添加稀土引致的磷化膜变化与促进机制

用能谱与SEM分析，发现加入稀土硝酸盐(REN)后明显提高了无定形晶体Zn2Fe(PO4)2在磷化膜表面的覆盖率，而使得膜的耐蚀性能提高.此时膜内相关元素含量比例发生了变化：P增大,Zn减小，可见磷对膜耐蚀性的贡献比锌大.讨论认为，稀土硝酸盐是一个有良好载氧能力的催化剂，具有良好的成核促进作用和阴极去极化作用，从而能加速磷化并使膜的耐腐蚀性能提高.      

Study on bioleaching of primary chalcopyrite ore with thermoacidophilic archae

A high temperature-tolerating thermoacidophilic archae （TA） was isolated from water samples collected from a hot sulfur-containing spring in the Yunnan Province, China, and was used in bioleaching experiments of a low-grade chalcopyrite ore. The TA grow at temperatures ranging from 40 to 80℃, with 65℃ being the optimum temperature, and at pH values of l.5 to 4.0, with an optimum pH value of 2.0. The bioleaching experiments of the chalcvpyrite ore were conducted in both laboratory batch bioreactors and leaching columns. The results obtained from the bioreactor experiments showed that the TA bioleaching rate of copper reached 97% for a 12-day leaching period, while the bioleaching rate was 32.43% for thiobacillus ferrooxidans （Tf） leaching for the same leaching time. In the case of column leaching, tests of a two-phase leaching （196 days）, that is, a two-month （56 days） Tf leaching in the first phase, followed by a 140-day TA leaching in the second phase were performed. The average leaching rate of copper achieved for the 140-day TA leaching was 195mg/（L.d）, while for the control experiments, it was as low as 78mg/（L .d） for the Tf leaching, indicating that the TA possesses a more powerful oxidizing ability to the chalcopyrite than Tf Therefore, it is suggested that the two-phase leaching process be applied to .for the heap leaching operations, whereas, the TA can be used in the second phase when the temperature inside the heap has increased, and the primary copper sulfide minerals have already been partially oxidized with Tf beforehand in the first phase.     

34CrNiMo钢齿轮轴开裂原因分析

对34CrNiMo钢齿轮轴的化学成分、金相组织及断口分析表明，其淬火开裂的主要原因是由于锻造温度过高，导致过热缺陷所致。     

几种Ni—Cr—Al基低偏析高温合金的抗氧性能研究

在１０００－１１００℃之间，对三种Ｃｒ，Ａｌ含量及微量元素，Ｓ，Ｚｒ含量不同的Ｎｉ－Ｃｒ－Ａｌ基合金进行了恒温和循环氧化实验。结果表明，高Ｃｒ，低Ａｌ，Ｓ含量，且不含Ｚｒ的合金其氧化膜层主要由连续致密的Ｃｒ２Ｏ３外氧化层和树根状Ａｌ２Ｏ３内氧化层构成，氧化膜的粘附性较好。     

不锈钢表面氧化皮的清除

不锈钢应用很广.但不锈钢并非绝对不锈,当不锈钢经各种加工处理后表面存在未除去的氧化皮或氧化痕迹时,其耐蚀性会大大降低.对于尚需进行下一道工序加工的不锈钢,这些氧化皮还将影响下道工序的质量.因此,有必要将不锈钢表面的氧化皮或氧化痕迹清除干净.本来,使金属表面形成一层氧化膜是防止金属表面进一步腐蚀的措施之一,因为这层氧化膜能对金属起到保护作用.但是,氧化膜保护性的好坏,首先取决于膜的完整性;其次,还受膜的晶体结构、电子结构及力学性能的影响.不完整的氧化膜使金属表面电化学腐蚀加快.氧化膜中新的氧化物的形成,由于体积差异,会在金属表面产生新的应力;氧化物与基体的热膨     

Wear resistance of ceramic coating on AZ91 magnesium alloy by micro-arc oxidation

The ceramic coating formed on AZ91 magnesium alloy by micro-arc oxidation （MAO） was characterized. The results show that the ceramic coating （3.4-23 μm in thickness）on the surface ofAZ91 alloy was attained under different micro-arc oxidation treatment conditions, which consist mainly of MgO, Mg2SiO4 and MgSiO3 phases. Nano-hardness in a cross-sectional specimen was determined by nano-indentation experiment. The MAO coatings exhibit higher hardness than the substrate. Dry sliding wear tests for the MAO coatings and AZ91 alloy were also carded out using an oscillating friction and wear tester in a ball-on-disc contact configuration. The wear resistance of the MAO coatings is improved respectively under different treatment time as a result of different structures of ceramic coatings formed on AZ91 alloy.     

