STRUCTURAL DETERMINATION OF TITANIUM-OXIDE NANOPARTICLES BY X-RAY ABSORPTION SPECTROSCOPY

As a potential application of titanium-oxide nanoparticles, it is extremely important to investigate a detailed picture of the surface and interior structural properties of nanocrystalline materials, such as rutile and anatase with diameters 7.0 and 4.5nm, respectively. X-ray absorption spectroscopy has been used to identify the local Ti environment and related electronic structure. We combine the experimental results at the Ti edge in both bulk and nano-crystals to determine the lattice distortion in terms of differently characteristic preedge features and the variation in the multiple-scattering region of X-ray absorption near-edge structure (XANES) spectra. The relationship between the transition peaks and the surface-to volume ratio is also discussed.     

阻燃OMMT/WPU纳米复合材料的制备及性能研究

采用端羟基聚丁二烯（HTPB）剥离层状有机蒙脱土（OMMT）为纳米片层,并与异佛尔酮二异氰酸酯（IPDI）、二羟甲基丙酸（DMPA）等单体通过原位聚合法制备了OMMT纳米片改性的水性聚氨酯（OWPU）纳米乳液及胶膜。利用小角XRD、TEM、DLS、EDS、TGA、LOI、CONE以及SEM对样品的结构和性能进行了表征。结果表明,HTPB剥离的OMMT纳米片的衬度均匀,完整性较好;改性后OWPU的乳液粒径增大,胶膜的弹性模量、热稳定性、抗熔滴性和阻燃性能均得到明显地改善,其中弹性模量可提高59.4%,热释放速率峰值可降低36.9%;燃烧炭渣表面形貌显示,瓦片状蒙脱土相互穿插形成了具有团簇结构的蒙脱土覆盖层。     

N,N−二甲基−二硫代甲酰胺丙磺酸钠对THPED体系化学镀铜的影响

研究了N,N?二甲基?二硫代甲酰胺丙磺酸钠(DPS)作为添加剂对以四羟丙基乙二胺(THPED)为单一配位剂的化学镀铜体系的沉积速率、镀层形貌和晶体结构的影响。结果发现,当DPS的质量浓度从0 mg/L增大到1.0 mg/L时,沉积速率从2.91μm/h提高到6.73μm/h,所得镀层结晶均匀、细致。线性扫描伏安测量结果表明,DPS是通过促进甲醛的阳极氧化来加速化学镀过程。本体系的Cu镀层主要呈面心立方多晶取向,DPS的添加会令晶面取向从(220)转变为(111)。     

化学镀镍内应力的研究

用于非金属电镀、电铸、化学镀、化学铸的现行许多化学镀镍工艺,总是在零件尖端部位发生崩裂,在镜面光洁的地方易起泡,这种难题至今未得到很好解决,这大大限制了化学镀镍的应用.针对这种情况,采用正交实验方法开发出一个低温、低内应力化学镀镍工艺,初步探讨了沉积层内应力与各工艺参数之间的关系,以及作为添加剂的糖精在化学沉积层中的作用机理,并对内应力和结合力的关系作了简介.实践证明了该工艺在短时间内能于多种复杂形状或镜面光亮的非金属表面上获得完整的化学镍沉积层.     

化学镀钴-磷基多元合金的研究现状

由于钴－磷基合金膜具有优异的磁性能和较高的耐蚀性，能有效的用于数字存储装置，已引起人们的极大关注。     

Studies on Preparation of Onion-like Fullerenes by Vacuum Heat-treatment

Onion-like Fullerenes were produced at high-temperature in vacuum. The morphology of the carbon nano onion-like fullerenes was examined and characterized by high-resolution transmission electron microscopy (HRTEM). It can be seen that the nano-sized, onion-like fullerenes possess high degree of graphization. The results suggested that the catalyst is the main factor affecting the size and yield of the fullerenes. The method is very promising for simple mass production.     

Low temperature bonding of LD31 aluminum alloys by electric brush plating Ni and Cu coatings

0Introduction Amongavarietyofbondingtechnologies,vacuum brazinghasbeenwidelyadoptedasareliablemethodfor joiningaluminumcomponents[1],whereintheAl Sialloys systemisrecognizedasthemostpopularfillermetals[2,3]. Althoughasoundjointcanbeachievedforcertainalumi…     

印制板化学镀镍

介绍了采用金属Zn粒子悬浮液活化要镀镍的印制板(PCB)Cu电路表面,使其可以进行化学镀镍的工艺方法,它可以克服Pd-Sn活化的缺点.     

化学沉积Ni-Zn-P合金制备和腐蚀性能研究

采用柠檬酸钠为络合剂 ,在氨性缓冲介质中化学镀Ni Zn P合金 .考察了工艺参数 (pH、ZnSO4·7H2 O浓度和温度 )对沉积速度和镀层组成的影响 .发现Zn离子在沉积过程中起阻碍作用 ,致使镀层中Zn含量不高 (最多含16 .0mass% ) .采用差示扫描量热 (DSC)和X射线衍射 (XRD)技术研究所得化学镀Ni Zn P合金 (Ni=78.7mass % ,Zn =11.7mass % )的晶化行为和结构 .结果表明 ,镀态Ni Zn P合金主要由非晶相和少量立方镍两相构成 .热处理至 384 .8℃时出现四方Ni3 P相 ,至 5 80 .7℃时出现Ni5Zn2 1相 .镀态及热处理后的Ni Zn P合金 (Ni=78.7mass% ,Zn =11.7mass% .)在 3.5 %NaCl中 (pH =7.0 )的腐蚀失重及阳极极化测量 .结果表明 ,该合金的耐腐蚀性能优良 ,特别是镀态Ni Zn P合金 .     

次亚磷酸盐溶液电镀三价铬工艺的电化学

研究了次亚磷酸盐溶液电镀三价铬工艺的溶液化学性质，对镀液中三价铬离子与次亚磷酸根离子的配位化合物进行了探讨。用线性电势扫描法、循环伏安法研究了镀液的电化学特征及镀液中氟离子、次亚磷酸根离子、溶液ｐＨ值对阴极析氢反应的影响。讨论了获得最佳电流效率的条件