Methane oxidation over vanadium-modified Pd/Al2O3 catalysts

Three different vanadium-modified Pd/Al₂O₃ catalysts were prepared and tested as catalysts for the deep oxidation of methane. Vanadium was added to the palladium catalyst by incipient wetness of palladium catalyst in order to modify its properties and improve its thermal stability and thioresistance. The behaviour of vanadium-modified catalysts depends on the concentration of this compound, being 0.5 wt.% the optimum amount. However, when strong catalyst poisons are present in the gas (SO₂), these modified catalysts do not show a better performance than unmodified catalyst. Bimetallic catalysts were tested with and without further reduction, being observed that reduced bimetallic catalysts perform worse than the non-reduced ones.     

CeO2对RuO2／γ-A12O3催化剂湿式氧化降解苯酚性能的影响

采用浸渍法制备了RuO2／γ-A12O3和RuO2／CeO2／γ-A12O3催化剂，并利用XRD、SEM和XPS对催化剂进行了表征，研究了Ce的加入对RuO2／γ-A12O3催化剂表面分散性和催化剂表面元素Ru，O和Ce化学态的影响，同时考察了RuO2／γ-A12O3和RuO2／CeO2／γ-A12O3催化剂湿式氧化降解苯酚的活性，并深入探讨了Ce对RuO2／γ-A12O3催化剂的助催化作用。结果表明：Ce掺杂改性后，使催化剂表面Ru的化学态降低、表面氧空位增加，并且活性组分Ru的分散性增加，从而使RuO2／CeO2／γ-A12O3催化剂的活性提高，因此Ce起到了显著的助催化作用。     

Oxidation of doped europium in BaMgAl10O17 by annealing studied by x‐ray‐absorption fine‐structure measurements

Abstract— We studied the influence of annealing in air on doped europium in BaMgAl₁₀O₁₇ by performing x‐ray absorption fine‐structure measurements. We determined the oxidation of doped divalent europium by annealing in air at over 500°C. The interatomic distance between the europium and the surrounding oxygen atoms was compressed by oxidation. It also appears that the oxidation process of europium is determined by the diffusion of oxygen into BaMgAl₁₀O₁₇.     

激光抛光技术的发展与展望

介绍激光抛光技术的发展历史,阐明激光抛光的应用现状及未来的发展前景,论述了激光抛光的工艺特点和作用机理,将激光抛光技术与其它抛光技术进行了全面的对比,指出激光抛光的优势及其存在的问题。     

垂直磁记录介质薄膜研制的新途径(英文)

本文阐述了铝氧化电沉积法获得磁记录材料的基本原理,研究了铝交流氧化膜中沉积磁性金属及其合金制备垂直磁记录薄膜的新途径,建立了铝交流氧化电沉积法,探讨了氧化膜的结构和磁特性的关系。     

A novel way to treat refractory waste: Sonication followed by wet oxidation (SONIWO)

The effectiveness of the hybrid system sonication followed by wet oxidation (SONIWO) to treat otherwise refractory waste has been demonstrated. In such a hybrid system homogeneous CuSO₄ catalyst was found to be very efficient.     

Nitric oxide reduction and carbon monoxide oxidation over carbon-supported copper-chromium catalysts

Carbon supported copper-chromium catalysts are shown to be very active for both the reduction of nitric oxide with carbon monoxide and the oxidation of carbon monoxide with oxygen. Mixed copper-chromium oxide active phases have good activity in the simultaneous removal of nitric oxide and carbon monoxide from exhaust gases. The influence of several catalyst variables has been investigated. The activity per volume of catalyst increases with increasing loading, while the intrinsic activity shows a maximum around C/M=100−50. An optimum catalyst for nitric oxide reduction and carbon monoxide oxidation has a copper/chromium ratio of 2/1. The apparent activation energy for the carbon monoxide oxidation over carbon supported copper-chromium catalysts is 77 kJ/mol, suggesting that the Cu---O bond rupture is the rate-limiting process. The reduction of nitric oxide takes place at higher temperatures. Since all catalysts have a low selectivity for molecular nitrogen formation at lower temperatures, the dissociation of nitric oxide is probably rate determining, resulting in a slightly reduced catalyst system. In an excess of carbon monoxide the reaction is first-order in nitric oxide and zero-order in carbon monoxide. Moisture inhibits the reaction by reversible competitive adsorption, whereas carbon dioxide does not. Oxygen completely inhibits the reduction of nitric oxide due to the more rapid reoxidation of the catalytic sites compared to nitric oxide. Therefore, the reduction of nitric oxide takes place only when all oxygen has been converted and, hence, is shifted to higher temperatures. As a possible consequence, the production of nitrous oxide is reduced. Nitric oxide and molecular oxygen react preferentially with carbon monoxide, so, in an excess of oxidizing component, gasification of the carbon support occurs at higher temperatures after carbon monoxide has been completely consumed.     

Dietary α-Tocopheryl Acetate Enhances Beef Quality in Holstein and Beef Breed Steers

The effect of long-term feeding (252 days) of three supplemental levels of α-tocopheryl acetate (actual 0, 360 and 1290 IU/head/day) on meat quality was evaluated in Holstein and beef breed steers. Tissue vitamin E concentrations were increased by each increment of supplementation. The color display life of fresh beef under simulated retail conditions was extended 2 to 5 days by vitamin E and lipid oxidation was markedly reduced. Microbial population was not affected by level of supplementation. No deterioration in sensory quality occurred for steaks from supplemented steers that were displayed until the time steaks from unsupplemented steers discolored.     

异丙苯在Cu-HMS分子筛上的催化氧化

以含Cu的中孔分子筛(Cu-HMS)为催化剂,研究异丙苯的催化氧化。研究发现,Cu-HMS催化剂的加入使异丙苯氧化的诱导期显著缩短。在75℃下,以Cu-HMS为催化剂,O2为氧化剂的纯异丙苯氧化反应,苯乙酮为主要副产物,反应的选择性和转化率都很高。当催化剂用量为1 5×10-4mol/ml时,反应8h后,异丙苯转化率为32 7%,目的产物的累积浓度(质量分数)为37 7%,选择性为99%;反应12h后,异丙苯转化率为42 4%,目的产物的累积浓度为46 3%,选择性为95 6%。     

Comparison of inward and outward grown Pt modified aluminide diffusion coatings on a Ni based single crystal superalloy

Two commercial Pt modified aluminide coatings (RT22 and MDC150L) on the same single crystal Ni-based superalloy (CMSX-4) were studied by: scanning electron microscopy; transmission electron microscopy; energy dispersive X-ray spectrometry; and gravimetry. The RT22 coating is an inward grown coating (high activity), while MDC150L is produced by outward growth (low activity). Samples were oxidised in still laboratory air at 1050 °C for various times up to 2000 h. It was found that the outward grown coating produced a slower growing oxide that was more spallation resistant. Several possible reasons for this were identified including: coating purity; coating surface topography; and ductile to brittle transition temperature. The microstructural differences between the two coatings in the as-coated condition were investigated and the development of their microstructure during heat treatment was described. A model for coating growth during heat treatment was proposed.