ADSORPTION MECHANISMS OF HS-IONS ON SULPHIDE MINERAL SURFACES RELATED TO Na_2S-INDUCED FLOTATION

The adsorption mechanisms of HS~- ions existing in air-saturated alkaline solutions on sulphide minerals (including pyrite, arsenopyrite, chalcopyrite and galena) were investigated. The measurement of adsorption density, solvent extraction-chemical analysis of neutral sulphur at the surfaces, measurements of pulp potential and voltammogram, and flotation tests were done. Both the electrochemical and non-electrochemi cal adsorption models of HS~- ions were established. The former was observed and resulted in the formation of neutral sulphur (S°)when the pyrite and arsenopyrite were chosen, and hence renders the surfaces hy drophobic and induced the two minerals flotation. It is called Na_2S-induced flotation. On the other hand, the latter took place and did not produce S° when the chalcopyrite and galena were selected, and hence de presses the collectorless flotation of the two minerals. The adsorptions of HS~- ions were mainly influenced by potentials, pH and the electron structures of the mineral surfaces.     

TiO_2直接电解还原过程的研究

采用SEM、EDS、XRD等方法对TiO2直接电化学还原产物进行分析,指出TiO2电极的还原是从外向内由高价到低价再到金属逐步进行的。对还原过程中电流、还原气相产物的分析结果表明:还原过程电流效率低,并且电流效率随电解时间延续而降低,阳极产物CO、CO2与阴极中间产物Ca发生副反应以及副反应产物炭黑造成电流短路是电流效率低的主要原因。提高电流效率的途径有两条:一是增大阴、阳极间距,减小副反应的发生;二是使电解池表面熔盐不断导出,或采取某一隔离措施,使副反应产生的炭黑在阴、阳极之间不造成电流短路。     

Fe-Ti-B激光熔敷层中TiB2晶须的原位合成

为了降低激光熔敷Fe-B涂层的高度脆性，使用不同成分的B4C和Fe-Ti合金混合粉末在奥氏体不锈钢基体上进行了激光熔敷，得到了具有TiB2晶须强化的复合Fe-Ti-B涂层。该涂层在保持原来Fe-B涂层的高硬度的同时，其抗裂性能亦得到了改善。     

00Cr17Ni14Mo2不锈钢的性能及应用研究

研究了00Crl7Nil4M02不锈钢材料的机械性能、焊接性能和耐腐蚀性能，从用户和研究开发的角度探讨了其在压力容器、化工装置、化肥装置、海洋装置和建筑业等领域的应用。     

Phase transition of lithiated-spinel Li2Mn2O4 at high temperature

1 Introduction Lithium manganese oxides are the most attractive cathode materials for rechargeable lithium-ion batteries because of their low-cost and less toxicity when compared with either cobaltates or nickelates[1?3]. Among these oxides, the spinel-fr…     

ZG3Cr18Ni25Si2耐热钢熔炼工艺的改进

介绍了改进后的ZG3Cr18Ni25Si2耐热钢熔炼工艺及特点，它具有较高的合金元素收得率，铸件的使用寿命比改进前延长了35％－45％。     

Cr3Si／Crl3Ni5Si2金属间化合物合金组织与高温滑动磨损性能的研究

利用水冷铜模激光熔炼炉制得了由初生枝晶Cr3Si和枝晶间Cr3Si／Crl3Ni5Si2共晶组成的金属间化合物合金。利用OM，SEM，TEM，EDS和XRD分析了该金属间化合物的显微组织，在400℃，500℃和600℃条件下测试了其耐磨性能。结果表明，由于Cr3Si和Crl3NisSi2硬度高、原子键合力强、组织细小、均匀，在高温滑动磨损条件下具有优良的耐磨性能。     

用相变方法制取高纯度超细钽粉的研究

报导了通过相变热处理使Ｋ２ＴａＦ７晶体参数发生变化，以利于制取高纯度超细钽粉的实验依据和结果。结果表明，Ｋ２ＴａＦ７在２００～２５０℃发生可逆相变；相变后Ｋ２ＴａＦ７晶体的粒径可由原来的１３５１．８μｍ减小至７０．８μｍ，极大地提高了比表面积；相变后，杂质极大挥发，提高了Ｋ２ＴａＦ７的纯度。     

Gd2O2S：Ti的长余辉性能研究及机理探讨

利用高温固相法合成了一种长余辉发光材料Gd2O2S：Ti，利用XRD测试了其结构并测试了其在紫外光激发下的发光特性；停止照射，有橙色的余辉，时间接近2h。分析该磷光体的发光和余辉产生细节，认为空穴和电子的复合导致Ti^3＋的^2E→^2T2的跃迁是产生发光和余辉的原因；并根据缺陷和空位对Gd2O2S：Ti的余辉机理进行探讨，提出了余辉机理模型。     

压痕法测定热压MoSi2基复合材料K1C值的研究

用不同的压痕方程计算了纳米ＺｒＯ２粒子韧化ＭｏＳｉ２基复合材料的室温断裂韧性Ｋ１ｃ值，同时研究了压痕载荷对Ｋ１ｃ值的影响。结果表明，试验材料在试验条件下的断裂韧性不遵从半月状裂纹系统方程，而遵从巴氏裂纹系统方程，其室温压痕断裂韧性保持与压痕载荷的独立性。