Sodium-ion batteries (SIBs) and potassium-ion batteries (PIBs) have been considered as attractive alternatives for next-generation battery systems, which have promising application potential due to their earth abundance of potassium and sodium, high capacity and suitable working potential, however, the design and application of bi-functional high-performance anode still remain a great challenge up to date. Bismuth sulfide is suitable as anode owing to its unique laminar structure with relatively large interlayer distance to accommodate larger radius ions, high theoretical capacity and high volumetric capacity etc. In this study, dandelion-like Bi2S3/rGO hierarchical microspheres as anode material for PIBs displayed reversible capacity, and 206.91 mAh·g−1 could be remained after 1,200 cycles at a current density of 100 mA·g−1. When applied as anode materials for SIBs, 300 mAh·g−1 could be retained after 300 cycles at 2 A·g−1 and its initial Coulombic efficiency is as high as 97.43%. Even at high current density of 10 A·g−1, 120.3 mAh·g−1 could be preserved after 3,400 cycles. The Na3V2(PO4)3@rGO//Bi2S3/rGO sodium ion full cells were successfully assembled which displays stable performance after 60 cycles at 100 mA·g−1. The above results demonstrate that Bi2S3/rGO has application potential as high performance bi-functional anode for PIBs and SIBs.
AbstractGraphene oxide (GO) was functionalized by polyether amine (PEA) via two methods which were one-pot modification in acetone (GON) and two steps with the intermediate product of GOCO-Cl generated (GONS). There were more PEA successfully grafted onto GO for GONS than GON. The onset polymerization temperatures of the benzoxazine (Bz) composites decreased by the inclusion of 1?wt% of GO, GON or GONS. Thermal stability of the polybenzoxazine (PBz) composites was significantly improved indicated from the increase of weight loss temperature. T10, T20 and T50 values of the composites with GONS were higher than that of the others. Toughness of PBzs may be enhanced by the incorporation of nanofillers, and GONS had stronger interfacial interaction with PBz matrix than GON. 相似文献