A probabilistic model for cleavage fracture with a length scale--parameter estimation and predictions of stationary crack experiments

This study presents a large experimental investigation in the transition temperature region on a modified A508 steel. Tests were carried out on single-edge-notch-bend specimens with three different crack depth over specimen width ratios to capture the strong constraint effect on fracture toughness. Three test temperatures were considered, covering a range of 85 °C. All specimens failed by cleavage fracture prior to ductile tearing. A recently proposed probabilistic model for the cumulative failure by cleavage was applied to the comprehensive sets of experimental data. This modified weakest link model incorporates a length scale, which together with a threshold stress reduce the scatter in predicted toughness distributions as well as introduces a fracture toughness threshold value. Model parameters were estimated by a robust procedure, which is crucial in applications of probabilistic models to real structures. The conformity between predicted and experimental toughness distributions, respectively, were notable at all the test temperatures.     

Dynamic crack propagation with cohesive elements: a methodology to address mesh dependency

In this paper, two brittle fracture problems are numerically simulated: the failure of a ceramic ring under centrifugal loading and crack branching in a PMMA strip. A three‐dimensional finite element package in which cohesive elements are dynamically inserted has been developed. The cohesive elements' strength is chosen to follow a modified weakest link Weibull distribution. The probability of introducing a weak cohesive element is set to increase with the cohesive element size. This reflects the physically based effect according to which larger elements are more likely to contain defects. The calculations illustrate how the area dependence of the Weibull model can be used to effectively address mesh dependency. On the other hand, regular Weibull distributions have failed to reduce mesh dependency for the examples shown in this paper. The ceramic ring calculations revealed that two distinct phenomena appear depending on the magnitude of the Weibull modulus. For low Weibull modulus, the fragmentation of the ring is dominated by heterogeneities. Whereas many cracks were generated, few of them could propagate to the outer surface. Monte Carlo simulations revealed that for highly heterogeneous rings, the number of small fragments was large and that few large fragments were generated. For high Weibull modulus, signifying that the ring is close to being homogeneous, the fragmentation process was very different. Monte Carlo simulations highlighted that a larger number of large fragments are generated due to crack branching. Copyright © 2003 John Wiley & Sons, Ltd.     

Preparation of Plate Fe_(60)Co_8Zr_(10)Mo_5W_2B_(15) Bulk Amorphous Alloy and Its Fracture Toughness

1Introduction Duwez[1]synthesizedthefoilAu Siamorphousalloyforthefirsttimewithrapidsolidification,whichinitiatedthepreparationofamorphousalloysintheprocessofalloysolidification,andthereaftertheresearchonamorphousal loysdevelopedrapidly.Since1980s,withthec…     

粗轧机前推床同步拉杆断裂的分析与改进

通过对机前推床同步拉杆的受力分析及强度计算，查找出了造成拉杆断裂的原因，并提出了解决拉杆断裂的具体措施。     

Alpha induced reactions on Sn: An experimental study of excitation functions and possible production pathways

In the frame of a systematic study of light ion induced threshold reactions on natural tin (Sn) excitation functions for alpha particles induced reactions are presented in a 12–38 MeV energy domain. Using a stacked foil activation method the following radioisotopes were identified: ¹¹⁶Te, ¹¹⁷Te, ¹¹⁸Te, ¹¹⁹Te, ¹²¹Te, ¹²³Te, ¹¹⁷Sb, ¹¹⁸Sb, ¹²⁰Sb, ¹²²Sb, ¹²⁴Sb, ¹²⁶Sb, ¹¹⁷Sn, ¹¹¹In. The experimental cross sections for these isotopes are presented for the first time in this energy range and a direct comparison with values calculated with the ALICE-IPPE code is discussed. Possible use of these data for production of some isotopes relevant in nuclear medicine is suggested.     

Stability of hydrogenated nanodiamonds under extreme ultraviolet irradiation

It is generally accepted that diamond is resistant to a wide spectrum of electromagnetic radiation from the ultraviolet through to the soft X-ray range, which makes it very attractive for the fabrication of diamond-based photodetectors. However the effect of photon radiation on the diamond structure has not yet been examined. In the work presented here, photoelectron spectroscopy has been used to study the graphitization of nanodiamond crystallites exposed to extreme ultraviolet radiation. Under such irradiation, the surface hydrogen groups and graphite species are found to prevent graphitization. The mechanism of radiation-induced nanodiamond graphitization is discussed.     

高压水射流射孔井眼应力数值模拟研究

水力射孔技术是一种新型完井方式,利用深穿透水力射孔技术辅助定向压裂,可实现油层改造和油井增产。考虑套管水泥环的影响,采用有限元理论结合ANSYS软件计算了高压水射流水力射孔井眼周围的应力,重点分析了水力射孔参数对井周应力的影响规律,初步研究了直井水力压裂时水力射孔对裂缝起裂的影响。计算结果表明,沿最大水平地应力方向布孔时,孔眼根部的周向拉应力最大,裂缝将会在孔眼根部起裂;选择合理水力射孔参数可有效降低地层破裂压力。研究结果可为高压水射流水力射孔辅助定向压裂提供参数优选的依据。     

水力压裂净压力拟合分析解释技术研究与应用

基于三维裂缝延伸模拟模型的水力压裂净压力拟合分析解释技术,提出了净压力拟合分析解释的一般步骤及理论方法,研究了现场监测净压力的计算方法,并介绍了其在现场施工中的应用情况。该技术可以帮助认识地层参数和压裂参数,提高压裂施工成功率和有效率。     

离子束辅助沉积制备高功率激光薄膜的研究

综述了离子束辅助沉积技术在高功率激光薄膜制备中的应用研究进展.指出该技术在制备高激光损伤阈值的薄膜中存在的问题,即出现过高的堆积密度,会给薄膜带来杂质缺陷、化学计量比缺陷、损伤缺陷、晶界缺陷,制备薄膜的残余应力存在着压应力增加的趋势,会改变薄膜的晶体结构等.并指出了该研究领域的研究方向.     

利用地震资料研究ZJD地区泥岩、泥灰岩裂缝的分布规律

从地层的异常孔隙流体压力、局部构造形变、断裂作用等多方面分析了ZJD地区裂缝的成因机理。利用地震资料确立了该区地层层速度与地层压力之间的函数关系。并运用异常孔隙流体压力、地层曲率和相干体等技术对该区裂缝性储层的平面分布规律进行研究，预测了该区主要的裂缝发育区带。