高银粗铋处理工艺的改进

本文介绍了高银粗铋处理工艺的实践，对如何有效地回收进入铋生产流程的金银进行了理论和实践上的探讨。在试验基础上对原工艺进行改进，确定了新的工艺技术条件，收到了预期的经济效果。     

WC/Ni60真空熔烧涂层的组织结构特性

研究了真空熔烧WC Ni60复合涂层的显微组织结构特性 ,并测定了沿层深方向的显微硬度分布。研究结果表明 ,涂层与母材 4 5钢在界面处形成牢固的冶金结合 ,界面两侧的显微硬度呈连续性分布     

Effect of Traveling Magnetic Field on Mould-Filling Length of the A357 Melt during Casting THin Walled Plate

In order to improver the mould filling ability ,the method for production of thin-walled castings in the traveling magnetic field was applied,The relationship between magnetic field density and input voltage as well as distance was investigated,and the mould filling length of A357 melt has been studied,The electromagnetic forces applied on the melt were also analyzed,The result shows that the mould-filling length of the melt increase rapidly with the increase of magnetic flux density,The mould filling lengths in gypsum upper mould and magnetic material upper mould were compared from the standpoint of application,It demonstrated that the steel upper mould is superior to gypsum mould.     

不锈钢上激光熔敷涂层结构特征与质量研究

采用5kW连续CO2激光器对经等离子喷涂的NiCoCrAlY结合层和ZrO2陶瓷层进行二次重熔处理，并利用金相显微镜、扫描电镜、电子探针和显微硬度计对激光熔敷涂层进行了显微结构、元素分布以及显微硬度观察与测试，结果表明：多道搭接工艺能降低熔敷涂层气孔率，ZrO2陶瓷层稀释度低，与基体结合完好，并观察到NiCoCrAlY合金层中存在明显的对流图案，加入了TiO2-Al-Ti添加剂的ZrO2陶瓷层激光重熔后得到了无裂纹的定向生长柱状晶，并且呈现一次枝晶平均间距为2．3μm的表层和平均间距为3．8μm的次表层结构。     

硫回收装置技术改造总结

湿法脱硫技术在我国中小氮肥企业应用技术已相当成熟，但硫磺回收技术却一直在国内存在较大的分歧．我公司采用连续熔硫技术获得了成功．介绍了连续熔硫技术的优点和使用经验．     

高温合金表面激光熔敷热障涂层组织结构与氧化性能

采用 5KW连续CO2 激光器对Ni基高温合金上二次重熔NiCoCrAlY和ZrO2 陶瓷层进行了研究。结果表明 :激光快速熔化和凝固获得定向外延生长、紧密堆积的柱状晶氧化锆陶瓷层。NiCoCrAlY结合层与柱状晶之间存在氧化铝层 ,保证了柱状晶与NiCoCrAlY层的联结。扫描电镜和电子探针联合分析发现 ,氧化锆层与NiCoCrAlY结合层、结合层与基体间均为冶金结合。采用化学改性氧化锆消除了涂层裂纹。高温氧化性能测试得出激光重熔试样氧化动力学近似地遵守抛物线速率方程。在 12 0 0℃ ,空气下激光熔敷TBCs 抗氧化性明显高于等离子喷涂TBCs。     

激光熔覆技术在模具表面处理中应用

针对模具制造、修复与预保护中表面处理问题,提出应用激光熔覆技术,对模具表面进行激光处理,该技术与常规的模具表面处理技术相比,具有工件变形小,涂覆层质量稳定,表面硬度、耐磨性、耐腐蚀性显著提高等优点。     

钢包炉(LF)预熔精炼渣的研究

预熔精炼渣具有成分均匀，性能稳定，储存时不吸水等特点，钢包炉中使用预熔精炼渣时成渣均匀且速度快，具有较强的吸附钢中非金属夹杂的能力。综合脱硫率高等冶金效果。有显著净化钢液作用。