15CrMoG钢棒材表面缺陷机理分析和工艺改进

分析得出,棒材表面细小纵裂纹和表面裂口缺陷产生于铸坯加热之前,且与结晶器弯月面保护渣有关。利用Thermo-Calc热力学软件计算15CrMoG钢凝固相变过程,结合亚包晶钢连铸凝固特点综合分析15CrMoG钢棒材表面缺陷的产生原因和产生机理。结果表明:15CrMoG钢在固相线温度附近发生包晶反应L+δ→γ和包晶转变δ→γ,不仅导致初生坯壳生长不均匀,而且加剧P、S元素在凝固前沿的偏析。而初生坯壳不均匀是导致棒材表面缺陷根本原因。棒材表面细小纵裂纹产生于结晶器内坯壳薄弱处,经过二冷和轧制工序在夹杂物和硫偏聚处扩展长大。棒材表面裂口缺陷是初生坯壳不均匀导致结晶器内液面波动大,造成铸坯夹渣所致。通过控制[C]0.16%～0.17%、[S]≤0.005%、保护渣碱度1.2、熔点≥1200℃、粘度≥1.0Pa·s,260 mm×30mm铸坯水量150 m³/h,拉速0.5 m/min等措施,裂纹合格探伤合格率由原45%提高至98%。     

Effect of an abrupt change in pulling rate on microstructures of directionally solidified Al2O3-Er3Al5O12 eutectic and off-eutectic composite ceramics

Directionally solidified microstructures of Al₂O₃-Er₃Al₅O₁₂ eutectic and off-eutectic in situ composite ceramics were explored under abrupt-change pulling rate conditions. Corresponding temperature distributions and interface locations were studied. In eutectic composition, fluctuation of eutectic spacing occurred when the pulling rate increased abruptly. A gradually increase or abrupt increase in eutectic spacing was observed when the pulling rate decreased abruptly. In hypoeutectic and hypereutectic compositions, formation of the primary phases were suppressed when the pulling rate increased abruptly from 10?µm/s to 100?µm/s, while primary phases precipitated when the pulling rate decreased abruptly from 100?µm/s to 10?µm/s. The interface altitude decreased after the pulling rate increased abruptly, but increased after the pulling rate decreased abruptly. The liquid composition restriction (around the eutectic composition) at the eutectic interface plays an important role in the suppression of the primary dendrite and coupled eutectic oxides can be obtained in off-eutectic compositions even under higher solidification rate conditions.     

A method for rapidly evaluating reliability and predicting remaining useful life using two-dimensional convolutional neural network with signal conversion

Journal of Mechanical Science and Technology - Real-time monitoring and rapid evaluation of bearing operating conditions, especially for the reliability evaluation and remaining useful life (RUL)...     

高强不锈钢绞线网与ECC黏结-滑移关系模型

高强不锈钢绞线网与ECC的黏结是二者协同工作的基础，且黏结 滑移关系模型是其黏结性能的综合反映，故通过对17组51个高强不锈钢绞网增强ECC薄板试件进行单边拉拔试验，研究横向钢绞线间距、纵向钢绞线直径和相对锚固长度等因素对钢绞线网在ECC中黏结性能的影响规律。试验结果表明，横向钢绞线的设置可使黏结破坏由脆性破坏转变为延性破坏；高强不锈钢绞线网与ECC的黏结滑移曲线可分为5个阶段，分别为上升段、微降段、延性强化段、下降段和残余段。基于试验结果，对钢绞线网在ECC中的黏结破坏特征和黏结 滑移机理进行分析，在相关黏结-滑移关系模型的基础上，提出钢绞线网与ECC的黏结 滑移关系模型，并进行模型参数分析。所提模型及模型参数计算公式与试验结果吻合良好，能较好地反映钢绞线网与ECC的界面黏结滑移特征。     

Semantic word shifts in a scientific domain

Understanding semantic word shifts in scientific domains is essential for facilitating interdisciplinary communication. Using a data set of published papers in the field of information retrieval (IR), this paper studies the semantic shifts of words in IR based on mining per-word topic distribution over time. We propose that semantic word shifts not only occur over time, but also over topics. The shifts are examined from two perspectives, the topic-level and the context-level. According to the over-time word-topic distribution, stable words and unstable words are recognized. The diverging and converging trends in the unstable type reveal characteristics of the topic evolution process. The context-level shifts are further detected by similarities between word vectors. Our work associates semantic word shifts with the evolving of topics, which facilitates a better understanding of semantic word shifts from both topics and contexts.     

03Cr18NiMoN节镍双相不锈钢的热变形行为及热加工图

关键词：双相不锈钢； 流变曲线； 本构方程； 热加工图     

基于DoG检测图像特征点的快速二进制描述子

针对SIFT描述子实时性差和传统二进制描述子对尺度、旋转和视角变化鲁棒性差的问题,本文通过优化采样模式和添加灰度差分不变量比较测试进行改进,提出了一种鲁棒性更高的二进制描述子。首先,设计了一种尺度关联、编号标记的采样模式;然后,旋转采样模式中各采样点到特定位置,确保描述子尺度、旋转不变性;接着,分析了采样点点对模式对描述子的影响,选择使用机器学习训练后的128对采样点对;最后,选择灰度值比较测试及梯度绝对值和比较测试构建二进制描述子。实验中采用DoG检测图像关键点,结果表明:本文提出的描述子在描述子构建和描述子匹配上比SIFT描述子分别快84%和67%;在有视角变化的图像匹配上,准确率比传统的二进制描述子高3%~5%,召回率平均要高30%以上。本文提出的特征点描述方法适用于时间要求高的图像匹配领域。