40CrNi2Si2MoVA钢制零件磁痕显示分析

本文采用磁粉、X射线、CT和超声等无损检测和金相分析等方法对40CrNi2Si2MoVA钢制零件的磁痕显示进行了系统分析.研究认为,40CrNi2Si2MoVA钢制零件的磁痕显示为显微成分沿变形方向偏析导致的马氏体转变点Ms差异所致.显微成分偏析是钢锭结晶过程中不可避免的,但可通过优化熔炼工艺参数降低显微偏析的程度.本文还分析了四种磁痕显示的类型及其判别方法.     

Fe-Cr-Mn奥氏体合金的辐照体胀与诱起晶界偏析行为的研究SCIEI

本文采用电子束辐照,研究了Fe-15Cr-xMn合金以及添加W,V合金的孔洞体胀和诱起晶界偏析行为,并对包含晶界在内的辐照区进行成分分析。结果表明,在Fe-Cr-Mn系合金中孔洞体胀孕育期可以被强烈抑制,晶界偏析也减少。特别是,合金中添加W,V效果更加明显。用Mn代替Ni,通常要发生体胀和相的不稳定性,由于反Kirkendall效应导致Ni和Mn的扩散行为不同,使Fe富集在尾闾处,局部地区形成铁素体,有利于减少体胀和晶界偏析。     

The influence of grain-boundary segregation of Y in Cr2O3 on the oxidation of Cr metal

The oxidation behavior at 900°C of pure Cr and Cr implanted with 2×10¹⁶ Y ions/cm² was studied. The kinetics of oxidation were measured thermogravimetrically and manometrically. The mechanisms of oxide growth were studied using¹⁸O-tracer oxidation experiments, and the composition and microstructure of the oxide scales were characterized by TEM and STEM. Segregation of Y cations at Cr₂O₃ grain boundaries was found to be the critical factor governing changes in the oxidation behavior of Cr upon the addition of Y. In the absence of Y, pure Cr oxidized by the outward diffusion of cations via grain boundaries in the Cr₂O₃ scale. When Y was present at high concentration in the scale, as when Cr implanted with 2×10¹⁰ Y ions/cm² was oxidized, anion diffusion predominated. It is concluded that strain-induced segregation of Y at grain boundaries in the oxide reduced the cation flux along the grain boundaries. The rate of oxidation was reduced because the grain-boundary diffusivity of cations became lower than the grain-boundary diffusivity of the anions, which then controlled the rate of oxidation. Changes in the relative rates of Cr³⁺ and O^2– transport, as well as a solute-drag effect exerted by Y on the oxide grain boundaries, resulted in changes in the microstructure of the oxide.     

A study on centrifugal casting of high speed steel roll

High speed steel (HSS) rolls can replace traditional rolls such as alloyed cast iron rolls and powder metallurgical (PM) hard alloy rolls. The main reasons for the replacement are that the wear resistance of low-cost alloyed cast iron rolls is poor and the cost of high-quality PM hard alloy rolls is very high. By means of centrifugal casting, HSS rolls having excellent wear resistance have been manufactured. The hardness of the HSS roll is 65～ 67 HRC, the range of variation is smaller than 2 HRC and its impact toughness is 15 J/cm2. The wear rate of HSS rolls used in the pre-finishing stands of high-speed hot wire-rod rolling mill reaches 2.5 × 10-4 mm per ton steel. Furthermore, the manufacturing cost of HSS rolls is significantly lower than that of PM hard alloy rolls; it is only 30 percent of that of PM hard alloy rolls.     

