爆炸排淤填石法中淤泥的本构模型

以爆炸排淤填石法为背景 ,对不同应变率阶段淤泥的本构模型进行了分析 ,利用ANSYS/LS-DYNA动态有限元分析程序对所选择的模型进行验证和确认。计算和分析结果表明 :在形成爆炸空腔的高应变率阶段 ,淤泥表现为理想不可压缩流体的性质 ;在小药量小抵抗线条件下 ,甚至在淤泥自重作用下的较低应变率变形阶段 ,其黏性效应也可以忽略不计。     

Salt-assisted solution combustion synthesis of NiFe2O4: Effect of salt type

The effects of three types of salt including NaF, KCl, and NaCl on the properties of NiFe₂O₄ nanoparticles using salt-assisted solution combustion synthesis (SSCS) have been investigated. The synthesized powders were evaluated by SEM, TEM, FTIR, XRD, and VSM analysis. Also, the specific surface area (SSA), as well as size distribution and volume of the porosities of NiFe₂O₄ powders were determined by the BET apparatus. The visual observations showed that the intensity and time of combustion synthesis of nanoparticles have been severely influenced by the type of salt. The highest crystallinity was observed in the synthesized powder using NaCl. The SSA has also been correlated completely to the type of salt. The quantities of SSA was achieved about 91.62, 64.88, and 47.22 m²g^-1 for the powders synthesized by KCl, NaCl, and NaF respectively. Although the magnetic hysteresis loops showed the soft ferromagnetic behavior of the NiFe₂O₄ nanoparticles in all conditions, KCl salt could produce the particles with the least coercivity and remanent magnetization. Based on the present study, the salt type is a key parameter in the SSCS process for the preparation of spinel ferrites. Thermodynamic evaluation also showed that the melting point and heat capacity are important parameters for the proper selection of the salt.     

High-surface-area mesoporous silica-yttria-zirconia ceramic materials prepared by coprecipitation method ― the role of silicon

A high surface area is one of desired properties for yttria-zirconia (Y₂O₃–ZrO₂) ceramic materials given their catalytic applications. The objective of this study is to develop high-surface-area Y₂O₃–ZrO₂ materials by silicon (Si) modification and investigate the role of Si. Si-modified yttrium-zirconium hydroxides were prepared via a one-step precipitation process and calcined at 800 or 950 °C to form Si-modified Y₂O₃–ZrO₂ (denoted as SiO₂–Y₂O₃–ZrO₂) materials containing 0-20 wt% Si as SiO₂. These hydroxides or materials were characterized by ²⁹Si NMR, XPS, TG-DSC, XRD, UV Raman, TEM, and N₂ physisorption measurements. Si species uniformly distributed in the hydroxides tended to be enriched on the material surface at high temperatures. These Si species dominated by the silicates blocked the migration of Y and Zr atoms, which resisted the crystallite growth of Y₂O₃–ZrO₂ components and reduced their crystallite size. Therefore, the SiO₂–Y₂O₃–ZrO₂ possessed a surface area of 59-112 m²/g after calcination at 950 °C for 9 h, which was significantly higher than that of the Y₂O₃–ZrO₂ (23 m²/g). This study may stimulate ideas for developing high-surface-area crystalline ceramic materials calcined at high temperatures.     

变形铝合金表面锆基化学转化膜的研究现状

化学转化膜是金属表面主要的处理方法之一，具备良好的附着力和耐蚀性，能为铝合金提供一定的临时防护。传统的六价铬酸盐化学转化膜在日渐严苛的环保压力下已经逐渐淘汰，取而代之的是近几年发展迅猛的三价铬及无铬锆基化学转化膜。铝合金可分为铸造铝合金和变形铝合金，按照所含主要合金元素和热处理状态可分为若干个系列和型号。本文选取几种典型的变形铝合金，综述了不同铝合金微观组织对转化膜成膜过程的影响，化学转化液添加剂、预处理和后处理工艺对转化膜性能的调控及作用机理，以及几种典型商业钝化剂在变形铝合金表面的应用。总结了目前变形铝合金表面锆基化学转化膜仍面临的问题和发展趋势，未来化学转化膜需在满足新型铝合金发展要求的基础上，通过不同有机、无机添加剂以及外场作用对转化膜的成膜均一性、完整性进行调控，以提高转化膜的综合性能。     

喷油方式对斜齿轮齿面温度的影响

为探讨喷油方式对齿面温度的影响，以斜齿轮为研究对象，通过CFD仿真和试验研究不同喷油方式对斜齿轮齿面温度的影响。针对斜齿轮喷油润滑过程的特点，分析其齿面摩擦生热量，简化轮齿喷油润滑计算模型，并基于CFX进行齿面对流换热仿真研究，得到了不同喷油方式下的齿面温度；基于功率开放式斜齿轮试验平台，对不同喷油方式下的齿面温度进行了试验测量，与仿真计算结果进行对比分析。结果表明：在高速重载斜齿轮传动系统中，啮出侧喷油润滑的方式比啮入侧喷油润滑方式的冷却降温效果要好。     

内燃机活塞环表面处理技术

活塞环在内燃机中有着支撑、密闭、储油、导热的作用,内燃机活塞环制备材料应该具备优良的加工性能、耐高温、耐腐蚀、导热性好且具有良好的强韧性,较好的与气缸材料表面的磨合性能。球墨铸铁和专用钢材已经成为制备内燃机活塞环的基础材料,目前国内外采用多种表面处理技术比如:镀铬、氮化、PVD与CVD镀膜、喷钼、喷涂陶瓷层等表面处理工艺进行表面改性,提高内燃机活塞环的使用寿命和使用性能。需要不断研究和开发新的内燃机活塞环的表面处理技术来满足实际生产和应用中内燃机越来越高的要求。     

电压对电刷镀三价铬镀层性能的影响

在45钢表面电刷镀得到三价铬镀层,镀液组成和工艺条件为:Cr2(SO4)36H2O 0.4 mol/L,甲酸铵0.5 mol/L,氨基乙酸0.5 mol/L,H3BO30.6 mol/L,NaH2PO2 H2O 0.3 mol/L,pH=1.5,温度50°C,镀笔移动速率15 cm/s。研究了电压对镀铬层显微结构、表面粗糙度、厚度、显微硬度和耐磨性的影响。随电压增大,镀层厚度增大,显微硬度和耐磨性均先提高后降低。电压为14 V时,镀层的表面平整,粗糙度为2.387μm,显微硬度为602 HV,耐磨性最好。     

脉冲电沉积镍-铜合金

采用脉冲电沉积技术在304不锈钢表面制备Ni-Cu合金镀层,镀液组成和工艺条件为:NiSO4ꞏ6H2O 200g/L,CuSO4ꞏ5H2O 10 g/L,十二烷基硫酸钠0.2 g/L,柠檬酸钠80 g/L,糖精0.2 g/L,pH 4.0,温度25°C,搅拌速率30 r/min,平均电流密度40~120 mA/cm2,脉冲频率0~100 Hz,占空比20%~90%,时间30 min。研究了平均电流密度、脉冲频率和占空比对Ni-Cu合金镀层的元素组成、表面形貌和显微硬度的影响,得到较优的工艺参数为:平均电流密度40 mA/cm2,脉冲频率50 Hz,占空比60%。该条件下所得Ni-Cu合金镀层由质量分数分别为56.53%和43.47%的Ni和Cu组成,呈“菜花”状形貌,结晶细致、均匀,显微硬度为614.4 HV。