论述了环境友好阻燃环氧树脂覆铜板研究开发的意义。提出通过开发并使用含氮、磷或硅的非卤阻燃型环氧树脂,含磷、氮或磷-氮的功能性阻燃固化剂和在体系中添加有机磷阻燃剂、氢氧化铝等无机阻燃剂等途径来开发环境友好阻燃环氧树脂覆铜板。并对我国在今后该领域的研究作了展望。     

生物分解性纤维及其应用

本文介绍了生物分解性纤维所用的树脂，生产方法及应用。     

甲基丙烯酸乙酯合成工艺研究

以大孔强酸性离子交换树脂为催化剂,甲基丙烯酸(MAA)与乙醇直接酯化合成甲基丙烯酸乙酯(EMA)。在MAA与乙醇摩尔比为1:3、反应温度89～93℃、空速0.3h~(-1)的条件下,MAA转化率不低于98％,EMA的选择性不低于99％。     

硼酸铝晶须增强环氧树脂和双马来酰亚胺树脂体系的研究

本文以硼酸铝晶须为增强剂，以4，5-环氧环己烷-1，2-二甲酸二缩水甘油酯(TDE-85)，甲基纳狄克酸酐(MNA)、N，N’-二胺基二苯甲烷型双马来酰亚胺(BMI)/O，O′-二烯丙基双酚A(BA)体系分别作为基体制备晶须增强复合材料。研究了晶须对树脂的尺寸、表面处理方法、含量对树脂体系力学性能和热性能的影响；通过扫描电子显微镜(SEM)分析了浇注体的弯曲、冲击断口，研究晶须的增强机理。     

Structure and properties of CE/CTBN/EP blends: II. Effect of EP on the mechanical properties and thermostability of the CE/CTBN system

Carboxyl‐terminated butadiene‐acrylonitrile rubber (CTBN) has often been used to improve the toughness of cyanate ester (CE) resin while sacrificing modulus and thermostability. In this paper, the addition of the appropriate amount of epoxy resin (EP) to the CE/CTBN system is shown to not only increase the modulus and thermostability of the blend, but also improve the toughness. The values of impact strength showed a maximum for the CE/CTBN/EP 100/5/5 blend. The temperature of 10 % weight loss (T₁₀) improves from 376 °C for CE/CTBN 100/5 to 407 °C for the CE/CTBN/EP 100/5/2.5 blend. It is proposed that addition of the appropriate amount of EP can decrease the mobility and increase the stability of CTBN via the reaction between the terminal carboxyl group of CTBN and the hydroxyl group of EP. But a very high EP concentration will decrease the crosslinking density of CE, consequently reducing the mechanical properties and thermostability of the blends. Copyright © 2004 Society of Chemical Industry     

聚合物-金属界面相形貌的研究

环氧树脂在 Al 合金表面生成纤维状的界面相结构,其形成、发展和特征与树脂的体系、交联反应条件以及 Al 合金的表面状态有关。环氧树脂的基础相为颗粒状的超结构组织。聚合物界面相的力学破坏表现为纤维体的拉伸、变形和断裂,而基础相在纯剪切受力时出现在45°方向的裂纹,并发展导致连接层的破坏。     

一种环氧树脂阻尼灌封胶的热氧加速老化研究

研究了某种环氧树脂阻尼灌封胶在热氧老化的作用下分子结构、硬度、断面形貌以及动态力学性能随时间的变化．傅立叶红外光谱图表明，所制备的样品环氧基团反应比较完全，热氧老化后试样表面由仲胺和环氧基团形成的酯键发生了部分断裂和氧化；邵氏硬度的增加、瓦向高温区移动则表明在老化过程中复杂的固化反应仍然继续进行；最大损耗因子（tanδmax）波动较小表明试样老化后分子结构几乎保持不变；SEM图片显示试样的冲击断裂由老化前的韧性转变为老化后的脆性断裂．     

Preparation of ultra‐low‐density microcellular materials

Microcellular polymeric materials can be obtained by the polymerization of a high‐internal‐phase emulsion. These materials are good candidates as targets toward inertial confinement fusion. This application requires severe specifications, including a very low density and a small cell size. In this study, we examined the influence of parameters such as emulsification conditions, surfactant nature, and the presence of a porogen on the obtainment of those requirements. It was possible to obtain microcellular polymeric foams with apparent densities as low as 0.0126 g/cm³. However, it was difficult to obtain very low material density and still maintain a small average pore size. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 96: 2053–2063, 2005     

Fluorescence and IR characterization of epoxy cured with aliphatic amines

Cure reactions of the stoichiometric mixtures of diglycidyl ether of bisphenol A (DGEBA) and two very low molecular weight aliphatic polyether diamines (PED) were studied by using fluorescence and mid- and near-IR spectroscopic techniques. As the cure proceeded, the primary amine groups in PED are converted to the secondary and the tertiary amines. Near-IR spectral analysis was used to calculate the concentration of the three amine groups as a function of cure time. The decrease in the fluorescence intensity of DGEBA at about 307 nm was observed due to more effective quenching of the tertiary amine groups in PED, in comparison to the primary and the secondary amine groups. A large decrease in fluorescence intensity at 75 and 95 °C cure was observed. The amount of all the amine species was estimated from NIR spectra to shed light on the cure kinetics of PPO (polypropylene oxide) in comparison with PEO (polyethylene oxide) epoxy, as well as to explain their fluorescence behavior.The fluorescence intensity changes were correlated to the extent of epoxy reaction obtained by mid- and near-IR spectroscopy.     

过氧化甲乙酮合成研究

论述了过氧化甲乙酮的合成方法，用阳离子交换树脂催化剂代替传统的无机酸催化剂。考察了离子交换树脂用量、反应温度对反应产率、活性氧含量的影响及溶剂对产品稳定性的影响。