Reticulated Porous Multiphase Ceramics with Improved Compressive Strength and Fracture Toughness

A multiphase reticulated porous ceramic (RPC) as Si₃N₄–Al₂O₃–SiO₂ was fabricated by replication techniques. Proper volumes of additives and twice sinter- twice immerse process endow the RPC an excellent crack healing and submerging property. The compressive strength and fracture toughness improved owing to the crack bridging behavior. The existence of pores in struts in RPC blunt the crack tip and increased the external force needed to propagate the crack. The mechanisms play a beneficial role in enhancing the compressive strength and fracture strength. Si₃N₄ RPC with additives of 5%Al and 5% Al₂O₃ yielded the compressive strength of 9.8 MPa and fracture toughness of 0.3 MPa m^1/2.     

黑河右岸溢洪洞左导墙优化试验

黑河水利枢纽右岸溢洪洞为缩短引渠左导墙的长度,减少施工开挖量,降低施工难度,减少工程投资,进行优化试验.通过对7种不同的方案对比分析,选择了合适的体型,满足了工程要求.     

疲劳裂纹的灰色残差预测

借助灰色理论，建立了预测疲劳裂纹扩展的灰色残差预测模型，并应用此模型预测了某不锈钢构件腐蚀疲劳裂纹的扩展，得到了较高精度的预测结果，为疲劳裂纹预测提供了一种简易而可靠的新途径。     

大体积砼产生裂缝的原因及防治措施

大体积砼裂缝问题是建筑业普通关心的问题.对砼裂缝进行控制,就必须研究砼结构中裂缝产生的原因以及在实际的设计和施工过程中采取合理的、经济的措施来控制裂缝.本文通过对大体积砼裂缝成因的理论研究,提出了合理的裂缝控制的设计和施工措施.     

关于最远点判定及直径的唯一性

给出了点到有界集最远点的一些必要或充分条件，然后对直径的唯一性也给出了一些判定条件。     

Determination of Discrete-Structure Parameters of Coatings with Allowance for Residual Stresses

The authors suggest that the dimensions of a discrete section of a coating should be chosen on the basis of calculation of the critical crack spacing in cohesion cracking. This approach allows for residual stresses in the coating. The reliability of the calculation method has been verified experimentally by direct measurement of the crack spacing.     

软基上超长闸底板的防裂问题研究

通过北京市北运河拦河闸土基上超长闸底板大体积混凝土的温度应力仿真计算，论证了各种温度荷载（气温年变化、气温日变化、寒潮）以及水化热、自生体积变形、干缩等几种因素对混凝土内部应力的影响，并且在此基础上掺加ZY膨胀剂，计算ZY膨胀剂带来的应力补偿作用。结果表明：寒潮和干缩是带来混凝土表面裂缝的主要因素，如果不加强养护和保湿，表面裂缝很可能向内部扩展；掺加ZY膨胀剂可以有效降低混凝土中的拉应力，对防裂有利，是实现大体积混凝土超长无缝施工的有效措施。     

Performance of a non‐load‐bearing steel stud gypsum board wall assembly: Experiments and modelling

A gypsum wall assembly was exposed to an intense real‐scale compartment fire. For the wall assembly, temperatures were measured at the exposed face, within the stud cavity, and at the unexposed face during the fire exposure. Total heat flux gauges were used to measure the temporal variation of the energy incident on the walls, and cameras, both visual and infrared, were used to image the unexposed face of the wall assembly during the fire exposure. The behaviour of the wall assembly under the fire load is discussed as are current model results for a simulation of the fire test. Copyright © 2006 John Wiley & Sons, Ltd.     

海洋平台损伤检测的发展现状与展望

针对海洋平台损伤检测技术进行了分析，总结了国内外海洋平台损伤检测技术的最新进展。对各种检测方法进行了分类与比较，分析了不同检测方法的基本原理及其适用范围，提出了海洋工程结构损伤检测的二步法，可以综合利用不同的损伤检测方法，更准确、有效地对平台进行损伤检测。     

静水压力下混凝土双K断裂参数试验测定

本文主要研究混凝土在机械荷载和水压力的双重作用下，裂缝的起裂、扩展和失稳断裂情况。试验采用楔入劈拉试件，试验时每间隔一定的机械荷载，施加一个循环的一定数值的水压力，直至试件断裂。试验采用“恒定裂缝张开位移”和“恒定荷载”两种加载方式，恒定裂缝张开位移是对水压力作用下的试件进行的定性对比分析，恒定荷载是对固定水压力作用下的试件，通过表面粘贴应变片的方法监测裂缝的起裂和扩展长度。采用混凝土裂缝扩展的双K断裂准则计算了粘聚韧度、失稳韧度和起裂韧度，并与试验测定结果进行了比较。结果表明，随着水压力的逐渐增大，试件的可承受最大荷载逐渐减小，裂缝的起裂提前。