应对跌宕起伏的氧化铝市场

自上世纪八十年代末,世界氧化铝工业快速发展,氧化铝贸易日益活跃。国内氧化铝实现了由价格双轨制向完全市场价格的转变,先后经历了4次价格浪潮,有喜有忧,耐人寻味。我国铝工业在氧化铝市场的跌宕起伏中快速成长,从名不见经传一跃成为世界最大的原铝生产国和氧化铝消费国,氧化铝生产第二大国。国内外氧化铝生产及市场状况1.世界氧化铝的生产及消费现状。2003年世界氧化铝总产量为5922万吨,其中冶金级氧化铝产量为5457万吨,化学品氧化铝产量为465万吨。截至2004年3月,世界氧化铝生产主要集中在29个国家的69个氧化铝厂,总产能6331万吨。其中冶…     

Fe20Cr4.5Al微晶和含Y2O3弥散氧化物微晶涂层的高温氧化性能

采用自行研制的高频电脉冲沉积(HFESD)设备在Fe20Cr4.5Al合金表面分别制备了Fe20Cr4.5Al微晶涂层与Fe20Cr4.5Al-Y2O3弥散氧化物微晶涂层.在1000℃和1100℃静态空气中,对合金基体和施加涂层试样进行了200 h的恒温氧化实验.结果表明在两种实验温度条件下,含有Y2O3弥散氧化物颗粒的微晶涂层,完全消除了Al2O3氧化膜中的凸脊,细化了氧化膜的晶粒,抑制了氧化膜的剥落,大大地提高了氧化膜的致密性和粘附性.单一的微晶涂层则部分抑制了凸脊状氧化膜的形成,氧化膜由脊状氧化物和细晶氧化物混杂组成.涂层对氧化增重的影响则与氧化温度-氧化膜的生长速率有关,在1000℃下,涂层试样的氧化增重均有所降低,其中弥散氧化物微晶涂层试样的氧化增重最低;在1100℃下,施加微晶涂层和弥散氧化物涂层对氧化增重影响很小.微晶和Y2O3弥散氧化物颗粒在提高Al2O3氧化膜保护性方面具有"协同效应".     

海外文献速报

20 0 30 4 0 1　魏瓞彰 ,潘永宁 .球状石墨铸铁之耐氧化性质研究 .铸造工程学刊 ,2 0 0 3 ,2 9(1 ) :1～1 2针对球墨铸铁 ,探讨在不同温度 (673K、873K及 1 0 73K)条件下 ,Si,Cr,Ni,Cu等合金元素、基体组织 (铁素铁、珠光体铁奥氏体铁 )等对于耐氧化性质的影响。由试验结果可知 ,在 673K(40 0℃ )时 ,所有试片的氧化程度均极轻微。在 873K(60 0℃ )时 ,添加 2Si 1 4Ni 6Cu 3Cr的试片其抗氧化性最佳 ,6Si 0 .5Cr试片则次之。但在 1 0 73K(80 0℃ )时 ,则以 6Si 0 .5Cr的试片具有最佳的抗氧化性 ,而 2Si 1 4Ni 6Cu 3Cr试片的抗氧化性…     

抗1200℃高温氧化的镍-铬合金

美国ＲｏｌｌｅｄＡｌｌｏｙｓ公司新近开发成功一种含Ｆｅ 8%、Ａｌ 1 8%的能抗温度高达 12 0 0℃的循环加热氧化的镍 铬合金 ,该合金还具有很高的抗晶粒长大性和蠕变断裂性能。其室温抗拉强度极限为 72 1ＭＰａ ,延伸率38% ,冲击强度为 78～ 84Ｊ。这一合金高的抗氧化性是由