Changes in the content and antioxidative activity of β-carotene and its metabolite vitamin A during gastrointestinal digestion and absorption and optimisation of HPLC-based detection

The β-Carotene (BC), an important precursor of vitamin A (VA), possesses antioxidant activity but is fat-soluble and has low bioavailability. In previous in-vitro assays evaluating antioxidant and 2,2′-azobis(2-amidinopropane) dihydrochloride (AAPH) free radical scavenging, both BC and VA showed a strong ability to scavenge radicals and protected cells from oxidative stress. Here, we used artificially simulated gastrointestinal digestion and Caco-2 cell absorption models to evaluate the bioavailability of the BC during gastrointestinal digestion and absorption using high-performance liquid chromatography (HPLC) analysis. We observed high absorptive and transfer rates of BC and detected retinol metabolites (Vitamin A). Therefore, BC can be detected in the acidic gastrointestinal environment using HPLC. Optimised method provided better separation of BC and VA in the column, improving the accuracy of the test results.     

Sealing behaviour of glass-based composites for oxygen transport membranes

In this study, seven different filler materials in different proportions were added to a Ba-Ca-Si glass matrix “H” to investigate new sealant with higher thermal expansion coefficient (CTE) value and good sealing performance for application in oxygen transport membrane (OTM). SrTi_0.75Fe_0.25O_3-δ (STF25) was used as an OTM, and the sealing partners were ferritic steel Aluchrom and pre-oxidized Aluchrom. Compatibility tests were carried out to investigate the feasibility of the composites. Higher CTE values were found in dilatometer tests on composite samples by adding 40 wt% Ag (HAg40) and 30 wt% Ni-Cr (HNC30). Gas-tightness measurements of sandwiched samples produced appropriate helium leakage rates in the range of 10^?6 mbar·l·s^?1. Sealing behaviour of sealants HAg40 and HNC30 were investigated by joining STF25 and as-delivered/pre-oxidized Aluchrom together. Scanning electron microscopy (SEM) on cross-sections of the joints revealed a homogeneous microstructure and good adherence of the glass sealants to support metals and STF25.     

Self-healing,elastic and deformable novel composite phase change polymer based on thermoplastic elastomer SEBS for wearable devices

Journal of Materials Science - Form-stable composite phase change materials (C-PCMs) prepared by microencapsulation method and porous matrix adsorption method need for compression molding after...     

Simultaneous improvement of thermal conductivity and mechanical properties for mechanically mixed ABS/h-BN composites by using small amounts of hyperbranched polymer additives

Recently, thermal interface materials (TIMs) are in great demands for modern electronics. For mechanically mixed polymer composite TIMs, the thermal conductivity and the mechanical properties are generally lower than expected values due to the sharply increased viscosity and poor filler dispersion. This work shows that addition of a small amount of polyester-based hyperbranched polymer (HBP) avoided the trade-off in mechanically mixed ABS/hexagonal boron nitride (h-BN) composites. After adding 0.5 wt% HBP, the maximum h-BN content in the composites increased from 50 to 60 wt%. The out-of-plane, in-plane thermal conductivity, and tensile strength of ABS/h-BN with 50 wt% h-BN were 0.408, 0.517 W/mK, and 18 MPa, respectively, and were increased to 0.729, 0.847 W/mK, and 32 MPa by adding 0.5 wt% HBP, while 0.972, 1.12 W/mK, and 29.5 MPa were achieved for ABS/h-BN/HBP with 60 wt% h-BN. The morphological and rheological results proved that these enhancements are due to the improved h-BN dispersion by decreasing viscosity of composites during mixing. Theoretical modeling based on the modified effective medium theory confirmed such results and showed that the interfacial thermal resistance also decreased slightly. Thus, this work demonstrates a facile and scalable method for simultaneously improving the thermal conductivity and mechanical properties of thermoplastic-based TIMs.     

