Cyclic thermal shock resistance of h-BN composite ceramics with La2O3–Al2O3–SiO2 addition

The effects of La₂O₃–Al₂O₃–SiO₂ addition on the thermal conductivity, coefficient of thermal expansion (CTE), Young's modulus and cyclic thermal shock resistance of hot-pressed h-BN composite ceramics were investigated. The samples were heated to 1000 °C and then quenched to room temperature with 1–50 cycles, and the residual flexural strength was used to evaluate cyclic thermal shock resistance. h-BN composite ceramics containing 10 vol% La₂O₃–Al₂O₃ and 20 vol% SiO₂ addition exhibited the highest flexural strength, thermal conductivity and relatively low CTE, which were beneficial to the excellent thermal shock resistance. In addition, the viscous amorphous phase of ternary La₂O₃–Al₂O₃–SiO₂ system could accommodate and relax thermal stress contributing to the high thermal shock resistance. Therefore, the residual flexural strength still maintained the value of 234.3 MPa (86.9% of initial strength) after 50 cycles of thermal shock.     

Improved Corrosion Resistance of Selective Laser Melted Ti–5Cu Alloy Using Atomized Ti–5Cu Powder

The different types of metal powder used for selective laser melting(SLM) process would cause distinct corrosion behavior due to the uniformity of the obtained microstructure.The SLM-produced Ti–5Cu alloy using atomized Ti–5Cu metal powder(SLMed Ti–5Cu) in this work reveals a relatively uniform microstructure with overwhelming acicular α/α′ phase and shows great advantages on corrosion resistance compared with the SLM-produced Ti–5Cu alloy using the mixture powder(SLMedM Ti–5Cu).The effect of the micro-galvanic cells decreases due to the undetectable Ti_2Cu phase in the microstructure of the SLMed Ti–5Cu.An apparent passivation behavior was observed for SLMed Ti–5Cu instead of severe pitting phenomenon for the SLMed-M Ti–5Cu.The charge transfer resistance of SLMed Ti–5Cu in this work is 10.09 ± 2.63 MΩ cm~2, which is significantly higher than that of SLMed-M Ti–5Cu(4.76 MΩ cm~2).The above result indicates the atomized Ti–5Cu powder plays an important role in the formation of the uniform microstructure of SLMed product, thereby enhancing its corrosion resistance in Hank's solution at 37 ℃.     

Design of disturbance observer based on adaptive-neural control for large-scale time-delay systems in the presence of actuator fault and unknown dead zone

This article presents an adaptive neural compensation scheme for a class of large-scale time delay nonlinear systems in the presence of unknown dead zone, external disturbances, and actuator faults. In this article, the quadratic Lyapunov–Krasovskii functionals are introduced to tackle the system delays. The unknown functions of the system are estimated by using radial basis function neural networks. Furthermore, a disturbance observer is developed to approximate the external disturbances. The proposed adaptive neural compensation control method is constructed by utilizing a backstepping technique. The boundedness of all the closed-loop signals is guaranteed via Lyapunov analysis and the tracking errors are proved to converge to a small neighborhood of the origin. Simulation results are provided to illustrate the effectiveness of the proposed control approach.     

Methyltransferase Contingencies in the Pathway of Everninomicin D Antibiotics and Analogues

Everninomicins are orthoester oligosaccharide antibiotics with potent activity against multidrug-resistant bacterial pathogens. Everninomicins act by disrupting ribosomal assembly in a distinct region in comparison to clinically prescribed drugs. We employed microporous intergeneric conjugation with Escherichia coli to manipulate Micromonospora for targeted gene-replacement studies of multiple putative methyltransferases across the octasaccharide scaffold of everninomicin effecting the A₁, C, F, and H rings. Analyses of gene-replacement and genetic complementation mutants established the mutability of the everninomicin scaffold through the generation of 12 previously unreported analogues and, together with previous results, permitted assignment of the ten methyltransferases required for everninomicin biosynthesis. The in vitro activity of A₁- and H-ring-modifying methyltransferases demonstrated the ability to catalyze late-stage modification of the scaffold on an A₁-ring phenol and H-ring C-4’ hydroxy moiety. Together these results establish the potential of the everninomicin scaffold for modification through mutagenesis and in vitro modification of advanced biosynthetic intermediates.     

