芯壳乳液胶粘剂的研究

介绍乙酸乙烯酯－丙烯酸丁酯－丙烯酸芯结构乳液的制备方法，并将它们的性能与均匀共聚乳液作了测试与比较。     

邻羟基环己基丙烯酸酯光聚合动力学研究

采用实时红外光谱技术(RTIR)研究了邻羟基环己基丙烯酸酯(HCA)光聚合反应动力学,探讨了光照强度、光引发剂种类和浓度对其光聚合动力学的影响,并与脂肪族羟基丙烯酸酯单体丙烯酸羟乙酯(HEA)进行了对比。结果表明,最终双键转化率和相对反应速率随光强增大而增加;光引发剂浓度对最终双键转化率和反应速率的影响随引发剂不同呈现不同规律;与HEA相比,HCA具有更高的反应活性,但最终双键转化率较低。     

Effect of miscibility and forced compatibility on damping properties of CIIR/PAc blend

In this study, a kind of novel damping materials was prepared based on the blend of chlorinated butyl rubber (CIIR) and polyacrylate (PAc) synthesized by different molar ratio of butyl methacrylate and ethyl acrylate. Research results from experiments and analyses by employing DMA, TEM, and FTIR show that whether at a cocured system or noncocured system, it can be achieved to shift a loss peak of CIIR towards a higher temperature region and to keep the damping value from markedlly decreasing, which broadens the effective damping function area of CIIR to the vicinity of ambient temperature. In the former system, the thermodynamical miscibility of CIIR and PAc, to some extent, is predominated by the molecular design of PAc, while in the latter system, covulcanized networks play a more significant role in improving compatibility and abating the peak split, though the suppression effect of thermal stress on the transition of CIIR T_ll transition still can not be neglected. Furthermore, transition state derived from the cocuring CIIR and PAc cannot make the phase separation completely take place, and consequently results in the deformation of phase morphology of the cocured CIIR/PAc blend. It is the influence of thermodynamics miscibility and forced compatibility in different size that makes the suppression effect of foreign PAc on CIIR T_ll transition be controllable. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 3127–3133, 2006     

HANa-AANa共聚物作为多功能陶瓷添加剂的研究

通过自由基水溶液微波共聚法合成了腐植酸钠-丙烯酸钠(HANa-AANa)共聚物,将之应用于陶瓷料浆及坯体中,研究了HANa-AANa共聚物对陶瓷料浆流动性、坯体可塑性及坯体干燥强度的影响。通过和腐植酸钠的对比研究表明,HANa-AANa共聚物是一种较好的陶瓷多功能添加剂,对料浆具有良好的解凝性,同时对坯体具有较大的增塑、增强效果。     

大粒径聚丙烯酸丁酯胶乳的制备

采用种子乳液聚合法制备了丙烯酸酯-苯乙烯-丙烯腈共聚物生产工艺中的基础胶乳聚丙烯酸丁酯(PBA),考察了配方和工艺条件对其粒径增大的影响。结果表明,在合成种子胶乳时可加入质量分数0.2%～0.8%的乳化剂十二烷基硫酸钠;在种子胶乳粒径放大试验时,加入质量分数0.3%的乳化剂十二烷基硫酸钠及补加的单体量为种子胶乳总固体物质量的33倍可以得到大粒径的PBA胶乳。采用种子乳液聚合法进行PBA胶乳粒径放大方法简便、效果明显。     

A new core–shell type fluorinated acrylic and siliconated polyurethane hybrid emulsion

A novel core–shell type fluorinated acrylic and siliconated polyurethane (FSiPUA) hybrid emulsion was prepared by seeded emulsion polymerization using siliconated polyurethane (SiPU) as a seed and forming the structure with SiPU as a shell and the copolymer of butyl acrylate (BA) with 2,2,2-trifluoroethylmethacrylate (TFEMA) as a core. SiPU was synthesized using isophorone diisocyanate (IPDI), polytetramethylene ether glycol (PTMG), polypropylene glycol (PPG), dihydroxybutyl-terminated polydimethylsiloxane (PDMS), dimethylol propionic acid (DMPA), 1,6-hexanediol (HDO) and triethylamine (TEA). The contents of siloxane and fluorine were determined according to the feed ratio. Fourier transform infrared spectroscopy (FTIR) was used to identify the chain structure of SiPU and FSiPUA. Investigation of transmission electron microscopy (TEM) confirmed the core–shell structure of FSiPUA emulsion and gave the particle size at about 50 nm. The measurement results of water contact angles and the solvent absorptions in water and n-octane for cured films showed that the water and the oil repellency for FSiPUA had been improved significantly with a suitable content of fluorine and siloxane.     

两性乳化剂体系对有机硅改性丙烯酸酯乳液合成的影响

采用新型琥珀酸类两性乳化剂(A1)与非离子乳化剂壬基酚聚氧乙烯醚(CA407)复配体系,合成了有机硅γ-甲基丙烯酰氧基丙三甲氧基硅烷(A174)改性的丙烯酸酯乳液。系统研究了两性乳化剂体系与非离子乳化剂复配比例、用量及乳化剂在种子乳液与预乳液中分布比例(R/F)E对乳液聚合及其性能的影响。研究表明:乳化剂配比m(A1)∶m(CA407)=30∶70时,乳液聚合稳定性及抗电解质稳定性较好;乳化剂用量越大,乳胶粒径越小,粒径分布越宽,乳液黏度越大,涂膜吸水率也越大;乳化剂在种子乳液与预乳液中的分布比例主要影响乳液聚合的稳定性。同时通过TEM乳胶粒形态分析及DSC涂膜的玻璃化转变温度分析认为,A174主要在乳液聚合时分布在乳胶粒表面,易水解交联。     

NCO含量对聚氨酯-丙烯酸酯复合乳液性能的影响

以甲苯二异氰酸酯(TDI-80)、聚醚二元醇(N210)、二羟甲基丙酸(DMPA)和甲基丙烯酸甲酯(MMA)为主要原料，采用原位乳液聚合法，合成聚氨酯-丙烯酸酯(PUA)复合乳液。在保证DMPA含量、中和度等不变的情况下，研究了NCO／OH物质的量之比对乳液的性能及外观的影响。     

有机硅改性丙烯酸酯核-壳结构压敏胶聚合物乳液的研制

采用种子乳液聚合的方法制备了一种新型具有核/壳结构的有机硅改性丙烯酸酯压敏胶聚合物乳液,讨论了多官能团有机硅氧烷功能性单体、核壳单体结构、乳化剂、引发剂以及聚合温度等因素对压敏胶聚合物乳液性能的影响。