Direct electroless Ni-P deposition on AM50 magnesium alloy from sulfate bath

A bright electroless Ni-P deposition on AM50 magnesium alloy in a sulfate plating bath was proposed by using direct plating process with non-chromate pretreatment. The electroless Ni-P plating on AM50 magnesium alloy has an admirable appearance and good adhesion. The results indicate that the electroless Ni-P deposition with non-chromate pretreatment has better adhesion than that of zinc immersion coating. Anodic polarization curves indicate that the electroless Ni-P deposition obtained from the sulfate bath has similar corrosion-resistance to that obtained from basic nickel carbonate bath. The deposition process generates less pollutant by a non-chromate plating bath and is suitable for the magnesium alloys manufacture because of its low cost. The hardness of the electroless Ni-P plated AM50 is about HV 720.6 and HV 969.7 after heat treatments at 180℃ for 2 h. The wear resistance of Ni-P plated magnesium alloy specimens is about 5 to 9 times as high as that of bare magnesium alloys.     

The influence of NaCl and CO2 on the atmospheric corrosion of magnesium alloy AZ91

The influence of NaCl and CO₂ on the atmospheric corrosion of magnesium alloy AZ91 is studied in the laboratory. Samples were exposed under carefully controlled air and flow conditions; the relative humidity was 95%, the temperature was 22.0°C and the concentration of CO₂ was < 1 ppm or 350 ppm. Different amounts of sodium chloride (0–70 μg/cm²) were added before exposure. The corrosion products were analyzed by gravimetry, ion chromatography, X‐ray diffraction and scanning electron microscopy. Mass gain and metal loss results are reported. The combination of high humidity and NaCl is very corrosive towards AZ91. However, the NaCl‐induced corrosion is inhibited by ambient concentrations of CO₂. Exposure in the absence of CO₂ gives rise to heavy pitting, with brucite, Mg(OH)₂, being the dominant corrosion product. In the presence of CO₂ a layer of hydrated magnesium hydroxy carbonate, Mg₅(CO₃)₄(OH)₂ · 5 H₂O forms. A tentative corrosion mechanism is presented that explains the behavior in the two environments.     

氯氧镁水泥对不饱和树脂的阻燃性能与阻燃机理研究

采用极限氧指数法、热重分析和烟密度测试法研究了氯氧镁水泥在不饱和树脂（UP）中的阻燃作用和阻燃机理。研究表明经偶联剂处理后的氯氧镁水泥对UP具有良好的阻燃抑烟效果，并通过增加UP在高温下的热稳定性和降低热失重速率等机理发挥阻燃作用：氯氧镁水泥含量在40％内对UP的力学性能影响较小，是一种新型的无机添加型阻燃剂。     

共沉淀法制备锰锌软磁铁氧体前躯体共沉过程中钙、镁深度脱除的热力学分析

通过对Fe(Ⅱ)-Mn(Ⅱ)-Zn(Ⅱ)-Ca(Ⅱ)-Mg(Ⅱ)-NH3-NH4HCO3-H2O体系的热力学分析，得到各金属离子浓度与pH的关系，从而确定共沉法制备锰锌软磁铁氧体前躯体共沉过程中钙、镁深度脱除的共沉区域。热力学分析结果表明，溶液中钙、镁的含量随着体系pH的增大而降低，在相同条件下镁的溶解度大于钙的溶解度。为减少进入共沉粉中的钙、镁含量，需要保证在铁、锰、锌共沉完全的基础上降低体系的pH。当溶液中[C]T=0．1mol／L，[N]T=1．0mol／L时，pH控制在6．23～6．50之间可以大大降低进入共沉粉中的钙、镁含量。确定共沉过程钙，镁深度脱除的共沉区域，对于生产高纯锰锌软磁铁氧体前躯体具有重要的指导意义。     

