Synthesis and characterization of biocompatible hydroxyapatite coated ferrite

Ferrite particles coated with biocompatible phases can be used for hyperthermia treatment of cancer. We have synthesized substituted calcium hexaferrite, which is not stable on its own but is stabilized with small substitution of La. Hexaferrite of chemical composition (CaO)_0.75(La₂0₃)_0.20(Fe₂O₃)₆ was prepared using citrate gel method. Hydroxyapatite was prepared by precipitating it from aqueous solution of Ca(NO₃)₂ and (NH₄)₂HPO₄ maintaining pH above 11. Four different methods were used for coating of hydroxyapatite on ferrite particles. SEM with EDX and X-ray diffraction analysis shows clear evidence of coating of hydroxyapatite on ferrite particles. These coated ferrite particles exhibited coercive field up to 2 kOe, which could be made useful for hysteresis heating in hyperthermia. Studies by culturing BHK-21 cells and WBC over the samples show evidence of biocompatibility. SEM micrographs and cell counts give clear indication of cell growth on the surface of the sample. Finally coated ferrite particle was implanted in Kasaulli mouse to test its biocompatibility. The magnetic properties and biocompatibility studies show that these hydroxyapatite coated ferrites could be useful for hyperthermia.     

BaTiO3基Au纳米颗粒复合薄膜的制备及其光学性质研究

采用溶胶-凝胶（sol-gel）方法，成功的将高体积面分比的Au纳米颗粒复合到BaTiO3的非晶薄膜中，并对其光学性质进行了研究。用XRD、TEM、椭偏仪、吸收光谱、光克尔效应OKE（Optical Kerr Effcet）方法对薄膜进行了表征和测试。从吸收光谱观察到表面等离子体共振SPR（Surface Plasma Resonance)峰随热处理温度升高而红移的现象。光学非线性测试表明薄膜具有高的三阶非线性极化率Χ^(3)和超快的响应时间。     

Ni-Al2O3纳米复合电镀工艺的初步研究

初步研究了复合电镀各工艺条件：电流密度、镀液pH值和温度以及搅拌方式对Al2O3纳米微粒在镍基复合镀层中含量的影响。研究表明：电流密度增大不利于提高镀层中纳米微粒的含量；pH值增大也明显使复合量降低;镀液温度升高，镀层中微粒的复合量随之略有改变；电镀时，加强搅拌或适当改变搅拌方式，可以使复合镀居中的纳米微粒含量提高。还利用扫描电镜及能谱对Ni-Al2O3镀层表面进行了观察与分析。     

Oxidation of Hastelloy-XR Alloy for Corrosion-Resistant Glass-Coating

The oxidation behavior of Hastelloy-XR alloy was investigated to obtain the optimum surface condition for corrosion-resistant glass-coatings. The surface morphology of oxide scales changed significantly with variation of temperatureand oxygen partial pressure (po2 ). The oxidation kinetics was mainly parabolic independent of oxidation conditions.The oxide scales were consisted of inner Cr2O3 and outer spinel layers. The phase component of spinel layers wereMn1.5Cr1.5O4 and (Mn,Ni)(Cr,Fe)2O4 for the oxygen partial pressures po2<10 kPa and po2>10 kPa, respectively.The optimum oxidation condition to obtain an oxide scale for well-adhered glass-coating to the substrate was 1248 Kand po2 =0.01 kPa for the oxidation time of 43 ks.     

等离子体刻蚀工艺控制模型分析

讨论了主因素分析法以及神经网络法在等离子体刻蚀工艺中的应用.结果表明主元素分析法可以实现对数据的压缩,而神经网络算法则显示出比传统的统计过程控制算法更好的准确性.     

磁电雾化电晕放电低温等离子体及其应用

本文讨论了磁电雾化电晕放电低温等离子体技术的基本原理,以及它在静电除尘、烟气脱硫等环保生物工程等领域中的应用前景.     

TEM Studies of High Temperature Corrosion Behaviour of TiAl Intermetallics with Surface Modifications

The oxidation/sulphidation behaviour of a Ti‐46.7Al‐1.9W‐0.5Si alloy with a TiAl₃ diffusion coating was studied in an environment of H₂/H₂S/H₂O at 850^oC. The kinetic results demonstrate that the TiAl₃ coating significantly increased the high temperature corrosion resistance of Ti‐46.7Al‐1.9W‐0.5Si. The SEM, EDX, XRD and TEM analysis reveals that the formation of an Al₂O₃ scale on the surface of the TiAl₃‐coated sample was responsible for the enhancement of the corroison resistance. The Ti‐46.7Al‐1.9W‐0.5Si alloy was also modified by Nb ion implantation. The Nb ion implanted and as received sampels were subjected to cyclic oxidation in an open air at 800^oC. The Nb ion implantation not only increased the oxidation resistance but also substantially improved the adhesion of scale to the substrate.     

纳米ZrO2等离子涂层的结构,性能和工艺特点

采用大气等离子喷涂技术(APS)，制备了常规氧化锆和纳米结构氧化锆两种涂层．利用扫描电镜(SEM)对涂层的显微结构进行了观察．对两种涂层的沉积效率、表面粗糙度和显微硬度作了对比研究．结果表明，粉末原料的显微结构、粒度、形态、喷涂工艺参数(喷涂功率和距离)对涂层的显微结构有较大的影响．等离子喷涂造粒纳米氧化锆粉制备的涂层沉积效率高而稳定，其显微结构与喷涂功率和距离密切相关．与常规氧化锆涂层相比，纳米结构氧化锆涂层具有较高的显微硬度和较低的表面粗糙度．     

Computational analysis of thin coating layer failure using a cohesive model and gradient plasticity

Thermal barrier coatings (TBC) are widely used to prevent transient high temperature attack and allow components high durability. Due to strong inhomogeneous material properties the TBC failure often initiates near the interface between the brittle oxide layer and the ductile substrate. A reliable prediction of the TBC failure requires detailed information about the crack tip field and the consequent fracture criteria. In the present paper both cohesive model and gradient plasticity are used to simulate the failure process and to study interdependence of the interface stress distribution with the specific fracture energies. Computations confirm that combination of the two models is able to simulate different failure mechanisms in the TBC system. The computational model has the potential to give a realistic prediction of the crack propagation process.     

化学复合镀层激光处理研究

研究了激光处理对Ni-P -SiC化学复合镀层的影响。借助于扫描电镜、能谱仪、X射线衍射、显微硬度计等设备对激光处理后复合镀层的表面形貌、组织结构及性能进行了综合分析。结果表明 ,对复合镀层进行激光处理可以获得与炉内加热同样的镀层硬度 ,且当激光功率 4 0 0W ,扫描速度 1.5m /min时 ,镀层硬度高于炉内加热的硬度