卡拉胶改性三聚磷酸铝对水性环氧涂层防腐性能的影响

通通过卡拉胶（KC）对三聚磷酸铝（ATP）进行接枝改性获得KC-ATP改性填料,再将其添加到水性环氧树脂（WEP）中制备复合防腐涂层。采用FTIR、XPS、TG、SEM对ATP改性前后的形貌、结构进行表征。结果表明,KC成功地接枝到ATP表面,改善了ATP的水溶性。采用电化学阻抗谱（EIS）和盐雾实验考察了复合涂层的防腐性能。结果表明,复合涂层的防腐性能明显优于纯水性环氧涂层,且当KC-ATP功能填料含量为1.0%时（以水性环氧树脂的质量为基准,下同）,涂层的耐腐蚀性能达到最佳,浸泡48 h后涂层的极化电阻Rp为8.183×107 Ω∙cm2,远高于ATP改性复合涂层和纯环氧涂层。     

Fabrication of Biodegradable Polyurethane Foam Scaffolds with Customized Shapes and Controlled Mechanical Properties by Gas Foaming Technique

Poly(ε-caprolactone) (PCL)-based polyurethane (PU) foam scaffolds with different mechanical properties are fabricated using a gas foaming technique to use as porous substitutes for ear or bone with cartilage. PCL diol or triol is used as a polyol in PU foam for biocompatibility and biodegradation, with an aqueous gelatin solution as a blowing agent. The highly porous inner and outer structures of the scaffolds are developed by employing a silicone surfactant and sulfuric acid, respectively. The PU scaffolds prepared by PCL diol show ductile and flexible properties, whereas the PU scaffolds prepared by PCL triol exhibit high compression strength. In vitro test reveals the low toxicity of the PU scaffolds and the high ALP activity of MC3T3-E1 cells in the PU scaffold prepared by PCL triol. By taking advantage of the difference in mechanical properties, customized PU scaffolds with ear or bone shapes are fabricated using a silicone mold. The PU scaffolds with two compartments of PCL diol and triol (corresponding to cartilage and bone, respectively) are fabricated as a substitute for bone with cartilage. It is believed that the PU scaffolds with highly porous structure and controlled mechanical properties have wide potential application for tissue engineering.     

铸造用聚氨酯粘合剂组份Ⅰ酚醛树脂合成研究

铸造用的聚氨酯粘合剂组合物，主要由极性和非极性溶剂溶解的酚醛树脂组份I和非极性溶剂稀释的聚异氰酸酯组份Ⅱ组成。组份Ⅰ酚醛树脂结构、性能是决定该类粘合剂性能因素之一。本文对铸造用聚氨酯粘合剂的组份Ⅰ酚醛树脂结构、合成方法、原料材料选择等问题进行了分析讨论，为铸造用聚氨酯粘合剂的组份Ⅰ的制备和苯醚型酚醛树脂的合成提供一些参考。     

环保型木器涂料

介绍水性和紫外光固化两类环保型木器涂料及其研究进展。水性木器涂料主要为丙烯酸酯与聚氨酯两大类，其研究进展集中表现为乳液改性，包括自交联、共混共聚、微乳液等；紫外光固化木器涂料包括其光固化树脂、活性稀释剂和光引发剂的功能及进展；指出研究新型乳液以提高水性木器涂料涂膜的表面性能，开发新型原材料以降低紫外光固化木器涂料的成本、扩大适应范围将成为今后环保型木器涂料的研究重点。     

降低湿法MD-240树脂的材料成本

通过调整聚氨酯树脂的生产配方,用乙二醇和/或聚乙二醇取代1,4-丁二醇和己二酸合成的聚酯多元醇,充当聚酯树脂的柔性链段,同时,用乙二醇等相对分子质量低的二元醇取代1,4-丁二醇作扩链剂,从而减少1,4-丁二醇的用量,降低湿法MD-240树脂的材料成本。     

沥青聚氨酯防水涂料的发展概述

简要介绍了沥青聚氨酯防水涂料的现状、配方设计、性能及应用,并探讨了沥青与聚氨酯的相容性问题。     

水性聚氨酯材料配方设计技巧

介绍了优选法的0.618法和分数法,对其进行改进创新和原理证明,并应用于生产涂料配方设计中。     

软段含羧基的水性聚氨酯贮存稳定性研究

合成了软段含羟基的水性聚氨酯（WPU），对影响其贮存稳定性的各种因素进行了研究，通过显微镜对PU进行了观察。结果表明：以甲苯二异氰酸酯（TDI）合成，在有性溶剂（如丁酮、丙酮）条件下用三乙胺中和，采用较小相地分子质量的聚酯有利于增强WPU的贮存稳定性，以TDI合成的PU-TDI体系的粒径较PU-IPDI体系的小，稳定性高；以丁酮、丙酮为溶剂的PU-IPDI体系相反转完全。     

水性聚氨酯结构与微相分离的研究

合成了一系列水性聚氯酯，并用红外光谱、差示扫描量热仪对乳液胶膜进行表征，考察了软段组成、DMPA含量及。(-NCO)：n(-OH)比值对产物微相分离的影响。实验结果表明：聚醚型产物的微相分离程度高于聚酯型产物。提高DMPA用量，软段Tg移向低温区，说明体系的做相分离程度加大。随着n(-NCO)：n(-OH)比值的增大，软段Tg也移向低温区，软硬段的微相分离程度增大.