铸态及快淬态La_2Mg(Ni_(0.85)Co_(0.15))_9B_x(x=0~0.2)贮氢合金的微观结构与电化学容量(英文)

用铸造及快淬工艺制备了La-Mg-Ni系(PuNi3型)贮氢合金La2Mg(Ni0.85Co0.15)9Bx(x=0,0.05,0.1,0.15,0.2),分析测试了铸态及快淬态合金的微观结构与电化学容量,研究了硼及快淬工艺对合金微观结构及电化学容量的影响。结果表明,铸态合金具有多相结构,包括(La,Mg)Ni3相(PuNi3型)、LaNi5相,一定量的LaNi2相和微量的Ni2B相,经快淬处理后Ni2B相消失。硼的加入对铸态及快淬态合金的容量产生不同的影响,铸态合金的容量随硼含量的增加而单调下降,而快淬态合金的容量随硼含量的增加有一极大值。快淬处理对含硼及不含硼合金的容量也有不同的影响,随淬速的增加,不含硼合金的容量单调下降,而含硼合金的容量可以获得一个极大值。     

Microstructures and Electrochemical Properties of Cobalt-Free LaNi_(4.0)Al_(0.2)Fe_(0.4)Cu_(0.4-x)Sn_x (x=0～0.4) Electrode Alloys Prepared by Casting

To decrease the cost of nickel-metal hydride (Ni/MH) batteries ,the replacement of Co in LaNi5-basedmetal hydride electrodes by other alloying elements hasbeen of great interest to many researchers[1 ~5]. Al-though researchers have considerably investigated thepreparation of low-Co ,Co-free hydrogenstorage alloy ,the results are still unsatisfactory[1 ,2].The main prob-lemis that the cycle stabilities of low-Co and Co-freeAB5-type electrode alloys are very poor ;therefore ,therole played b…     

铸态及快淬态La2Mg(Ni0.85Co0.15)9Crx(x=0～0.4)贮氢合金的电化学性能

为了提高La-Mg-Ni系(PuNi3型)贮氢合金的电化学循环稳定性,在La2Mg(Ni0.85Co0.15)9合金中加入微量Cr,用铸造及快淬工艺制备了La2Mg(Ni0.85Co0.15)9Crx(x=0,0.1,0.2,0.3,0.4)贮氢合金.研究了Cr含量对铸态及快淬态合金微观结构及电化学性能的影响.XRD,SEM及TEM的分析结果表明,铸态及快淬态合金具有多相结构,包括(La,Mg)Ni3相(PuNi3型结构)、LaNi5相和一定量的LaNi2相.随Cr含量的增加,铸态合金中LaNi2相的量增加.电化学测试结果表明,Cr的加入提高了铸态及快淬态合金的循环稳定性,但使合金的容量下降.当Cr添加量从0增加到0.4时,铸态合金的容量从396.3 mAh/g下降到355.6 mAh/g,循环寿命从72次增加到97次;快淬态(30 m/s)合金的容量从364.2 mAh/g下降到334.2 mAh/g,循环寿命从100次增加到131次.Cr添加使铸态合金的放电电压特性和活化性能得到改善.