铸造Al-Cu合金凝固缺陷研究现状

铸造Al-Cu合金的凝固缺陷严重影响了铸件的性能,控制或消除凝固缺陷对提高铸件成品率有重大意义。综述了铸造Al-Cu合金在工程中出现的常见凝固缺陷,如偏析、热裂、显微疏松、缩孔等。重点分析了各类缺陷的形成机理与特点,从合金化、熔铸工艺、热处理工艺、数值模拟等角度提出了减少铸造Al-Cu合金凝固缺陷的方法。     

大塑性变形制备超细晶/纳米晶Al-Mg铝合金的研究进展

近年来,大塑性变形(SPD)制备具有先进结构和功能的超细晶和纳米晶Al-Mg铝合金的研究取得了很大进展。SPD后,合金的晶粒显著细化、位错密度提高及有非平衡晶界和晶界偏析形成,这些微观结构导致合金的强度、硬度大幅提高。然而,SPD合金的塑性普遍较低。综述了SPD制备的Al-Mg铝合金在结构和性能方面的一些最新研究成果。     

超重力场凝固对Cu-1.6%Cr共晶合金组织的影响

本实验分别在普通重力场和4230g超重力场下制备了Cu_(98.4)Cr_(1.6)合金的凝固样品,研究了重力场对Cu_(98.4)Cr_(1.6)合金棒状共晶尺寸和宏观偏析情况的影响。结果表明:与普通重力场的凝固组织相比,当Cu_(98.4)Cr_(1.6)合金棒状共晶在4230g超重力场下凝固时,棒状共晶组织得到了明显的细化,其直径由250~350nm降至100~200nm。同时,Cu_(98.4)Cr_(1.6)共晶合金沿超重力场方向的硬度和成分分布基本一致,未出现明显的宏观偏析。     

基于三维LBM-CA模型模拟Al-4.7%Cu合金的枝晶形貌和成分分布

建立了三维格子玻尔兹曼方法(LBM)-元胞自动机(CA)耦合数值模型,并用该模型模拟研究了Al-4.7%Cu(质量分数)固溶体合金的凝固过程。该耦合模型采用元胞自动机方法模拟枝晶的生长,同时采用基于分子动力学理论的格子玻尔兹曼方法模拟合金凝固过程中的温度场、流场以及溶质场。模拟结果再现了合金凝固过程中的三维枝晶形貌变化以及溶质富集过程,并将三维流场因素考虑进去,定量研究了自然对流、过冷度对单枝晶形貌和成分分布的影响。研究表明,在纯扩散条件下,枝晶呈现对称的生长现象,模拟自由枝晶稳态生长的尖端速度、尖端半径和过冷度的关系与Lipton-Glicksman-Kurz(LGK)理论模型吻合得较好。在自然对流条件下,枝晶的生长形貌呈现不对称性,即枝晶生长在迎流方向上得到了促进,在顺流方向上受到了抑制。熔体过冷度对枝晶生长的影响较大,过冷度的增加导致枝晶生长加快,二次枝晶增多且呈现出粗化现象,枝晶尖端固液界面处的溶质浓度偏高,加重了溶质偏析。     

一种信息泄漏的新方式及其应对策略

文章基于验证和解决信息设备内存储器存在的信息安全泄漏隐患,提出了内存储器信息泄漏概念并对内存储器存在信息泄漏的原因做了介绍。实测发现现有内存储器存在信息泄漏状况,基于此,该文提出了基于公共信息网和文件型恶意代码窃取的内存储器信息泄漏方式并完成了实测过程,文章结论对于信息安全保密领域的内存储器信息泄漏隐患防护具有重要意义,尤其适用于安全隔离和信息交换等信息系统领域,具有较广泛的应用前景和重大的社会意义。     

基于计算听觉场景分析和语者模型信息的语音识别鲁棒前端研究

传统抗噪算法无法解决人声背景下语音识别(Automatic speech recognition, ASR)系统的鲁棒性问题. 本文提出了一种基于计算听觉场景分析(Computational auditory scene analysis, CASA)和语者模型信息的混合语音分离系统. 该系统在CASA框架下, 利用语者模型信息和因子最大矢量量化(Factorial-max vector quantization, MAXVQ)方法进行实值掩码估计, 实现了两语者混合语音中有效地分离出目标说话人语音的目标, 从而为ASR系统提供了鲁棒的识别前端. 在语音分离挑战(Speech separation challenge, SSC)数据集上的评估表明, 相比基线系统, 本文所提出的系统的语音识别正确率提高了15.68%. 相关的实验结果也验证了本文提出的多语者识别和实值掩码估计的有效性.