Formation and wear mechanism of nickel titanium intermetallics during heat treatment of nickel coating on Ti-6Al-4V substrate

In the present work, inter-diffusion of nickel and titanium and formation of Ni-Ti intermetallic compounds on Ti-6Al-4V substrate have been studied. Initially, nickel was electrodeposited on the alloy using a modified Watts bath solution at a current density of 2 A dm^?2 for 1?h. The coated specimens were then heat treated for different durations at 750, 800 and 850 °C under argon atmosphere. The effects of temperature and time on the characteristics, hardness and wear resistance of intermetallic phases were investigated. The results showed that a multilayer structure was formed after heat treatment, an outer layer of residual nickel, an area of intermetallic layers with different compositions followed by a solid solution of Ni-Ti. It was also observed that an increase in time or temperature at first led to the formation of thicker intermetallic layers; however, after passing a critical point, the intermetallic layers seem to dissolve into the substrate. Furthermore, the wear rates of the diffusion treated samples were four times lower compared to Ti-6Al-4V alloy when sliding against AISI 52100 hardened steel.     

Influence of SiC content on the oxidation of carbon fibre reinforced ZrB2/SiC composites at 1500 and 1650 °C in air

The microstructure and the oxidation resistance in air of continuous carbon fibre reinforced ZrB₂–SiC ceramic composites were investigated. SiC content was varied between 5–20?vol.%, while maintaining fibre content at ～40?vol.%. Short term oxidation tests in air were carried out at 1500 and 1650?°C in a bottom-up loading furnace. The thickness, composition and microstructure of the resulting oxide scale were analysed by SEM-EDS and X-Ray diffraction. The results show that contents above 15?vol.% SiC ensure the formation of a homogeneous protective borosilicate glass that covers the entire sample and minimizes fibre burnout. The scale thickness is ～90?μm for the sample containing 5?vol.% SiC and decreases with increasing SiC content.     

Preparation of CaO granules using the granulation method

ABSTRACT

Improving the hydration resistance of CaO particle in manufacturing and application of free CaO-containing materials has practical significance. In this study, CaO granules was made from Ca(OH)₂ particles, which were fabricated by the granulation method. The results showed that the hydration resistance of the CaO granules which was prepared under 1700?r?min^?1 was the best, the CaO granules was sintered well in calcination process, the shell of CaO granules was relatively dense, which improves the hydration resistance of CaO granules, and the rate of hydration weight increment was 0.58% after placed in the air for 20 days under a temperature of 10–14°C and a relative humidity of 57–81%.     

Studying the effect of organo-modified nanoclay loading on the thermal stability,flame retardant,anti-corrosive and mechanical properties of polyurethane nanocomposite for surface coating

Clay polyurethane nanocomposite (CPN) coating films were fabricated by uniformly dispersing nanoclay, organically modified with 25–30 wt.% octadecylamine in varying concentrations up to 5 wt.%, in a commercial two component, glossy, acrylic aliphatic polyurethane using ultrasonication. Organo-modified nanoclay was characterized by X-ray diffraction (XRD). The dispersion of the nanoclay into the matrix was investigated by scanning electron microscopy (SEM). CPN coating films were characterized by thermogravimetric analysis (TGA), and flame retardant, corrosion resistance and mechanical properties were also investigated. The XRD measurement indicated that, the organo-modified nanoclay particles were mainly constituted of montmorillonite with traces of quartz and calcite also found to be present. The SEM analysis showed that the nanoclay layers were dispersed and intercalated into the polyurethane coating. Thermogravimetric analysis showed that incorporating 5 wt.% organo-nanoclay into polyurethane considerably enhanced the thermal stability and increased the char residue to 14.11 wt.% relative to 4.58 for the sample without organo-nanoclay (blank polyurethane). The limiting oxygen index (LOI) test revealed that incorporation of organo-nanoclay led to a further increase in LOI values, which indicate an improvement in flame retardancy properties. The corrosion resistance also improved and this improvement increases with increase nanoclay wt.%. The mechanical resistance measurements demonstrated that the gloss of the CPN coating films slightly decreased, although hardness, adhesion and impact resistance of the CPN coating films improved with the incorporation of the organo-nanoclay.     

Active disturbance rejection based trajectory linearization control for hypersonic reentry vehicle with bounded uncertainties

This paper investigates a novel compound control scheme combined with the advantages of trajectory linearization control (TLC) and alternative active disturbance rejection control (ADRC) for hypersonic reentry vehicle (HRV) attitude tracking system with bounded uncertainties. Firstly, in order to overcome actuator saturation problem, nonlinear tracking differentiator (TD) is applied in the attitude loop to achieve fewer control consumption. Then, linear extended state observers (LESO) are constructed to estimate the uncertainties acting on the LTV system in the attitude and angular rate loop. In addition, feedback linearization (FL) based controllers are designed using estimates of uncertainties generated by LESO in each loop, which enable the tracking error for closed-loop system in the presence of large uncertainties to converge to the residual set of the origin asymptotically. Finally, the compound controllers are derived by integrating with the nominal controller for open-loop nonlinear system and FL based controller. Also, comparisons and simulation results are presented to illustrate the effectiveness of the control strategy.