Effects of sintering pressure and temperature on microstructure and tribological characteristic of Cu-based aircraft brake material

A novel Cu-based P/M aircraft brake material was prepared and the effects of sintering pressure and temperature on microstructure and tribological characteristic were investigated. For the constant sintering temperature, when the sintering pressure increases from 0.5 MPa to 1.5 MPa, the porosity, wear loss and friction coefficient decrease remarkably. When the sintering pressure increases from 1.5 MPa to 2.5 MPa, the porosity further decreases but in a little degree and wear behaviors are improved slightly. However, once the sintering pressure is larger than 2.5 MPa, it has no obvious effect on microstructure and tribological characteristic. For the constant sintering pressure, when the sintering temperature increases from 900 ℃ to 930 ℃, the sintered density remarkably-increases, and wear behaviors are obviously improved. For further increasing sintering temperature to l 000 ℃, the density keeps on increasing, but wear behaviors change slightly.     

计算Fe-C-Xi合金系在正平衡和准平衡模式下γ→α相变驱动力的简便方法

根据Fe—C-Xi合金系的正平衡和准平衡热力学模型，推导了简便的奥氏体-铁素体相变驱动力计算解析式．根据公式，代入合金原始成分和Ae3温度，即可准确计算正平衡和准平衡模式下的奥氏体-铁素体相变驱动力．采用这一方法计算了Fe-C—Mn—Si—Ni—Or—Mo—Cu八元系的正平衡和准平衡奥氏体-铁素体相变驱动力．     

Windows NT/2000/XP环境下访问底层I/O端口的方法

不同于Windows 9x/ME操作系统,Windows NT/2000/XP对硬件实现了屏蔽,对I/O端口实行了严格控制,用户不能对底层I/O端口进行直接访问.论文基于利用PortTalk驱动,开发了对I/O端口直接访问的动态链接库,从而成功解决应用软件访问底层物理端口的问题,并用实例说明了该动态库的调用方法.     

Filling and solidification of TiAl melt in centrifugal field

A model was established based on the combination of the equation of continuity, the equation of conservation of momentum and the equation of general energy to describe the filling and solidification of TiAl melt by permanent mold centrifugal casting. The model was solved numerically and the filling and solidification processes in the centrifugal field were discussed. The results indicate that the centrifugal field essentially influences the filling and solidification processes of TiAl melt. The melt will first fill the cavity along the back boundary until it reaches the end. After the end is fully filled, the whole cavity will be filled gradually by the way that free surface of the melt moves towards the entrance, hence the entrance is the last part to be filled. Furthermore, the mechanism by which internal defects can be formed in centrifugally cast TiAl components were interpreted.     

HG70钢的焊接性分析

从焊接结合性能和焊接使用性能两方面对HG70钢的焊接性进行了系统地研究。在拘束焊接条件下，采用E6015-DI型焊条，试验钢板的冷裂纹率为零，说明焊接结合性能良好。焊接接头的拉伸、硬度和冲击韧性试验结果表明，粗晶区的硬度高而韧性低，回火区的强度低，细晶区具有良好的综合力学性能。微观组织分析结果表明，焊接接头形成了马氏体、粒状贝氏体、粒状组织等多种形态的组织。结合组织特点及其分布，对焊接接头的力学性能进行了讨论。     

304不锈钢精铸件点缺陷的形成与控制

针对典型304不锈钢精密铸件内出现的黑色点缺陷,对其表面形貌、成分进行了分析,并在此基础上总结了缺陷的形成机制,确定了相应的防止措施。研究结果表明,铸件内的点缺陷可以划分为两类:一类具有不规则截面,为脱蜡过程中剩余腊料的燃烧残留物;另一类为熔炼过程中,由于脱氧剂和除渣剂的去除不彻底而引入的夹杂。通过优化脱蜡和熔炼工艺,使得铸件内的点缺陷得到了很好的控制。     

艺术铸件冷冻冰模制模方法的研究

艺术铸件是艺术创作和铸造技术的完美组合，铸造工艺是艺术思想的重要保证。从古至今，艺术家和铸造工作者进行了不懈的探索。本文通过试验，分析了冷冻铸造方法用于艺术铸造的一些优势，探讨了用硅橡胶模具制作冰模的工艺方法，并将用此工艺成功制作的一些冰模展示出来。     

ITO和ZnO基底对电化学沉积氧化亚铜薄膜的形貌、结构的影响及作用机制

采用电化学恒电位沉积方法在ITO导电玻璃上和在ZnO薄膜上沉积氧化亚铜（Cu2O），并通过X射线衍射（XRD）和扫描电镜（SEM）对晶体的微观结构和表面形貌进行了分析．在ZnO基底上沉积得到了纳米级的Cu2O粒子并且具有明显择优取向，而在ITO导电玻璃上仅得到粒径为2—5胛的Cu2O粒子，没有明显的择优取向，对薄膜的生长机理进行了讨论．     

磷渣对硅酸盐水泥凝结时间的影响及机理