罩式退火温度对高强IF钢组织及性能的影响

为研究不同退火温度下高强IF钢的组织性能及织构的变化规律,采用温箱式电阻炉加热模拟罩式退火工艺,研究了不同退火温度下高强IF钢210P1冷轧板力学性能;对不同退火温度钢板的r90进行了统计并对其进行显微组织观察;采用X射线衍射仪及热场发射扫描电镜对不同退火温度的罩式退火成品板进行了织构分析。结果表明,在高强IF钢210P1冷轧板的罩式退火过程中,提高退火温度将使晶粒明显长大。随着退火温度的升高,屈服强度及抗拉强度下降,伸长率升高,n值略有上升,板材横向r值增加较明显,有利织构{111}取向密度增加,不利织构{100}取向密度降低。     

30Cr13不锈钢冶炼过程夹杂物控制技术

  针对30Cr13生产过程中存在的轧材非金属夹杂物合格率偏低仅85%左右的问题，通过对30Cr13不锈钢精炼过程钢中非金属夹杂物存在形态进行分析，并结合现有精炼工艺制度，在实验室研究的基础上制定了不锈钢精炼过程非金属夹杂物控制方案。工业应用后，精炼结束钢中大于5 μm的非金属夹杂物总数、形状以及尺寸等参数均得到了有效改善，钢水洁净度大大提高。     

风机主轴锻件锻后热处理工艺优化

通过对42CrMo4风机主轴结构尺寸、性能要求、材质特点等方面进行分析,对原有锻后热处理工艺进行优化,制定出既能达到锻后热处理效果又经济节能的工艺参数。     

Toughness enhancement and equivalent initial fracture toughness of cementitious composite reinforced with aligned steel fibres

Based on theoretical analysis and numerical simulation, the impact of steel fibres on the stress intensity factor (SIF) at the crack tip for cementitious composite was studied. The enhanced toughness of steel fibre reinforced cementitious composite (SFRC) in resisting cracks was explained by the decrement of SIF caused by steel fibre inclusions at the crack tip of the composite. The equivalent initial fracture toughness was used to characterize the crack initiation of SFRC. A simplified method for determining the of SFRC was proposed based on a linear regression method. Fracture tests were conducted on three‐point bending notched beams with different steel fibre volume fractions and specimen sizes to study the crack initiation behaviour of aligned steel fibre reinforced cementitious composite (ASFRC). of ASFRC was calculated, and the size effect of was analysed. The results showed that slightly increased with the steel fibre volume fraction and gradually became stable. For the tested specimens, whose heights varied between 40 and 100 mm, the specimen size had little impact on the .     

Damage mechanism at different transpassive potentials of solution-annealed 316 and 316l stainless steels

Electrochemical impedance spectroscopy (EIS), anodic polarization and scanning electron microscopy techniques were used to investigate the damage mechanism in the transpassive potential region of AISI ...