补强剂和共混工艺对PA/PVC/NBR三元共混弹性体性能的影响

在选择三元共聚尼龙（PA）、聚氯乙烯（PVC）、丁腈橡胶（NBR）为主体材料，制备PA／PVC／NBR（10／30／60）三元共混弹性体的工作基础上，进一步探讨了填料品种和用量，共混温度，加料顺序等因素PA／PVC／NBR三元共混弹性体的影响。试验结果表明：在PA／PVC／NBR（10／30／60）共混体系中，补强型填料的补强效果优于非补强型的填料，6种填料补强效果依次是：快压出炭黑＞半补强炭黑＞白炭黑＞活性重质，CaCO3＞陶土＞滑石粉，快压出炭黑的适宜用量是20－50份。在制备PA／PVC／NBR三元共混物时，适宜的共混温度是122－140℃，并且采用二段法混工艺制得的共混物性能优于采用一段法共混工艺。     

In vivo aging of gutta‐percha dental cone

Gutta‐percha cone is the most widely used material for root canal filling. The in vivo aging of this cone focus on the degradation of its main organic component, trans‐1,4‐polyisoprene, was studied. Aged cones (25 samples) from 2 to 30 years of root canal filling were extracted from different patients in the occasion of retreatment by mechanical way. The information about the aging time was given by the patients. Gel‐permeation chromatography (GPC) and infrared spectroscopy (FTIR) were the analytical techniques used. Polyisoprene degrades with time of aging, but in a slow process. Decrease in polymer molar mass from 5.7 × 10⁵ to 1.7 × 10⁵ g/mol was observed in polyisoprene from cone after 30 years of root canal filling and inside a noninfected tooth. In tooth with caries and periodontal infection, the decrease in molar mass is higher (4.6 × 10⁴ g/mol in cone with 10 years of aging). The production of carbonyl and hydroxyl groups in the aged material indicates that the process is oxidative, even in closed teeth. In these cases, the oxygen could be provided from tissue fluid. The degradation mechanism is complex and depends on many factors, besides time of root canal filling. The dental problem caused by the aging could be the production and migration of cytotoxic substances to periodontal ligament and the reduction on the canal sealing property due to the polymer weight loss. Both of them could contribute to the root canal treatment failure. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100:4082–4088, 2006     

FR-1型粘合剂的性能及其应用

介绍了FR-1型粘合剂用于氟橡胶、硅橡胶、三元乙丙橡胶与金属热硫化粘着，制作橡胶金属复合制品的情况。金属骨架经喷砂或表面化学处理并用溶剂清洗之后，涂FR—1型粘合剂，经预烘干后与橡胶进行热硫化粘着，效果良好。     

尿素包合法分离橡胶籽油中的多价不饱和脂肪酸

用尿素包合法从橡胶籽油混合脂肪酸中分离多价不饱和脂肪酸 ,用正交设计实验法对分离工艺进行研究 ,其最佳分离条件是 :原料配比为m(混合脂肪酸 )∶m(尿素 )∶m(乙醇 ) =1 0 0∶1 5∶1 8,回流时间 12 0min。经一次尿素包合法分离即可得到多价不饱和脂肪酸质量分数大于90 %的产品 ,实验收率大于 35 %     

Photoelastic Studies on Rubber-to-Rubber Joints

Photoelasticity is a method which yields information on the principal stress difference and orientation in a composite structure. Various problems associated with this technique, especially those concerning the fundamental relationship between the fringe order and the stress, have yet to be investigated. A few studies of this relationship in a universal stress state have been presented, particularly in the field of rubber-to-metal and rubber-to-fabric composites, but no evaluations have so far been made in the field of rubber-to-rubber joints. Applying the photoelastic method, we report our observations on the stress distribution in a natural rubber to natural rubber joint subjected to uniaxial tension. A comparison between the results of experimental photoelastic studies and the corresponding computer modelling has been illustrated. The theoretical displacement pattern of the angular joints of bi-rubber part has also been highlighted.     

纳米碳酸钙/炭黑并用对丁苯橡胶性能的影响

研究了纳米碳酸钙／N330炭黑并用比对丁苯橡胶性能的影响。结果表明，随着CaCO3／N330并用比的改变，材料的强度有了显著的提高，特别是CaCOa／N330并用比为20／30(质量份)时复合材料的拉伸强度达到了20MPa以上，同时材料具有较好的弹性和较低的硬度；两种处理剂相比，树脂酸处理的碳酸钙具有较好的性能；表面处理的纳米炭酸钙与炭黑并用，可以降低炭黑填充橡胶的动态滞后，表面处理的纳米碳酸钙的加工性能比纳米炭黑好，可以通过并用纳米碳酸钙来改善炭黑胶料的加工性能。     

镍系低门尼黏度顺丁橡胶

通过采用适当的相对分子质量调节剂、优化催化剂配方和加入添加剂的工艺合成了镍系低门尼黏度顺丁橡胶(NiBR)。结果表明,加入含氧类相对分子质量调节剂可以加宽NiBR门尼黏度的调节范围;加入α-烯烃类相对分子质量调节剂,可以明显降低NiBR的门尼黏度;在环烷酸镍-三异丁基铝-三氟化硼乙醚络合物-含氧类相对分子质量调节剂四组分体系中,可使三异丁基铝与三氟化硼乙醚络合物的摩尔比较低,以减少催化剂用量;加入少量苯类添加剂可以明显提高NiBR的拉伸强度和300%定伸应力。     

氯醚树脂与氯化橡胶的比较

将氯醚树脂和氯化橡胶分别作为基料制成底漆、中涂、面漆,从性能上进行比较,得出氯醚树脂与氯化橡胶无明显优劣之分.从环保角度来看,氯醚树脂完全可以取代氯化橡胶.     

湿法磷酸生产装置衬胶防腐技术及胶板的选用

介绍衬胶防腐在湿法磷酸生产中的应用 ,特别是真空设备设计衬胶防腐的要点以及目前我国湿法磷酸装置中国产 (含合资、独资企业 )胶板的特点和选用、施工中应注意的事项。