TC11钛合金应变率相关的拉伸行为

为了获取TC11钛合金拉伸性能随应变率的变化规律,对该材料开展了宽应变率范围下的单轴拉伸试验。结果表明,随着应变率从准静态增加到动态,TC11钛合金的屈服强度略有上升,而应变硬化模量下降。此外,在准静态和动态拉伸下,TC11钛合金均发生了剪切断裂,但动态断裂面上韧窝尺寸小于准静态断面上韧窝尺寸。进一步对材料在变形过程中的温升进行了分析,结果发现,高应变率下材料断裂面上更小尺寸的韧窝和材料更容易发生应变软化归因于动态加载情况下材料中产生了更高的温升。     

Thermal and mechanical properties of polyamide 11 based composites reinforced with surface modified titanate nanotubes

The preparation of polyamide 11 (PA11) based composites reinforced with pristine and surface-modified titanate nanotubes (TTNT) is reported. Twin-screw melt compounding was used to produce composites with up to 2 wt% of TTNT. To enhance dispersion and TTNT compatibility with the thermoplastic, these were modified with cetyltrimethylammonium bromide (CTAB) and sodium dodecyl sulphate (SDS). Fourier transform infrared spectroscopy and thermogravimetry were used to demonstrate that surface modification prior to composite processing was successful, while scanning transmission electron microscopy combined with energy-dispersive X-ray analysis confirmed the retention of surfactants on TTNT in composites. Nevertheless, scanning and transmission electron microscopy revealed incomplete dispersion of TTNT inside polyamide. The improved wettability on the TTNT–PA11 interface was observed for composites comprising surface-modified TTNT. Consequently, these composites exhibited better thermal and mechanical properties than those containing pristine TTNT. A significant rise of the decomposition temperature was detected in composites containing TTNT modified with CTAB, while the uppermost increment of the storage and Young’s modulus (of about 35% and 26%, respectively) was achieved in the composite comprising 0.5 wt% of TTNT modified with SDS. The increase of the nanofiller content improved the yield strength and led to the drop in the strain at break.     

模拟乘法器MC1496的应用研究

模拟乘法器是一种完成两个模拟信号相乘的电子器件。本文基于电路设计与仿真软件Multisim进行模拟乘法器MC1496的应用研究,具体实现普通调幅（AM）、双边带调幅（DSB）、同步检波器、混频器的电路设计与仿真。     

EAST 装置电子回旋共振加热系统波纹圆波导研究*

在EAST装置上正在建设140GHz/4MW/1000s电子回旋共振加热(ECRH)系统,单个回旋管输出的1MW功率通过波纹圆波导传输到天线聚焦镜上,然后经天线反射镜进入等离子体。运用表面阻抗法对波纹圆波导进行了理论分析,针对EAST装置ECRH系统需求的140GHz波纹圆波导进行了设计研究,所设计的波导传输模式为HE11模,具备1MW连续波运行能力且欧姆损耗低于0.02d B/100m,同时分析了HE11模在波导口外辐射模式及其与TEM00模耦合特性。     

Entrepreneurial quality and regional development: Characterizing SME sectors in low income areas*

This paper analyses the characteristics of SMEs in less‐developed areas in comparison with more advanced economies. The conceptual framework includes different factors making up the so‐called ‘entrepreneurial quality’ of the SME sector: the personal characteristics of the entrepreneurs (motivations and previous experience), different dimensions of the SMEs’ entrepreneurial orientation, and the patterns of the SMEs’ insertion in national and global value chains. The empirical analysis uses data of SMEs in four different Spanish provinces representing examples of low income economies and comparatively high income ones, respectively. Results show the SMEs in the low income economies to be characterized by a lower entrepreneurial quality.     

发动机压气机转子叶片裂纹分析

对发动机压气机转子叶片试验件裂纹进行失效分析。通过对故障叶片进行外观检查、断口分析、表面形貌检查、截面金相检查、材质分析及断口区域成分分析,并对叶片振动应力分布进行计算,确定叶片裂纹性质和产生原因。结果表明:故障压气机转子叶片裂纹为高周疲劳性质,导致叶片过早出现疲劳裂纹的主要原因是叶身表面振动应力最大区域抛光、喷丸效果差,存在原始机械加工痕迹;最后提出避免叶身表面残留原始机械加工痕迹的改进建议。     

伊利石合成磷酸硅铝分子筛及其表征

采用碱熔活化方法对伊利石进行活化,系统地考察了煅烧温度、煅烧时间、矿物粒度、矿碱质量比等条件对伊利石活化的影响;以活化伊利石为主要硅、铝源,采用水热法合成磷酸硅铝分子筛（SAPO-11）,系统地考察模板剂种类、模板剂用量、投料硅铝物质的量比、晶化温度等合成条件对产物结构和性质的影响。利用X射线衍射（XRD）、N₂吸附-脱附、扫描电镜（SEM）和透射电镜（TEM）等分析手段对活化产物和合成的分子筛进行了分析表征,结果表明,伊利石的最佳碱熔活化条件为煅烧温度为800 ℃、煅烧时间为90 min、伊利石矿粒径为75 μm、矿碱质量比为1∶0.8,经活化后伊利石的晶型结构基本完全被破坏,活化产物主要是高活性的低聚合态硅铝酸盐,化学反应活性较高;在原料配比为n（三氧化二铝）∶n（五氧化二磷）∶n（模板剂）∶n（二氧化硅）∶n（水）=1∶1∶1∶0.5∶50、水热晶化温度为190 ℃、晶化时间为24 h时成功合成结晶度较高的纯相SAPO-11分子筛,合成的SAPO-11分子筛具有较大的比表面积,样品主要由粒径为1~3 μm的椭球状颗粒组成,该合成方法丰富了磷酸硅铝（SAPO）分子筛的原料来源,拓展了中国伊利石的高附加值利用途径。     

烃类异构化小粒径、多级孔SAPO-11分子筛催化剂研究进展

由于小粒径、多级孔或兼具小粒径与多级孔结构的SAPO-11分子筛能够显著提高SAPO-11分子筛催化剂在烃类加氢异构化中的活性和选择性,近年来已成为烃类异构化催化剂研究的热点。本文按照SAPO-11分子筛的制备方法进行分类,系统介绍了小粒径、多级孔和兼具小粒径与多级孔结构的SAPO-11分子筛的制备及其临氢异构化性能,指出在今后的研究中,研究开发新的绿色高效合成方法,降低合成成本和减少环境污染是小粒径或（和）多级孔SAPO-11分子筛催化剂实现工业化应用亟待解决的突出问题和研究方向。     

Synthesis and luminescence properties of nitrided lanthanum magnesium hexaluminate LaMgAl11O19 phosphors

Nitrided LaMgAl₁₁O₁₉ phosphors were prepared by a two-step method involving synthesis at 1550 °C for 4 h, trituration, and firing at 1650 °C for 5 h under a nitrogen atmosphere. Nitrogen was doped into LaMgAl₁₁O₁₉ and bonded with aluminium atoms. The nitrided LaMgAl₁₁O₁₉ phosphors showed plate-like morphology with a rough surface and exhibited strong blue emission at 442 nm and 450 nm, which may be attributed to the energy transition between defect levels. A weak emission band at 590 nm was ascribed to the transition between the V_Al acceptor and the valence band, which was excited at 254 nm.