Advanced Sn/C composite anodes for lithium ion batteries

Metallic tin was deposited in fine particulate form on the surface of carbonaceous mesophase spherules (CMS) and in the pores of porous carbon by the decomposition and reduction of tin(II) 2-ethylhexanoate at 450 °C. The Sn/C composite powders obtained were used as anode materials for lithium ion cells. Electrochemical cycling tests of coin cells show that the dispersion of tin into the carbonaceous materials enhances the reversible capacity of the electrodes. The capacity retention at the 50th cycle is 91 % for Sn/CMS composite containing 22% tin, against 428 mAh g^–1 at the first cycle. With further increase in tin content, the capacity fade upon cycling is more rapid.     

电导法测定水的全盐量

采用电导法研究了水溶液中盐的浓度与其电导率的关系，根据模拟水样和实际水样在电导率与全盐量的关系上有较好的吻合性，介绍了电导法测定水中全盐量的方法，结果表明在低浓度范围内电导率与盐浓度成线性关系，与传统的重量法相比，具有快速、简便、准确度高的特点。     

超重力反应结晶法纳米碳酸钙浆料及粉料的表面处理

研究了脂肪酸盐A、水溶性铁酸酯偶联剂B（B1)以及铁酸酯偶联剂C对新型超重力反应结晶法所得的纳米CaCO3浆料及粉料的湿法表面处理的配方与工艺，确定了A体系的最佳改性时间为30～40min、改性温度为40～50℃、改性剂用量(质量分数)为3%～5％；B(B1)体系搅拌强度必须很高，改性时间30～40min，改性温度80℃左右，改性剂用量(质量分数)3％～5％；C体系的最佳改性时间为30～40min，改性剂用量(质量分数)为3％～5％。同时，采用红外光谱对改性前后的纳米碳酸钙进行了表征，表明改性刑已连接至CaCO3表面。最后，用分散稳定模型简要分析了改性机理。     

三轴应力下盐岩声发射特征研究（研究生论坛稿件）

利用MTS815 Flex Test GT岩石力学试验系统和PCI–2声发射(AE)三维定位实时监测系统,开展不同围压下盐岩的三轴压缩声发射定位试验,探讨盐岩轴向加载过程中声发射特征的围压效应。研究结果表明：盐岩AE定位点多少与振铃计数率大小、能率高低具有良好的一致性。声发射高计数、高能率、定位点集聚段等随围压增加而滞后。低围压下,盐岩发生剪切破坏,高计数、高能率、AE定位点集聚段主要出现在屈服阶段和峰值应力前阶段;高围压下,盐岩呈塑性大变形特征,高计数、高能率、AE定位点集聚段主要在峰值阶段及峰后阶段出现。围压增加,累计计数和定位点的总量呈减少趋势;最大能率和累计能量随围压增加而减小,5MPa约分别为30MPa的43倍和22倍。     

相转移催化氧化合成苯甲酸

研究了季铵盐CTAB催化高锰酸钾氧化氯化苄合成苯甲酸的反应。考察了CTAB用量、高锰酸钾用量、反应温度、反应时间对反应的影响。结果表明,合成苯甲酸的最优条件为:高锰酸钾与氯化苄的摩尔比为2∶1,CTAB的摩尔分数为氯化苄的8%,反应温度90℃,反应时间为3h,苯甲酸的产率可达89%。     

高分子铁盐絮凝剂制备及其应用研究

研究了以废铁屑和工业硫酸亚铁为原料,在常压和加热条件下,用氯酸钾作为氧化剂制取聚合硫酸铁(PFS)的工艺条件,并在PFS制备的基础上,合成了聚磷硫酸铁(PPFS)和聚氯硫酸铁(PFCS)。将所制备的聚铁用于污水处理实验,结果表明:用该方法制备的聚铁絮凝剂对实际水样具有较好的混凝处理效果,且制备工艺简单、速度快,从根本上消除了用NaNO_2催化氧化法制备聚铁对环境造成的二次污染。     

我国锌盐工业的现状与展望

阐述了我国锌盐工业的发展现状、存在的问题和面临的机遇与挑战,提出了发展锌盐工业的建议。     

Contributions to the Ohmic Drop in the Electrolysis of ZnCl2 in a Molten Chloride Electrolyte

The electrowinning of zinc from zinc chloride with a molten chloride electrolyte was investigated. The electrolysis of zinc chloride shows ohmic limitations. The energy consumption is to a large extent determined by the anodic reaction, the evolution of chlorine. The chlorine gas plume was visualised in a see-through furnace and images were analysed to determine the plume angle. This parameter serves as an input parameter for a model to determine the ohmic contributions of the electrolyte, the plume and a layer of chlorine bubbles sticking to the anode, as well as the plume velocity. The results indicate that the major contribution (60%) to the ohmic drop is due to a stagnant layer of bubbles growing and sticking to the anode, thereby decreasing the effective anode area by coverage. The plume velocity influences coverage characteristics to some extent, which influences the ohmic drop.     

碱金属盐对低氢酯比下苯甲酸甲酯加氢催化剂的修饰

为了考察了Mn与Zn摩尔配比以及不同碱金属盐修饰制得的锰锌复合氧化物催化剂对苯甲酸甲酯气固催化加氢合成苯甲醛反应活性和选择性的影响,在氢酯比为1.5的条件下,进行苯甲酸甲酯催化加氢反应,发现以5%LiCl修饰的活性组分负载量为25%、n(Mn)/n(Zn)为1.14的MnO-ZnO/γ-Al2O3催化剂,在常压、430℃、空时为1.84 h时,苯甲酸甲酯的转化率为97.71%,苯甲醛的选择性为84.80%.     

微波干法制备阳离子淀粉絮凝剂及其应用

以3—氯—2—羟丙基三甲基氯化铵为阳离子醚化剂，天然物质淀粉为原料，微波干法制得季铵型阳离子淀粉絮凝剂。通过正交试验，研究了各种因素对合成的影响，确定了最佳反应条件。结果表明：阳离子醚化剂与淀粉摩尔比0．35、NaOH与阳离子醚化剂摩尔比1．2、微波功率184W、辐射时间5min时，产物相对黏度为3．18，阳离子取代度为0．31。