不连续增强镁基复合材料的界面行为

综述了近年来国内外关于Ａｌ２Ｏ３短纤维、ＳｉＣ晶须、ＳｉＣ颗粒、Ｂ４Ｃ颗粒增强镁基复合材料的界面结构及其对复合材料性能影响的研究进展，并对今后的研究提出了一些看法。     

察尔汗盐湖镁资源的开发及展望

察尔汗盐湖不仅具有丰富的镁资源，而且具有开发盐湖的能源，政策优势，由脱水氯化镁可制得多种镁产品。氯化镁脱水技术，氯化镁制金属镁技术是综合开发盐湖水镁资源的关键技术，将纳米技术应用于盐湖镁资源的开发，使镁产品高值化，精细化，将是察尔汗盐湖镁资源的开发方向。     

The distribution of nutrient elements in cell wall and other fractions of the herbage of some grasses and legumes

The distribution of 10 nutrient elements was assessed in three fractions of herbage samples of perennial ryegrass, tall fescue, white clover and lucerne. The cell wall fraction, prepared by mechanical disintegration of undried material, contained the following proportions of the total herbage content of the major elements: N, 2.9–16.4%; P, 3.0–6.9%; S, 3.6–17.2%; Ca, 11.3–51.8%; Mg. 6.4–27.6% and K, 0.1–1.7%. Substantial though more variable proportions of the trace element cations, Fe, Mn, Zn and Cu were also present in the cell wall fraction. The extent to which the elements were soluble in water was assessed by analysis of the water-insoluble fraction prepared from freeze-dried samples of each herbage. The proportions of the total herbage content of the major elements soluble in water were: N, 30–57%; P, 80–92%; S, 35–71%; Ca, 48–69%; Mg. 65–83% and K, 90–96%. With the trace element cations the proportions soluble in water were more variable, though they were generally less than 70% of the total. The extent to which the various elements were soluble in 80% aqueous ethanol was assessed by analysis of the insoluble fraction prepared from freeze-dried materials. With each of the major elements, smaller proportions of the total herbage content were soluble in 80% ethanol than in water, which may reflect in part the lower solubility of proteins and pectin. With the trace element cations, the differences in solubility between 80% ethanol and water were generally small and inconsistent.     

磷酸镁水泥制备试验研究

基于水工建筑物的应急抢险与快速修补加固处理的需要,运用常规的水泥凝结时间、强度等基本性能试验,研究各材料组成对磷酸镁水泥性能的影响,确定磷酸镁水泥配方,并对不同粒径砂土的磷酸镁水泥砂浆水胶比、养护条件、强度等进行了试验研究。结果表明,硼砂是磷酸镁水泥的有效缓凝剂;氧化镁细度对水泥性能有明显影响,氧化镁越细水泥早期强度越高,但细度过细凝结时间将难以满足施工要求;磷酸镁水泥配方为:P/M值1∶3,硼砂掺量10%,氧化镁细度宜为195 m~2/kg左右;磷酸镁水泥砂浆抗压强度与胶水比具有线性相关性,与龄期呈对数关系;水中养护与标准养护相比,抗压强度降低约6%～27%,磷酸盐水泥在长期水下环境中的适用性需论证。研究成果可为水工建筑物的应急抢险与快速修补加固处理提供参考和依据。     

阻燃型氢氧化镁制备及其影响因素探讨

以七水硫酸镁为原料、氨水为沉淀剂、选择适宜的表面活性剂。以样品XRD图中（001）面与（101）面衍射峰的相对强弱为考察指标，通过单因素实验，分别考察了反应温度、恒温反应时间、陈化时间、表面活性剂用量及氨镁摩尔比等因素对氢氧化镁样品XRD图中（001）面与（101）面衍射峰相对强弱的影响。实验结果表明，制备阻燃氩氧化镁较适宜的工艺条件为：反应温度40℃、恒温反应时间40min、陈化时间120min、表面活性剂A体积用量4ml、氨镁摩尔比6：1.