Corrosion behavior of under‐, peak‐, and over‐aged 6063 alloy: A comparative study

The mechanical property of age‐hardenable Al‐alloys is governed by the state of ageing, which determines the microstructure and consequently, their corrosion behavior which is a vital aspect for a number of applications. This article presents a comparative assessment of corrosion behavior of under‐, peak‐ and over‐aged Al‐Mg‐Si alloy. Corrosion characteristics have been determined via immersion tests in 0.1 M ortho‐phosphoric acid solution and intergranular corrosion (IGC) tests. Corroded surfaces are examined by field emission scanning electron micrographs‐energy dispersive spectroscopy and 3D optical profilometer. The obtained results reveal that the corrosion rate at a specific immersion time as well as the depth of IGC increases in the order for under‐, peak‐, and over‐aged states. Irrespective of the state of ageing, corrosion loss increases linearly but the rate of corrosion decreases rapidly with increasing immersion time. The dominant mode of corrosion in under‐aged alloy is identified as localized pitting, while peak‐aged is highly susceptible to IGC in contrast extensive pitting corrosion is observed for over‐aged alloy. The observed differences in corrosion behavior are explained considering characteristics of precipitates. Formation of β (Mg₂Si) in case of over‐aged alloy and presence of inclusions like AlFeMnSi particles are found to accelerate pitting corrosion.     

The influence of volume fraction of amorphous phase on corrosion resistance of Mg67Zn 29Ca 4 alloy

The aim of this study was to investigate the structure and corrosion resistance of amorphous, amorphous‐crystalline, and crystalline Mg₆₇Zn₂₉Ca₄ alloy for biodegradable applications. This paper presents a preparation method and results of the structural characterization and corrosion resistance analysis of the material. Samples were prepared in the form of 3 mm diameter rods. The structure of the alloy was examined with the use of X‐ray diffractometry and scanning electron microscopy. The thermal properties of the samples were examined with differential scanning calorimetry (DSC). Results of DSC analysis were used to determine heat treatment temperatures, allowing to obtain different fractures of crystalline phase in the material. Corrosion resistance of heat‐treated samples was investigated by immersion tests and electrochemical measurements performed in the simulated body fluid. The X‐ray diffraction results confirmed that the prepared Mg₆₇Zn₂₉Ca₄ alloy's structure is fully amorphous. After heat treatment, samples with different fractions of amorphous phase in the structure were obtained. Immersion tests of the samples showed that the structure significantly influenced corrosion resistance in examined materials. It should be pointed out, that certain amounts of crystalline phase in amorphous matrix can greatly improve the corrosion resistance of Mg₆₇Zn₂₉Ca₄ alloy.     

Damage mechanism at different transpassive potentials of solution-annealed 316 and 316l stainless steels

Electrochemical impedance spectroscopy (EIS), anodic polarization and scanning electron microscopy techniques were used to investigate the damage mechanism in the transpassive potential region of AISI ...     

Corrosion behavior of air plasma spraying zirconia-based thermal barrier coatings subject to Calcium–Magnesium–Aluminum-Silicate (CMAS) via burner rig test

Three different kinds of thermal barrier coatings (TBCs) — 8YSZ, 38YSZ and a dual-layered (DL) TBCs with pure Y₂O₃ on the top of 8YSZ were produced on nickel-based superalloy substrate by air plasma spraying (APS). The Calcium–Magnesium–Aluminum-Silicate (CMAS) corrosion resistance of these three kinds of coatings were researched via burner rig test at 1350 °C for different durations. The microstructures and phase compositions of the coatings were characterized by SEM, EDS and XRD. With the increase of Y content, TBCs exhibit better performance against CMAS corrosion. The corrosion resistance against CMAS of different TBCs in descending was 8YSZ + Y₂O₃, 38YSZ and 8YSZ, respectively. YSZ diffused from TBCs into the CMAS, and formed Y-lean ZrO₂ in TBCs because of the higher diffusion rate and solubility of Y³⁺ in CMAS than Zr⁴⁺. At the same time, 38YSZ/8YSZ + Y₂O₃ reacts with CAMS to form Ca₄Y₆(SiO₄)₆O/Y_4·67(SiO₄)₃O with dense structure, which can prevent further infiltration of CMAS. The failure of 8YSZ coatings occurred at the interface between the ceramic coating and the thermally grown oxide scale (TGO)/bond coating. During the burner rig test, the Y₂O₃ layer of the DL TBCs peeled off progressively and the 8YSZ layer exposed gradually. DL coatings keep roughly intact and did not meet the failure criteria after 3 h test. 38YSZ coating was partially ablated, the overall thickness of the coating is thinned simultaneously after 2 h. Therefore, 8YSZ + Y₂O₃ dual-layered coating is expected to be a CMAS corrosion-resistant TBC with practical properties.     

