Effect of microbial hydrogen consumption on the hydrogen permeation behaviour of AISI 4135 steel under cathodic protection

The feasibility of microbial hydrogen consumption to mitigate the hydrogen embrittlement (HE) under different cathodic potentials was evaluated using the Devanathan-Stachurski electrochemical test and the hydrogen permeation efficiency η. The hydrogen permeation efficiency η in the presence of strain GA-1 was lower than that in sterile medium. The cathodic potential inhibited the adherence of strain GA-1 to AISI 4135 steel surface, thereby reducing the hydrogen consumption of strain GA-1. The adherent GA-1 cells were capable of consuming ‘cathodic hydrogen’ and reducing the proportions of absorbed hydrogen, indicating that it is theoretically possible to control HE by hydrogen-consuming microbes.     

浅析火力发电厂汽水系统中内径管与外径管的设计选择

按照管道加工工艺的不同,管道可分为内径控制管和外径控制管。通过热轧工艺生产的外径控制无缝钢管,可满足火力发电厂汽水系统中绝大部分管道的使用要求。对于超(超)临界机组的主蒸汽和高温再热蒸汽管道采用的P91/P92材质的大口径厚壁无缝钢管,由于对材料性能和加工工艺有特殊要求,因此宜采用内径控制管。     

基于振动实测的非均质地层钻头失效分析与对策

四川盆地作为国内页岩气开发的重点区域,通过近几年的不断攻关和实践,机械钻速得到了提高,但由于受地层复杂、可钻性差、非均质性强等地质因素的影响,导致井下钻柱系统不良振动剧烈,容易出现钻头损坏严重、钻速较低等问题,严重影响了钻井时效。为了解决上述难题,以该盆地涪陵工区上二叠统龙潭组—中二叠统茅口组为例,采用井下振动高频测量工具的实测手段,测量了钻头—钻柱系统的动态振动加速度参数,结合地层的岩性和矿物组分分析,研究钻头失效原因与对策,并开展了现场试验。研究结果表明:①在非均质地层中钻进的钻头—钻柱系统产生了大于40 m/s~2的高幅值瞬时冲击振动,高幅值的瞬时冲击是导致钻头先期失效的主要原因;②提出了抑制高幅值的瞬时冲击振动采用"减振+增压"工具组合和避免井下工具共振的钻井参数;③采用钻井新参数的试验井比邻井的高幅值瞬时振动降低了17%,单只钻头进尺增加24%,钻头工作环境得到了较大的改善,钻头使用数量减少。结论认为,该研究成果能够有效地改善钻头—钻柱系统的振动状态,有利于达成延长钻头使用寿命的目标。     

随钻扩眼工具及技术研究

基于随钻扩眼技术优势的分析，研究了机械式、液压式和偏心式随钻扩眼工具执行机构和扩眼总成的机构原理，并介绍了国内所开展的相关研究。文章提出应加强现有工具的适应性和匹配性研究，发掘各类工具的优势。优化执行机构、扩眼总成和水力机构、重视底部钻具组合力学特性的分析是今后发展和完善随钻扩眼工具及技术的几个重要内容。实践表明，随钻扩眼技术在处理井下复杂情况、降低钻井综合成本、提高钻井速度、提高建井质量和安全性等方面具有显著的优势，随钻扩眼工具也正逐渐成为一种重要的石油钻井配套工具。     

最大塑性功原理在烧结体上限分析中的应用

最大塑性功原理又称第二塑性变分原理，在致密体塑性变形分析叶l是运用能量法进行变形力能计算的基础。本文从分析Drucker公设的亢要条件出发，证明了烧结体塑性变形最大塑性功原理的存在，片在该原理的荩础卜，推导出塑性变形的上限功率表达式，并以平面挤压条件下的上限法应用作为实例加以说明。     

Effects of Rare Earths on Toughness of 31Mn2SiRE Wear-Resistance Cast Steel

The toughness of 31Mn2SiRE wear-resistance cast steel were increased by means of RE compound modification and high temperature austenitizing. The results show that the microstructures can be refined, needle and network ferrite are eliminated, the dislocation density and the quantity of dislocated martensite are increased remarkably, and the shape and distribution of inclusions are improved by the addition of RE. Therefore, the mechanical properties of the modified steel can be greatly increased, especially the toughness (αK) by 44%, yield strength (σs) by 10%, and elongation (δ5) by 42%.     

指纹考勤管理软件的研究与实现

针对企、事业单位原有的考勤系统，如打卡钟、磁卡、IC卡等考勤方式存在代打卡、卡丢失等不足和缺陷的实际，结合指纹识别技术，建立一套考勤、薪资、人事管理于一体的软件系统。给出了系统的体系结构和功能实现，能使企业考勤管理更加简便快捷、客观公正。并提出了进一步的发展方向和展望。     

不锈钢塔器在硫酸装置中的应用

摘 要:主要介绍Sasol Agri公司硫酸四系统的技术改造,分两步进行,第一步更换转化器、热换热器及主省煤器,生产能力由1600t/d提高到1750 t/d,且鼓风机出口压力很低。第二步更换干燥塔、二吸塔及冷换热器,连续生产能力在1950 t/d以上。使用不锈钢材质及克瓦纳·凯密迪公司专有的换热器,使装置的改造相当成功,维护及操作费用较低,并具有较大的灵活性和可操作性。     

腐蚀引起钻柱刺漏的机理分析及预防措施

详细分析了腐蚀引起钻柱刺漏的机理，得知：造成钻柱刺漏的主要原因是空气中的O2、地层中的硫化氢和二氧化碳、钻井液残液、钻井液中的盐类对钻柱的腐蚀和钻井液对钻柱的冲蚀。针对引起钻柱刺漏的原因，制定了去除钻井液中的O2、监测钻井液腐蚀性并加入相应的添加剂去除CO2和H2S、定期对钻杆进行检测、对存放的钻杆进行防腐处理、使用厚过渡区改进型钻杆等措施。在苏丹某区块现场实践证明，采取这些措施，由腐蚀引起的钻柱刺漏事故大大减少，在该区块的T-1井和D-1井钻进的3个月中，仅发生一次钻柱刺漏事故。     

印制电路板翘曲弓形的模具整平法

当PCB板发生翘曲,用常规方法整平仍达不到出货要求时,推荐采用弓形模具进行整平。