Enhanced electromagnetic microwave absorption of Fe/C/SiCN composite ceramics targeting in integrated structure and function

The Fe/C/SiCN composite ceramics were synthesized by polymer-derived method to obtain the integration of structure and functions. The electromagnetic waves (EMW) absorption properties at X and Ku bands were investigated. The addition of nano-sized Fe particles improved the magnetic loss and impedance matching, and the carbon nanotubes generated by the iron in-situ catalysis increased the internal relaxation polarization and interfacial polarization, which together improved the EMW absorption properties significantly. In particular, the Fe/C/SiCN-9 showed the optimum reflection loss (RL) of ?31.06 dB at 10.03 GHz with an effective absorption bandwidth (EAB, RL < ?10 dB) of 3.03 GHz at 2.51 mm, indicating the excellent EMW absorption properties of Fe/C/SiCN composite ceramics.     

Fabrication and laser performances of Yb:Sc2O3 transparent ceramics from different combination of vacuum sintering and hot isostatic pressing conditions

In this paper we report on the preparation and laser performance of transparent 3at.% Yb:Sc₂O₃ ceramics by reactive sintering of commercially available powders under vacuum followed by hot isostatic pressing (HIP). Combinations of different vacuum sintering temperatures (1650 °C and 1750 °C) and different HIP treatments (1700 °C and 1800 °C at 200 MPa) were tested in order to understand how these steps influence the microstructure and thus the optical and lasing properties of the ceramic samples. All the samples showed a good optical quality. The microstructure analysis and the laser tests showed that the vacuum pre-sintering temperature is the key factor determining the quality of the samples and the laser performances. The best values of slope efficiency i.e. η_L = 50 % and output power i.e. P_out = 6.62 W were obtained for the sample pre-sintered under vacuum at 1650 °C and hot isostatically pressed at 1800 °C.     

Surveying of Na2O3–BaO–PbO–Nb2O5–SiO2–Al2O3 glass-ceramics system in terms of alpha,proton, neutron and gamma protection features by utilizing GEANT4 simulation codes

In this study, nuclear shielding qualities of glass-ceramics with chemical composition Na₂O₃–BaO–PbO–Nb₂O₅–SiO₂–Al₂O₃ containing different amount of BaO and PbO were investigated. The μ_ρ values were simulated using GEANT4 toolkit at 0.015–20 MeV wide energy range and the obtained results were verified by theoretical WinXCOM results. The variables such as μ_ρ, HVL, MFP, Z_eff, N_eff, EBF and EABF were computed to determine the gamma-ray shielding performances of studied glass ceramics. The results revealed that increase in PBO and BaO percentages in glass samples has caused to decrease the HVL, MFP, EBF and EABF values and increase μ_ρ, Z_eff values. It has been seen that N28 and S24 samples own superior protection ability against gamma radiation. In addition, the shielding capacity of these glass ceramics against charged and uncharged particles were predicted by determination of MSP and PR values for alpha, proton and ΣR values for neutrons. It has been concluded that PbO and BaO addition improve radiation shielding competences of glass ceramics. The data obtained from this study will be beneficial for designing glass ceramics shields for radiation protection enforcements.     

Warm-white light performance of Dy3+, Eu3+: NaLa(WO4)2 phosphors excited with a 450-nm LED

Dy³⁺, Eu³⁺: NaLa(WO₄)₂ phosphors are successfully synthesized through the solid-state reaction technique. The phase-structure and morphology are measured via X-ray diffraction and energy dispersive spectrometry. The concentrations of Dy³⁺, Eu³⁺, La³⁺, and W⁶⁺ are measured via ICP. The absorption and excited spectra are presented, which indicate that a blue band ranging from 430 to 480 nm is suitable for excitation. Using a commercial blue LED with a wavelength of 450 nm as the excitation light source, emission spectra for samples with varying dopant concentration ratios of Dy³⁺ to Eu³⁺ are obtained, which show good tunable yellow and red emission. For the purpose of investigating white LED performance, CIE spectra and a white light photo are also presented. The results reveal that varying the dopant concentration ratio of Dy³⁺ to Eu³⁺ plays a key role in the warm-white performance. With increasing concentration of Eu³⁺, the correlated color temperature decreases from 4069 to 3172 K, which indicates good warm-white performance.     

Microstructure and permeability of porous YSZ ceramics fabricated by freeze casting of oil-in-water suspension

Porous yttria-stabilized zirconia (YSZ) ceramics are fabricated through freeze casting of oil-in-water suspension followed by sintering at 1250−1550 °C. The pore structure, compressive strength and permeability of porous YSZ ceramics are tailored via altering the emulsion content and sintering temperature. The samples obtained using higher emulsion content or at lower sintering temperature show larger Darcian and non-Darcian constants due to their higher open porosity and larger pore size. Furthermore, the investigation on individual contributions of viscous and inertial resistances on the total pressure drop during permeation process indicates that the viscous resistance increases but the inertial resistance decreases with increasing the emulsion content or decreasing the sintering temperature for samples. Porous YSZ ceramics obtained in this work with a k₁ range of 3.14 × 10⁻¹³–1.12 × 10⁻¹² m² are appropriate for applications in filters and membrane supports.     