规整有机分子自聚集体对铜的高效缓蚀的研究

通过多步法合成了离子型含双苯并三氮唑环的目标分子，4，4'-{苯-1，3-二基二[(1E)-3-羰基丙-1-烯-1，3-二基]}二[2-(2H-苯并三唑-2-基)苯醇酸]二钾。在室温条件下，目标分子在3.5%（质量）NaCl/DMSO（二甲基亚枫）混合溶液 （体积比：40/60） 中能够发生分子自组装产生纳-微米级的自聚集体。通过傅里叶变换红外光谱 （FT-IR）、拉曼光谱和X射线光电子能谱 （XPS） 的表征，证实了所形成的目标分子自聚集体能够对铜表面产生强烈的化学吸附作用，在铜表面形成自组装膜。利用电化学方法测定了目标分子自聚集体吸附在铜表面形成自组装膜后，在3.5%（质量）NaCl溶液中的缓蚀性能。结果表明目标分子自聚集体在NaCl溶液中能高效地抑制铜腐蚀。     

Chitosan Microspheres as Carriers for pH‐Indicating Species in Corrosion Sensing

Chitosan microspheres containing bromocresol green, cresol red, and phenolphthalein for corrosion detection, through pH change, are synthesized in order to be used in protective coatings for aluminium alloys. Microspheres containing corrosion detection species are characterized morphologically (SEM) and physico‐chemically (FTIR, TGA). Release studies (UV–vis) are performed in corrosion‐promoting conditions (pH, NaCl), and detection studies by immersion in media associated with corrosion activity while microspheres' sensing activity is evaluated visually. Electrochemical characterization of AA2024 substrates in the presence of chitosan spheres is performed to understand material performance, and a color change is observed as a result of local pH increase in cathodic areas when corrosion takes place. These findings can be correlated with the results from release studies and seem a promising approach for corrosion sensing purposes, not only because pH increase is possible to detect due to corrosion, but also because chitosan is considered an environmentally friendly material.     

Corrosion behaviors of Cr2AlC/α-Al2O3 composites in 3.5 wt. % NaCl aqueous solution

Cr₂AlC and its composites containing α-Al₂O₃ (6.1 and 15.2 wt %) were prepared by hot pressing and their corrosion behaviors in air-saturated 3.5 wt % NaCl aqueous solution were investigated by electrochemical testing methods. It was revealed that the secondary phase of Al₂O₃ particles mainly distributed along grain boundaries of Cr₂AlC matrix. The potentiodynamic polarization measurements showed that the corrosion current densities of these Cr₂AlC composites were lower than that of the pure Cr₂AlC. The Aluminum in Cr₂AlC was prone to be attacked more easily. When immersed at open circuit potential (OCP), Al readily slipped out from Cr₂AlC matrix into NaCl solution in the form of dissoluble species. But in the case of polarization, regardless of potentiostatic polarization or potentiodynamic polarization, more de-intercalated Al, reacted with the electrolyte to form corrosion products of Al₂O₃ and/or AlOOH and deposited on the sample surface. For Cr₂AlC/α-Al₂O₃ composites, the presence of Al₂O₃ weakened the corrosion along grain boundaries by partly blocking the permeation of electrolyte and inhibiting the anodic dissolution process.