Synthesis,characterization and antifungal property of Ti3C2Tx MXene nanosheets

Although the antibacterial properties of MXene nanosheets containing Ti₃C₂T_x are known, their antifungal properties have not been well studied. Herein, we present for the first time a report on the antifungal properties of Ti₃C₂T_x MXene. The Ti₃C₂T_x MXene was obtained by first exfoliating MAX phase of Ti₃AlC₂ with concentrated hydrofluoric acid, then the Ti₃C₂T_x was intercalated and deliminated by ethanol treatment and ultrasonication process. The delaminated Ti₃C₂T_x MXene nanosheets (d-Ti₃C₂Tx) were characterized using field emission scanning electron microscopy (FE-SEM), energy dispersive X-ray (EDX), X-ray diffraction spectroscopy (XRD), and Raman spectroscopy. It was found that Ti₃C₂T_x MXene was characterized by lamellar structure alternating with layers of Ti, Al and C. The EDX results revealed that the delaminated Ti₃C₂T_x MXene nanosheets were composed of Ti, C, Si, O, F, and a trace amount of Al. The XRD and Raman spectra further indicated the elimination of Al and the formation of two-dimensional Ti₃C₂T_x MXene nanosheets. The antifungal activity of the delaminated Ti₃C₂T_x MXene was determined against Trichoderma reesei using the modified agar disc method. Observation using inverted phase contrastmicroscopy revealed inhibited fungus growth with the absence of hyphae around the discs treated wtih MXene. The surrounding of the control groups without an inclusion of MXene was found with large number of hyphae and spores. In addition, the spores of the fungi treated with the samples containing d-Ti₃C₂T_x MXene nanosheets did not germinate even after 11 days of culture. The results demonstrated disruption to the hemispheric structural formation of fungi colony, inhibition of hyphae growth and cell damage for fungi grown on the d-Ti₃C₂T_x MXene nanosheets. These new findings suggest that d-Ti₃C₂T_x MXene nanosheets developed in this work could be a promising anti-fungi material.     

The improvement of the self-healing ability of MoSi2 coatings at 900–1200 °C by introducing SiB6

The brittleness of MoSi₂ ceramic and the thermal mismatch between MoSi₂ coating and C / C composite lead to brittle cracking of the coating at 900−1200 °C. This problem has been overcome in this studyby introducing submicron-SiB₆ into the coating. The pre-fabricated cracks and a kinetics model of hot-pressed SiB₆-MoSi₂ ceramic could quantitatively predict the glass growth and crack healing. As expected, enhancing temperature and SiB₆ content increased the growth rate of the borosilicate glass and the crack healing ability of MoSi₂ ceramic, which was ascribed to the lower oxidation activation energy and larger specific surface area of submicron-SiB₆. For the plasma sprayed coating, SiB₆ with submicron structure was benefit for cracking inhibition and formation of borosilicate glass during oxidation, reducing the oxygen permeability and the consumption of inner coating. Hence, the 15 % SiB₆-MoSi₂ coatings raised the protection times to 84 and 120 h at 900 and 1200 °C respectively, presenting favorable oxidation protective performance.     

稀土石膏常压酸化法制备硫酸钙晶须的研究

以含稀土的石膏为原料运用常压酸化法合成硫酸钙晶须,探讨了不同工艺条件对生成的硫酸钙晶须形貌的影响,同时还考察了晶型助长剂的种类和晶型助长剂的含量对硫酸钙晶须生长的影响,利用SEM和XRD分别对硫酸钙晶须的表面形貌、物相特征做了表征分析。实验得到制备硫酸钙晶须的最佳的反应条件：稀土石膏质量浓度为0.22 g/mL、反应时间为25 min、盐酸浓度为2.8 mol/L、反应温度为70 ℃、陈化时间为4 h,在此条件下合成的硫酸钙晶须平均长度为61 μm,平均长径比为30.5;通过对比实验选出了CuCl₂作为促进硫酸钙晶须生长的助长剂,在添加5%（质量分数）的CuCl₂的情况下可使硫酸钙晶须长径比从30.5增至41,长度从61 μm增至81 μm。     

