Microstructure and strength of brazed joints of TiB2 cermet to TiAl-based alloys

In this study, TiB2 cermet and TiAl-based alloy are vacuum brazed successfully by using Ag-Cu-Ti filler metal.The microstructural analyses indicate that two reaction products, Ti ( Cu, Al ) 2 and Ag bused solid solution ( Ag ( s. s ) ) , are present in the brazing seam, and the iuterface structure of the brazed joint is TiB2/TiB2 Ag ( s. s ) /Ag ( s. s ) Ti ( Cu,Al)2/Ti( Cu, Al)2/TiAl. The experimental results show that the shear strength of the brazed TiB2/TiAl joints decreases us thebrazing time increases at a definite brazing temperature. When the joint is brazed at 1 223 K for 5 min, a joint strength up to 173 MPa is achieved.     

EFFECT OF BRAZING TIME ON TiC CERMET／IRON JOINT BRAZED WITH Ag-Cu-Zn FILLER METAL

The brazing of TiC cermet to iron was carried out at 1223K for 5-20min using Ag-Cu-Zn filler metal.The formation phase and interface structure of the joints were investigated by electron probe microanalysis(EPMA).scanning electron microscopy(SEM) and X-ray diffraction(XRD).and the joint strength was tested by shearing method.The results showed:there occurred three new formation phases,Cu(s.s),FeNi and Ag(s.s) in TiC cermet/iron joint.The interface structure was expressed as TiC cermet/Cu(s.s) FeNi(Ag(s.s) a little Cu(s.s) a little FeNi/Cu(s.s) FeNi/iron.With brazing time increasing,there appeared highest shear strength of the joints.the value of which was up to 252.2MPa when brazing time was 10min.     

Evolution of Ti （C, N）-based cermet microstructures

Two series of Ti(C, N)-based cermet materials originating from the same chemical composition but with dif-ferent grain size distribution and sintered to different stages of the sintering cycle have been studied using SEM, TEM,EDX, and XRD. Much of the surrounding structure is formed during solid state sintering. During the solid state sintering, at first, the Mo and W rich (Ti, Mo, W)C inner rim is formed by the interaction among TiC, WC, and Mo2C; then the Mo and W lean (Ti, Mo, W)(C, N)outer rim is formed. During the liquid phase sintering, the outer rim of coarse grains grows rapidly throw a solution-reprecipitation process; aLso coarse grains grow by particle coalescence. The interface between coarse grain outer rim and binder is flat (crystal surface).     

Preparation and optical properties of Nb-NbN multilayer films as solar selective absorptive coatings

Based on the cermet double layer structure, Nb-NbN multi-layer films for solar selective coatings were deposited by direct current reactive magnetron sputtering. The Nb/Nb-NbN/Al2O3 trilayered structure was deposited on a stainless steel (SS) substrate by using a single niobium target. The expected components were adjusted by changing the gas flowing ratios of Ar: N2. The Al2O3 antireflective layer on the top of the film was produced by r. f. magnetron sputtering using Al2O3 ceramic target. A solar absorptivity of 0.94 and a normal emissivity of 0.16 at room temperature have been achieved for the coating. Thermal vacuum aging to the samples was carried out at 350 and 500 ℃ for 1 h. The results show a good thermal stability. Microstructure and its dependence on temperature of the Nb, NbN and Nb-NbN single layers were investigated, respectively.     

Ti(C,N)基金属陶瓷烧结过程中的相变

该文对不同温度下烧结的试样作了X－射线分析，测定了不同温度下，硬质相和粘结相的点阵常数，各主要组成相X射线的相对衍射强度，并对最终烧结体进行了能谱分析。通过以上实验，确定了Ti（C，N）基金属陶瓷烧结过程中所发生的相变、固溶等变化规律。     

新型陶瓷刀具的发展与应用

回顾了陶瓷刀具的发展简况及其意义,重点介绍了Si3N4基和TiCN基复合陶瓷刀具的研制、性能和应用.复合Si3N4陶瓷刀具有较高的耐磨性和抗冲击性,特别适合于各类铸铁件的粗精加工,也能进行铣削、刨削等冲击力很大的加工,其切削效率可提高3～10倍;复合TiCN金属陶瓷刀具具有很高的硬度和耐磨性,特别适合于各类高硬高强钢(如淬硬钢等)的加工,可对高硬材料实现"以车代磨"干切削,免除退火工艺和冷却液,大幅度提高生产效率.新型复合陶瓷刀具已经在我国冶金、水泵、矿山机械、轴承、滚珠丝杠、汽车、军工等十几个行业得到应用.     

反应等离子喷涂制备FeAl2O4-Al2O3-Fe涂层的性能研究

对反应等离子喷涂制备的FeAl2O4-Al2O3-Fe金属／陶瓷复合涂层的性能进行了研究。结果表明该复合涂层显微硬度存在压痕尺寸效应，并符合Meyer公式，其Meyer指数约为1．75；复合涂层以穿晶断裂为主，断口存在较大起伏，并具有金属拔出机制和韧窝明显的韧性断裂特征，复合涂层韧性较好；涂层结合性能好，结合强度约23．03MPa，要高于普通AT13陶瓷涂层；涂层较致密，孔隙率约为3．33％，低于普通AT13陶瓷涂层。     

大尺寸TiB2-Cu-Ni金属陶瓷块体的燃烧合成及准热等静压致密化

利用燃烧合成结合准热等静压 (PHIP)技术成功制备了直径为 2 40mm的大尺寸TiB2 Cu Ni金属陶瓷 ,对合成产物进行了X射线衍射 (XRD)、扫描电镜 (SEM)和力学性能等实验研究。XRD结果表明反应产物中只有TiB2 和 (Cu ,Ni)两相。SEM分析发现增强相TiB2 陶瓷颗粒已经形成骨架状 ,其间为 (Cu ,Ni)基体相 ,TiB2 颗粒形貌为近等轴状 ,尺寸细小且较均匀。合成产物的致密度为 94.2 % ,弯曲强度和断裂韧性分别达到 5 99.4MPa和12 .5 6MPa·m1/ 2 。     

SHS-PHIP法制备TiC-Ni(Mo)金属陶瓷

采用Ti粉、碳黑、Ni粉和Mo粉的混合物，通过自蔓延高温合成(SHS)结合准等静压(PHIP)方法制备了TiC—Ni(Mo)金属陶瓷材料。X射线衍射结果表明，材料由TiC相和Ni合金粘结相组成。扫描电镜观察，球形的TiC颗粒较均匀地分布在Ni合金粘结相中,TiC颗粒尺寸约为2～4μm，在局部较大的TiC颗粒之间存在微孔缺陷。SHS—PHIP法制备的TiC—Ni(Mo)金属陶瓷材料具有良好的致密性和优良的力学性能。     

Ni粘结的Ti（C,N）金属陶瓷的横向断裂强度与断口的分形分析

以分维几何学为基础，建立了断口二次电子像的分维Ｂｒｏｗｎｉａｎ模型，提出了以图像处理系统为手段的断口形貌的分维测量方法，研究了Ｎｉ粘结的Ｔｉ（Ｃ，Ｎ）金属陶瓷在三点弯曲条件下，断裂表面的分形维数与横与断裂强度与显微组织之间的关系，建立了金属陶瓷的微观断裂的Ｆｒａｃｔａｌ模型，给出断口分形维数的计算表达式，实验结果表明，横向断裂强度的对数值ｌｇσｂｂ随分形维数ＤＦ增加呈单调上的直线关系；显微组织的对