Double emulsion (W/O/W) gel stabilised by polyglycerol polyricinoleate and calcium caseinate as mangiferin carrier: insights on formulation and stability properties

Mangiferin (MGF) is a phenolic compound isolated from mango, but its poor solubility significantly limits its use. In this study, MGF was embedded into the inner aqueous phase of W₁/O/W₂ emulsions. Firstly, the dissolution method of MGF was determined. MGF remained stable in solution with pH 13 at 30 min, and its solubility reached 10 mg mL⁻¹. When the pH of MGF solutions was adjusted from pH 13 to pH 6, MGF did not immediately crystallise, providing sufficient time to construct the MGF-loaded W₁/O/W₂ emulsions. Subsequently, the MGF-loaded W₁/O/W₂ emulsions were constructed using polyglycerol polyricinoleate (PGPR) and calcium caseinate (CAS). The formation and stability of the W₁/O/W₂ emulsions were investigated. The MGF-loaded W₁/O/W₂ emulsions stabilised with 1% PGPR and 1% – 3% CAS exhibited a low viscosity, limited loading capacity, and poor stability. Conversely, the MGF-loaded W₁/O/W₂ emulsions stabilised by 3%PGPR–3%CAS exhibited optimal loading capacity (encapsulation efficiency = 95.31% and loading efficiency = 0.91%) and stability, which was attributed to the fact that high viscosity and gel state retarded the migration of inner aqueous phase. These results indicated that the W₁/O/W₂ emulsions stabilised by PGPR and CAS may be a potential alternative for encapsulating mangiferin.     

Application of big data language recognition technology and GPU parallel computing in English teaching visualization system

International Journal of Speech Technology - With the development of multimedia technology and network technology applications, it is possible to implement online teaching systems in schools. This...     

Alkylated lignin with graft copolymerization for enhancing toughness of PLA

Journal of Materials Science - A green modification method for effectively enhancing toughness of PLA was established. Herein, alkaline lignin (LG) was firstly alkylated with dodecane, and then...     

Substrate temperature-controlled precursor reaction mechanism of PEALD-deposited MoOx thin films

Journal of Materials Science - Molybdenum oxide (MoOx) films had been grown by using plasma-enhanced atomic layer deposition (PEALD) with Mo(CO)6 precursor and O2 plasma reactant in a substrate...     

Fabrication of barium titanate ceramics via digital light processing 3D printing by using high refractive index monomer

A digital light processing (DLP) technology has been developed for 3D printing lead-free barium titanate (BTO) piezoelectric ceramics. By comparing the curing and rheological properties of slurries with different photosensitive monomer, a high refractive index monomer acryloyl morpholine (ACMO) was chosen, and a design and preparation method of BTO slurry with high solid content, low viscosity and high curing ability was proposed. By further selecting the printing parameters, the single-layer exposure time was reduced and the forming efficiency has been greatly improved. Sintered specimens were obtained after a nitrogen-air double-step debinding and furnace sintering process, and the BTO ceramics fabricated with 80 wt% slurry shows the highest relative density (95.32 %) and piezoelectric constant (168.1 pC/N). Furthermore, complex-structured BTO ceramics were prepared, impregnated by epoxy resin and finally assembly made into hydrophones, which has significance for the future design and manufacture of piezoelectric ceramic-based composites that used in functional devices.     

Porous Co3O4 column as a high-performance Lithium anode material

Journal of Porous Materials - Co3O4 has been widely investigated as a promising candidate anode material for lithium-ion batteries. We report on the porous Co3O4 column synthesized via a simple...     

Facile preparation and strong adhesive strength of honeycomb polyurethane films with small pore diameter

With the continuous development of bionics, such as, geckos and virginia creeper with both superhydrophobic and super-adhesive, the surface wetting and super-adhesive properties of various porous materials have attracted extensive attention of the scientific and medical communities. Here, the honeycomb polyurethane (PU) porous films with strong adhesion were successfully prepared by microphase separation method and the effects of growth parameters on their microstructure and adhesive strength to ice were investigated. It was found that a high relative humidity (e.g., 100%) and a low solution concentration (e.g., 2%) facilitated the formation of ordered honeycomb PU porous films, and as-prepared PU pores with average pore diameter as small as 5 μm are better ordered and more uniform than these in related documents. Although the contact angle of water droplets on the surface of PU porous films increased from the premodification value of 85–130° to more than 160° after surface modification with polydopamine (PDA), the corresponding rolling angle remained approximately constant (180°), indicating that the surface of PU porous films has strong adhesion similar to geckos and virginia creeper. Furthermore, at lower temperature, the PU porous films exhibited the high adhesive strength of 142.13 kPa on ice, which was strongly dependent on the porous microstructures and surface compositions. The improved adhesive behavior to ice of honeycomb PU porous films modified with PDA provides new strategies for surface modification of materials and potential applications in medical domain.     

近源成藏——来自鄂尔多斯盆地延长组湖盆东部“边缘”延长组6段原油的地球化学证据

延安以东和以北的鄂尔多斯盆地东北部地区曾被认为位处三叠纪延长组7段（长7段）沉积期古湖盆的"边缘"，一些学者认为该区延长组烃源岩不发育，因而其油藏原油系湖盆中心生成的原油经长距离侧向运移而来；但也有研究认为，包括盆地边缘在内的整个鄂尔多斯盆地致密油藏均为近源成藏。为明确盆地东部地区延长组原油来源，对三叠纪湖盆"东缘"七里村油田的主力油层延长组6段（长6段）原油开展了原油地球化学和油源对比研究。七里村油田长6段原油具有高饱和烃、高饱芳比、低非烃和低沥青质的特征，正构烷烃呈前高单峰型，主峰碳为C₁₉，生物标志化合物分析显示长6段原油为同源成熟原油，生油母质以藻类等低等水生生物为主，混有陆源高等植物，母源沉积环境为偏还原性的淡水湖泊。七里村油田长6段原油与本地区长7段黑色泥页岩和暗色泥岩2种烃源岩均具有明显亲缘关系，而与志丹、富县等湖盆中心地区的长7段烃源岩在族组成、生物标志化合物和稳定碳同位素特征上均存在明显区别。综合分析认为七里村油田长6段原油并非湖盆中心长7段优质烃源岩所生油气经长距离运移而来，而主要为原位长7段烃源岩生成的原油经垂向运移和短距离侧向运移在长6段等储层中聚集成藏，属于近源成藏。