柠条的纤维特性及其双螺杆CMP制浆性能研究

以柠条为原料，分析了其化学组分和纤维形态，并探讨了柠条双螺杆CMP法的制浆工艺以及浆料的纤维形态和成纸的物理性能。研究结果表明：与针、阔叶木相比，柠条原料中纤维素和综纤维素质量分数较低，苯醇抽出物和热水抽出物质量分数较高，柠条纤维长度总体偏短，木质部和皮部的纤维质量平均长度分别为0.621和0.819 mm，还存在部分杂细胞。采用3.5% Na₂SO₃和1.5% NaOH常温预浸12 h、90℃汽蒸1 h后再用双螺杆挤浆机在质量分数35%下进行搓丝，并结合高浓盘磨机磨浆，所得CMP浆得率可达73%。柠条CMP浆基本保持了纤维原有的长度，质量平均长度达0.650 mm，长宽比为32.7，纤维解离较好，但分丝帚化情况不理想，含有部分纤维束和杂细胞。当加拿大游离度为300 mL时，柠条CMP浆成纸的环压强度指数和松厚度较高，分别为8.67（N·m）/g和2.56 cm³/g，抗张指数为19.6（N·m）/g，本色浆白度较高，达50%（ISO）。柠条CMP浆适合配抄瓦楞原纸等包装用纸，漂白后可配抄新闻纸和白板纸。     

Simulation of thermal barrier coating spallation induced by the initiation/growth/coalescence of internal crack and interfacial crack based on a real image model

In the furnace cycle test, the growth of oxide film leads to the propagation and coalescence of multiple cracks near the interface, which should be responsible for the spallation of thermal barrier coatings (TBCs). A TBC model with real interface morphology is created, and the near-interface large pore is retained. The purpose of this work is to clarify the mechanism of TBC spallation caused by successive initiation, propagation, and linkage of cracks near the interface during thermal cycle. The dynamic growth of thermally grown oxide (TGO) is carried out by applying a stress-free strain. The crack nucleation and arbitrary path propagation in YSZ and TGO are simulated by the extended finite element method (XFEM). The debonding along the YSZ/TGO/BC interface is evaluated using a surface-based cohesive behavior. The large-scale pore in YSZ near the interface can initiate a new crack. The ceramic crack can propagate to the YSZ/TGO interface, which will accelerate the interfacial damage and debonding. For the TGO/BC interface, the normal compressive stress and small shear stress at the valley hinder the further crack propagation. The growth of YSZ crack and the formation of through-TGO crack are the main causes of TBC delamination. The accelerated BC oxidation increases the lateral growth strain of TGO, which will promote crack propagation and coalescence. The optimization design proposed in this work can provide another option for developing TBC with high durability.     

The overall crystallization behavior of polyethylene/wax blends as phase change materials for thermal energy storage: A mini review

This review paper deals with the overall crystallization behavior of polyethylene/wax blends as phase change materials (PCMs) for thermal energy storage with the determination of their thermal properties. The addition of molten wax to the polyethylenes decreases the crystallization and melting temperatures of the blends. However, incorporating fillers to the polyethylene/wax blends can either decrease or increase the crystallization and melting temperatures of the composites depending on the filler type. The normalized enthalpy values of linear low-density polyethylene showed no significant change when increasing the wax content. On the contrary, the normalized enthalpy values of the wax in the blends were lesser than that of pure wax and increased with increasing wax content. Since the wax in the blend had a lower crystallinity compared to pure wax, this influences its effectiveness as a PCM for thermal energy storage. The effect of different polyethylenes on the wax morphology gave rise to enhance phase separation when wax was blended to high-density polyethylene as compared to the other polyethylenes. On the contrary, the effect of various waxes on the morphology of polyethylene resulted in different morphologies due to the molecular weight of the wax used and the structure of the polyethylene chain. The addition of fillers to the polyethylene (PE)/wax samples resulted in enhanced phase separation. The overall isothermal crystallization rate and the equilibrium melting temperature of PEs in the PEs/wax blends were depressed by wax addition due to the wax dilution effect.     

基于时空的弱点状运动目标检测技术

如何在复杂背景下持续有效地检测目标位置,一直是研究者们需要面对的主要挑战。本文在研究红外点状移动目标特征的基础上,根据目标无纹理,无形状的特性,提出一种改进的形态学目标增强算法,并利用目标连续时空不变性检测目标。首先,建立多尺度的图像金字塔,在每层上采用改进的形态学算法快速、粗糙定位小目标。然后进一步的根据目标在时空上的位置相关性,提出基于目标运动特征分析的精确检测方法。得到精确稳定的检测结果。最后实验结果表明与经典的形态学检测算法及其他算法相比,该技术能更有效地检测弱小目标,具有更高的鲁棒性。     

Improvement of polyamide/thermoplastic polyurethane blends with polyamide 6-polyurethane copolymer prepared via suspension polymerization as compatibilizer

The polyamide 6-polyurethane copolymer (PA6-b-PU-b-PA6) was synthesized through anionic suspension polymerization and then mixed with polyamide 6/thermoplastic polyurethane (PA6/TPU) and polyamide 6, 6/thermoplastic polyurethane (PA66/TPU) blends using as the compatibilizer. The results show that the PA6-b-PU-b-PA6 copolymers powders several can be obtained through suspension polymerization using dimethicone as disperse medium. The average diameter of PA6-b-PU-b-PA6 copolymer powders decreased with the increasing of PU content. With the addition of PA6-b-PU-b-PA6, the TPU phase dispersed more uniformly in PA6 or PA66 matrix, and the size of TPU dispersed phase decreased obviously. The PA6-b-PU-b-PA6 copolymer with higher PU content shows better compatibilizing effect. Addition of PA6-b-PU-b-PA6 can improve both strength and toughness of the PA/TPU blends. When the amount of PA6-PU25% copolymer was 5 phr, the tensile strength and notched impact strength of PA6/TPU/PA6-PU25% blends increased 29 and 159.4%, respectively, compared to the PA6/TPU blend without compatibilizer.     