Effect of lanthanum doping on water content and diffusion properties of corundum for producing transparent ceramics

The effect of doping corundum with lanthanum on the content of water and other gas impurities, on the diffusion characteristics, on the unit cell size and static strength of fine-crystalline corundum synthesized under thermovapours conditions in a supercritical water fluid was studied.Content, release and diffusion coefficients of water and other volatile impurities in corundum were measured by kinetic thermodesorption mass spectrometry. Water is the main volatile impurity in fine-crystalline corundum. It was found that the introduction of lanthanum into the structure of corundum reduces several times the content of water and other gas-liquid impurities. An increase in the diffusion coefficient of water during the doping of corundum with lanthanum leads to an increase in the degassing rate of fine-crystalline raw materials. When doping corundum, lanthanum, being localized in structural defects, not only displaces structural hydroxyl groups with the formation of strong aluminate-like bonds, but also decreases in the unit cell and increases in the average static strength of the crystals. La-doped corundum, due to the reduced content of water and other gas impurities, is a promising raw material for the production of transparent ceramics.     

Bond characteristics,vibrational spectrum and optimized microwave dielectric properties of chemically substituted NdNbO4

Coordination chemistry, bond state and vibrational spectrum of co-substituted microwave dielectric NdNb_1-x(Zr_0.5W_0.5)_xO₄ ceramics (x = 0.01∼0.05) were investigated. Raman spectra and XRD refinement showed a solid solution was formed. The compressed and elongated chemical bonds are responsible for the variations of crystal parameters and cell volume. Calculated chemical bond parameters indicated bond covalency, lattice energy and Nb-site bond energy act on the fluctuations of the permittivity, quality factor and temperature coefficient, respectively. Meanwhile, the infrared vibrational spectrum is fitted to quantify the contributions of observed IR mode to the intrinsic loss. Compact ceramic possesses excellent properties: ε_r ∼ 19.2, Q × f ∼ 55282 GHz and τ_f ∼ -11.36 ppm/°C with x = 0.04, at 1250°C.     

Low-temperature hot-press sintering of AlN ceramics with MgO–CaO–Al2O3–SiO2 glass additives for ceramic heater applications

Aluminum nitride (AlN) is used a ceramic heater material for the semiconductor industry. Because extremely high temperatures are required to achieve dense AlN components, sintering aids such as Y₂O₃ are typically added to reduce the sintering temperature and time. To further reduce the sintering temperature, in this study, a low-melting-temperature glass (MgO–CaO–Al₂O₃–SiO₂; MCAS) was used as a sintering additive for AlN. With MCAS addition, fully dense AlN was obtained by hot-press sintering at 1500 °C for 3 h at 30 MPa. The mechanical properties, thermal conductivity, and volume resistance of the sintered AlN–MCAS sample were evaluated and compared with those of a reference sample (AlN prepared with 5 wt% Y2O3 sintering aid sintered at 1750 °C for 8 h at 10 MPa). The thermal conductivity of AlN prepared with 0.5 wt% MCAS was 91.2 W/m?K, which was 84.8 W/m?K lower than that of the reference sample at 25 °C; however, the difference in thermal conductivity between the samples was only 14.2 W/m?K at the ceramic-heater operating temperature of 500 °C. The flexural strength of AlN–MCAS was 550 MPa, which was higher than that of the reference sample (425 MPa); this was attributed to the smaller grain size achieved by low-temperature sintering. The volume resistance of AlN–MCAS was lower than that of the reference sample in the range of 200–400 °C. However, the resistivity of the proposed AlN–MCAS sample was higher than that of the reference sample (500 °C) owing to grain-boundary scattering of phonons. In summary, the proposed sintering strategy produces AlN materials for heater applications with low production cost, while achieving the properties required by the semiconductor industry.     

Ablation behavior of (TiZrHfNbTa)C high-entropy ceramics with the addition of SiC secondary under an oxyacetylene flame

The ablation behavior of high-entropy ceramics (HECs) was investigated in this study using an oxyacetylene flame at 2000 °C. Spark plasma sintering was used to construct a dense HEC (TiZrHfNbTa)C with a 20 vol% of SiC addition (HEC-20SiC). The densification of HEC-20SiC can be improved to a certain extent by adding SiC particles, increasing the hardness of HEC-20SiC to up to 24.6 GPa, and the crack deflection observed through the addition of SiC particles were considered to be the strengthening and toughening mechanisms. After ablation, Hf₆Ta₂O₁₇, Ti_5.1Ta_4.9O₂₀, Nb₂Zr₆O₁₇, TaZr_2.75O₈, and SiO₂ can be detected on an ablated surface and HEC-20SiC possesses the minimum mass ablation rate (?1.9 mg s^?1) and line ablation rate (2.1 μm s^?1) among the comparative ceramics. On the one hand, the SiC phase forms gaseous CO, CO₂, and SiO as well as viscous SiO₂ during ablation and some part of the heat can be dissipated by the evaporation of gaseous CO, CO₂, and SiO; further, pore defects can be healed by viscous SiO₂, thus inhibiting the diffusion of reactive oxygen species. On the other hand, the HEC phase with a lattice-distortion caused by single-phase solid-solution can effectively inhibit the invasion of reactive oxygen species and the outward migration of metal atoms. The invasion rate of reactive oxygen is considered to be the main step during HEC-20SiC ablation, and it is believed that higher principal component HECs can improve ablation performance even further.