile tests carried out on the standardized test piece with diameter 6 mm and 8 mm, thus, compression tests were extracted from the positions of 0°, 45° 90° with test specimen of 4 mm diameter and 6.5 mm length at weld center. Whereas, the impact test pieces were picked up in two positions, the first one is symmetrical, which it obtained to the respect of the rotation axis and the interface, on the other hand, the second one is non-symmetrical with the axis of rotation and symmetrical to the interface, for making the notch head coincide with the center of the welded joint, The obtained results showed that with reducing of friction pressure will present lack of bonding increasing from peripheral toward the welding center, which will responsible on reducing of the mechanical properties such as tensile, compression and impact strength.     

基于材料力学性能的最低设计金属温度曲线分析

铁素体钢在低温条件下存在明显的韧脆转变现象。为防止脆断事故的发生,需要确定铁素体钢制压力容器的最低使用温度。针对ASME中的A^D四条冲击豁免曲线,对应地选取了4种材料,基于材料实际的屈服强度和参考温度,按照ASME中豁免曲线的计算方法,计算得到4种材料的最低设计金属温度曲线,并与对应的A^D曲线对比,定量地分析ASME中豁免曲线的保守性。结果表明,ASME中的豁免曲线相对于材料自身的最低设计金属温度曲线保守性较大;韧性相近的材料被划分到不同的豁免曲线,使得韧性富裕量差异较大,对于某些材料,其断裂韧性被低估。