Fabrication and properties of Si3N4 based ceramics using combustion synthesized powders

Silicon nitride (Si₃N₄) based ceramics were fabricated with β-SiAlON and Si₃N₄ powders synthesized by combustion synthesis method via power injection molding (PIM). In the PIM process, the solids loading for each material was first determined from the results of the torque rheometer experiment. The mixing process was repeated to produce the homogeneous feedstock, and homogeneity of feedstocks was evaluated by observing the shear viscosity with time at a constant shear rate. The rheological behavior of feedstocks was investigated using capillary rheometer. It found that both feedstocks have no problem in injection molding. The binder decomposition behavior was also investigated, and a wax-polymer binder system was nearly removed by the optimized solvent and thermal debinding processes. Thereafter, the debound samples were sintered at 1750 and 1800 °C for 4 h in nitrogen atmosphere. Regardless of sintering temperature, the relative density of higher than about 96% was achieved. When comparing mechanical properties including bending strength, Vickers hardness and fracture toughness, Si₃N₄ with 2 wt% Y₂O₃ and 5 wt% Al₂O₃ (Si₃N₄+2Y5A) had higher values than β-SiAlON with 4 wt% Y₂O₃ (β-SiAlON+4Y) regardless of sintering temperature. It was supported by observing the microstructures of the plasma-etched samples.     

Evolution mechanism of the microstructure and mechanical properties of plasma-sprayed yttria-stabilized hafnia thermal barrier coating at 1400 °C

Yttria stabilized hafnia (Hf_0.84Y_0.16O_1.92, YSH16) coatings were sprayed by atmospheric plasma spraying (APS). The effects of thermal aging at 1400 °C on the microstructures, mechanical properties and thermal conductivity of the coatings were studied. The results show that the as-sprayed coating was composed of the cubic phase, and the nano-sized monoclinic (M) phase was precipitated in the annealed coating. The presence of M phase effectively constrained the sintering of the coating due to its superior sintering-resistance. The Young's modulus kept at a nearly same level of ~78 GPa even after annealing, and the coating annealed for 6 h yielded a maximum value of hardness but revealed a declining tendency in the Vicker's hardness with prolonged sintering time. The thermal conductivity increased from 0.8-0.95 W m^-1 K^-1 at as-sprayed state to 1.6 W m^-1 K^-1 after annealing at 1400 °C for 96 h. The dual-phase coating is promising to serve at temperatures above 1400 °C due to its excellent thermal stability and mechanical properties.     

Construction of BiVO4 microspheres sensitized TiO2 NTAs for the enhanced photocatalytic mineralization of organic dyes

In the present work, BiVO₄ microspheres were deposited on TiO₂ NTAs via the solvothermal method using urea as the mineralizer. The binary heterojunction formation significantly enhanced the solar response region and intensity, and the electron transfer path was built at the interface of two semiconductors, which was the main reason for the enhanced photoelectrochemical and photocatalytic performances. The S-2 electrode prepared with urea concentration of 2 mol/L displayed the high visible light photocurrent of 73.76 μA/cm² and photovoltage of −0.30 V. Furthermore, the S-2 photocatalyst also showed excellent photocatalytic decoloration ability of MO, RhB and MB dyes, and the corresponding decomposition efficiencies were 55.82%, 41.62% and 89.90% under solar irradiation. Except for the organic dyes, Cr(VI) ions also could be reduced into Cr(III), and the photocatalytic efficiency achieved 74.05% after 3 h solar irradiation. The active group and photocatalytic mechanism were proposed to illuminate the essential reason. The experimental results indicated that the novel BiVO₄/TiO₂ NTAs with binary heterojunction are attractive photocatalysts for the dyeing and printing water treatment.