单根氧化锌纳米带/Au电极体系I-V特性的测量

利用电子束刻蚀和真空蒸镀法，在单要氧化锌纳米带和SiO2/Si片上，制备了金纳米电极，采用四端法对氧化锌带的电流-电压（I-V）特性进行测量。实验发展氧化锌纳米带/金电极组成的体系存在三种完全不同的I-V特性曲线，分别为对应于较淖电阻的非对称阀值型曲线以及电阻较大的整流型和线性对称曲线，我们认为这主要是由于氧化锌纳米带和电极的接触情况不同所造成的。测量表明器件在不同环境下（空气和真空）具有不同的I-V特性，表面在当测量环境由空气变为真空时，前一类的I-V特性变化不大，而后一类由整流型变为线性对称型。     

微桥法镍膜的弹性模量和残余应力测量

利用MEMS技术制作了不同尺寸的镍(Ni)膜微桥结构样品。采用纳米压痕仪XP系统测量了微桥载荷与位移的关系,并结合微桥力学理论模型得到了两种不同尺寸的Ni膜的弹性模量和残余应力。结果表明,两种不同尺寸的Ni膜的弹性模量结果一致,为190 GPa左右,但是残余应力变化较大。与采用纳米压痕仪直接测得的带有硅(Si)基底的Ni膜弹性模量186.8 7.5 GPa相比较,两者符合较好。     

Effect of oxygenation on electrocatalysis of La0.6Ca0.4CoO3−x in bifunctional air electrode

A vacuum-annealed La_0.6Ca_0.4CoO_3−x was consecutively oxygenated in air at temperatures decreasing from 800 to 100 °C, and its electrocatalytic activities for oxygen reduction and evolution were then measured as a function of the oxygenation temperature. The valence of Co cation, changing between +2 and +3, was found susceptible to annealing either in vacuum or air. The catalytic activities initially decrease monotonically as the oxygenation temperature was decreased from 800 to 300 °C, as a result of increasing oxygen content, and then rise abruptly with the oxygen reduction activity reaching a maximum at 200 °C and the oxidation activity at 150 °C. X-ray photoelectron spectroscopy analysis indicated that the enhancements by the low-temperature oxygenation involved increased OH coverage and less charged cations at surface. The results clearly reveal the importance of the post-calcination annealing process for optimizing the performance of La_0.6Ca_0.4CoO_3−x in air electrode applications.     

Effect of Stoichiometry on Properties of Rare-Earth-Based Hydrogen Storage Alloy for Nickel-Metal Hydride Secondary Battery

Effect of stoichiometry on microstructures, electrochemical properties and PCT characteristics of the alloys MI(Ni0.71Co0.15-Al0.06Mn0.08)x (MI=Lanthanum-rich Michmetal, x=4.6~5.2) have been investigated. The lattice constants a, c, and cellvolumes of non-stoichiometric alloys are bigger than those of the stoichiometric alloy. With the increasing stoichiometry x,the value of a decreases, and the value of c and cell volume increases except for those of the stoichiometric alloy; the plateaupressure of PCT curve, discharge capacity and cycling stability all increase. The alloy with x=5.2 shows the highest dischargecapacity and the best cycling stability among the studied alloys.     

Gamma-irradiation-induced Ag/SiO2 composite films and their optical absorption properties

Small Ag particles or clusters dispersed mesoporous SiO₂ composite films were prepared by a new method: First the matrix SiO₂ films were prepared by sol-gel process combined with the dip-coating technique, then they were soaked in AgNO₃ solutions followed by irradiation of γ-ray at room temperature and in ambient pressure. The structures of these films were examined by X-ray diffraction (XRD), high-resolution transmission electron microscope (HRTEM), and optical absorption spectroscopy. It has been shown that the Ag particles grown within the porous SiO₂ films are very small, and they are isolated and dispersed from each other with very narrow size distributions. With increasing the soaking concentration and an additional annealing, an opposite peakshift effect of the surface plasmon resonance (SPR) was observed in the optical absorption measurements.     

掺Er Al2O3光波导薄膜材料的制备及光学特性

介绍了掺ErAl2O3光波导薄膜的四种典型制备方法的研究结果。比较铒的发光环境和发光特性,分析了影响光致发光强度和寿命的条件和因素。不同工艺制得的Er∶Al2O3薄膜,膜内成分、膜的晶相、掺杂浓度等对Er3 的发光特性均有影响。退火对发光特性及材料具有改善作用。     

流量比对等离子体基团分布和薄膜结构的影响

使用光强标定的发射光谱(AOES)测量了CHF3／C6H6混合气体的微波电子回旋共振(ECR)放电等离子体中基团的分布状态。实验发现随着CHF3流量的增加，成膜基团CF、CF2、CH等的相对密度增大，而刻蚀基团F的密度也会增加，从而使得a—C：F薄膜的沉积速率降低。同时红外吸收谱(IR)分析表明，在高CHF3流量下沉积的a—C：F薄膜中含有更高的C—F键成分。可见在a—C：F薄膜的制备中CHF3／(CHF3 C6H6)流量比是重要的控制参量。     

铝薄膜CMP影响因素分析

提出了在碱性抛光液中铝薄膜化学机械抛光的机理模型,对抛光液的pH值、磨料、氧化剂浓度对过程参数的影响做了一些试验分析。试验结果表面粗糙度的铝薄膜所需的最优化CMP过程参数:硅溶胶粒径为15～20nm,pH值为10.8～11.2,氧化剂浓度为2.5%～3%。