Influences of chip serration on micro-topography of machined surface in high-speed cutting

Saw-tooth chip changes from macroscopically continuous ribbon to separated segments with the increase of cutting speed. The aim of this study is to find the correlations between chip morphology and machined surface micro-topography at different chip serration stages encountered in high speed cutting. High strength alloy steel AerMet100 was employed in orthogonal cutting experiments to obtain chips at different serration stages and corresponding machined surfaces. The chips and machined surfaces obtained were then examined with optical microscope (OM), scanning electron microscope (SEM), and white light interferometer (WLI). The result shows that chip serration causes micro-waves on machined surface, which increases machined surface roughness. However, wave amplitudes (surface roughness) at different serration stages are different. The principal factor influencing wave amplitude is the thickness of the sawed segment (tooth) of saw-tooth chip. With cutting parameters in this study, surface roughness contributed by chip serration ranges from 0.39 μm to 1.85 μm. This may bring on serious problems in the case of trying to replace grinding with high-speed cutting in rough machining. Some suggestions have been proposed to control the chip serration-caused surface roughness in high-speed cutting based on the results of the current study.     

Thermo-physical properties of as deposited and aged thermal barrier coatings (TBC) for gas turbines: State-of-the art and advanced TBCs

In the perspective of fuelling the future generations of gas turbines by hydrogen rich syngas, the evaluation of the effect of a higher water vapour content into the flue gases on the TBC used, or potentially usable, is a need. For this purpose YPSZ APS TBC with two different microstructures have been exposed for 500?h at different temperatures in the range 1000?°C–1250?°C either in air and air +20% vol. H₂O. The comparison between the different testing conditions has been performed in terms of sintering kinetics and phase stability, as evaluated by thermal diffusivity measurements and Synchrotron X-Rays diffraction, respectively. Furthermore the characterisation of thermal properties of two innovative TBCs (GZO-YPSZ and YAG) potentially able to withstand the CMAS attack and erosive environments, respectively, has been carried out.No clear evidence of a different behaviour of TBC has been observed, at least in the considered aging time and temperature range.     

A facile pathway to prepare molybdenum boride powder from molybdenum and boron carbide

Molybdenum boride is an ideal hard and wear-resistant material. In this study, a new method is proposed for preparing molybdenum boride, by which Mo first reacts with B₄C to generate the mixture of molybdenum boride and C, and then the product is decarburized by molten Ca to generate CaC₂. Pure molybdenum boride could be obtained after acid leaching to remove the by-product CaC₂. According to the experimental and thermodynamic calculation results, it is concluded that the single-phase MoB could be successfully prepared, while Mo₂B, Mo₂B₅, and MoB₄ could not be synthesized by this method. Moreover, it was found that the particle size of finally prepared MoB is determined by particle size of raw Mo powder. The residual carbon content of the product could be decreased to 0.10 wt% after first reaction at 1673 K for 6 hours and then decarburization reaction at 1673 K for 6 hours.     

基于3D打印技术复制砂浆节理的剪切试验及峰值抗剪强度模型

为进一步研究节理三维形貌特征与节理峰值抗剪强度的关系,首先采用巴西劈裂试验获取了自然劈裂岩石表面,通过三维扫描技术获取了节理面形态的高精度点云,通过逆向建模得到了自然岩石表面的立体模型,结合3D打印技术制作出了与自然岩石表面一致的PLA模具,以3D打印获得的底模通过水泥砂浆浇筑了含有自然结构面形貌的相似节理面试样。PLA模具与复制材料差异较大,复制材料在凝结过程中不易与PLA模具黏结,进而使脱模过程较为方便,不会破坏节理面。同时PLA模具可重复进行相似材料复制工作,具有可重复使用的优点。然后进行了具有5组形貌面的20个水泥砂浆节理面在4种不同法向荷载情况下的结构面剪切试验,得到了结构面剪切位移-荷载曲线。研究了结构面峰值抗剪强度、峰值位移、剪切刚度影响因素。节理经过剪切后形貌面出现不同程度的磨损,其磨损范围与等效高差分布范围基本一致,并且在等效高差为剪断破坏模式且成片的区域磨损较为严重。在新粗糙度指标基础上提出了新的峰值抗剪强度模型,经试验对比显示出新模型的有效性。在新模型基础上提出了一个简化模型。对比发现新模型简化后其计算精度较新模型有所降低但由于所需参数减小计算较为方便,新模型简化结果精度虽然有所下降但是还是比Barton公式精度高。     

葛洲坝水利枢纽泄水建筑物进水口冲磨与修复

葛洲坝水利枢纽工程已运行20余年，近年水下检查中发现泄水建筑物进水口存在不同程度的冲磨，有些已威胁到建筑物安全运行，分析冲磨原因和探讨修复材料和手段是非常重要的，本文就此问题提出一些看法和建议供参考。