Reaction behavior and mechanism of anatase in digestion process of diasporic bauxite

Based on the study of influence of temperature, digestion time, amount of CaO added and composition of aluminate solution on reaction behavior of pure anatase in high-pressure digestion process of bauxite, reaction mechanism of anatase was preliminarily determined. Anatase first reacts with caustic soda to produce Na2TiO3, then the resultant Na2TiO3 reacts with 3CaO·Al2O3·6H2O resulting from the reaction of CaO with sodium aluminate solution to produce CaO·2TiO2·H2O which eventually converts into CaTiO3. Higher temperature, concentration of free Na2Ok (the caustic soda uncombined with aluminate anions in the form of Na2O) and molar ratio of CaO to TiO2 are favorable to the conversion of CaO·2TiO2·H2O to CaTiO3. And Al(OH)4- shows the function of a catalyzer in the reaction of anatase with caustic soda with or without CaO added during the digestion process of diasporic bauxite.     

烧结法高浓度铝酸钠溶液中硅酸二钙的絮凝机理

通过测定硅酸二钙与高浓度铝酸钠溶液(ρ(Al2O3)≥180g/L)反应后浆液的絮凝沉降性能,结合红外光谱、Zeta电位和接触角的测定结果,探讨絮凝剂与硅酸二钙的絮凝机理。沉降实验结果表明:添加含酰胺基、羧基的絮凝剂A和B时,浆液不絮凝沉降;而含酰胺基、羧基和羟肟酸的絮凝剂C的沉降效果好,沉降初始5min的平均速度达到19.0mm/min。红外光谱分析结果表明:添加絮凝剂A、B和C后,絮凝剂中的R—COO-基团均可与硅酸二钙中的Ca2+形成配位键。沉降后固相的有机碳含量分析结果表明:硅酸二钙可吸附约40%的絮凝剂A和B,或吸附91.04%的絮凝剂C,这直接导致吸附絮凝剂C的硅酸二钙的Zeta电位、接触角和固体表面能变化较絮凝剂A、B的大;在烧结法高浓度体系中,电中和脱稳不是主要原因,絮凝剂在颗粒表面的大量被吸附并通过疏水力增强或架桥作用的形成是改善浆液絮凝沉降的关键。     

焦绿石型氧化钨的研究现状和应用前景

综述了焦绿石型氧化钨的结构特点、制备方法及应用前景,重点介绍了水热合成法的研究进展及其反应机理,提出了该领域中的几个重要问题,并展望了未来的发展趋势。     

磷酸钠对铝酸钠溶液晶种分解的影响

研究了磷酸盐杂质对铝酸钠溶液晶种分解的影响,并探讨了其影响机理.结果表明,在浓度小于5g/L时,磷酸盐能提高铝酸钠溶液的分解率,使晶种分解产品的粒度增大.磷酸盐杂质的存在不会显著影响铝酸钠溶液中氢氧化铝颗粒表面的Zeta电位值,但是会使铝酸钠溶液表面张力增大.     

Recovery of alumina and ferric oxide from Bayer red mud rich in iron by reduction sintering

A great amount of red mud generated from alumina production by Bayer process not only threatens the environment but also causes waste of secondary resources. High-iron-content red mud from Bayer process was employed to recover alumina and ferric oxide by the process of reduction-sintering, leaching and then magnetic beneficiation. Results of thermodynamic analyses show that ferric oxide should be reduced to Fe if reduction of ferric oxide and formation of sodium aluminate and calcium silicate happen simultaneously. Experimental results indicate that alumina recovery of Bayer red mud can reach 89.71%, and Fe recovery rate and the grade of magnetite concentrate are 60.67% and 61.78%, respectively, under the optimized sintering conditions.     

高铁一水硬铝石型铝土矿的低钙比烧结

研究烧结法处理我国高铁中等品位矿石的工艺条件,确定钙比为1.5时熟料中存在3CaO·2SiO2和2CaO·2Si02.结果表日月,增大钙比使熟料A1203溶出率、Si02溶出率均有所降低;延长烧成时间,提高烧成温度有利于A1203溶出率的增加和Si02溶出率的降低;提高铁铝比,熟料最佳烧成温度降低,烧成温度范围变窄;提出的A1203有效溶出率概念表明,钙比为1.5时,熟料烧成效果最好;确定高铁铝土矿适宜的烧成制度为:烧成温度1250～1300℃,烧成时间20-40rain,钙比1.5.     

添加剂对一水硬铝石型铝土矿焙烧强化溶出的影响

研究了在一水硬铝石型铝土矿焙烧过程中添加剂对焙烧矿溶出性能的影响。实验结果表明, 在一水硬铝石型铝土矿焙烧过程中添加氟化铝, 对焙烧矿的溶出性能有明显的改善作用。在铝土矿中添加1%的氟化铝焙烧, 经185 ℃溶出1 h 后, 焙烧矿氧化铝的溶出率达52%, 比未添加时提高15%左右;且随着氟化铝添加量的增加, 氧化铝的溶出率随之升高, 当添加量为5%时, 在同样溶出条件下氧化铝溶出率可达71%;而铝土矿添加3%氟化铝焙烧, 在200 ℃溶出1 h, 氧化铝溶出率即可达到88%。     

粉煤灰中铝硅高效分离的动态扩大试验

为缓解我国氧化铝工业存在的铝土矿需求量大与国内铝土矿供应严重不足间的矛盾和粉煤灰大量堆积造成的环境问题,基于粉煤灰还原?氧化焙烧?碱浸实现铝硅分离的全新工艺路线,在已有静态小实验基础上,开展了实验室回转窑动态扩大试验研究.结果表明:在1100℃、配料比n(Fe):n(Al):n(C)=1.2:2:1.2、进料量75 g...     

铝酸钠溶液中硫和铁组元间的相互作用（英文）

对铝酸钠溶液中铁化合物与含硫组元间的反应行为进行研究。结果表明:铝酸钠溶液中铁化合物能显著脱除溶液中的S2-,对S2O32-、SO32-和SO42-等硫化合物则没有脱除效果。当Fe(Ⅲ)和Fe(Ⅱ)化合物加入量达到铁硫摩尔比为2:1时,100°C下S2-的脱除率分别达到86.10%和92.70%。在Fe(Ⅲ)和Fe(Ⅱ)化合物的除硫过程中,均有水合硫代铁酸钠、赤铁矿、无定型硫化亚铁、聚合硫铁化合物和硫酸铁等物质生成,主要区别在于Fe(Ⅱ)化合物反应初期生成的水合硫代铁酸钠会继续转化为不含钠的二硫化亚铁。     

钠硅渣在氧化铝熟料烧结过程中的物相变化

结合相关热力学计算结果,推测钠硅渣在氧化铝熟料烧结法处理过程中存在的多级反应及其产物组成,并通过研究钠硅渣在不同条件下的反应行为,验证中间相Na2-xAl2-xSix O4的存在及其溶出性能的差异。结果表明:在烧结过程中,硅系数x为0、0.05、0.25、0.35、0.45、0.55、0.85的Na_(2-x)Al_(2-x)Si_xO_4均可以生成;烧结产物组成形态受反应温度和生料配比影响;当配钙比为2、烧结温度由750℃升高至1200℃时,或当配钙比由1.0升高至2.5、温度为900℃时,反应产物的硅系数x均可由0.85逐渐下降至0;硅系数决定反应产物的溶出性能,当x≤0.25时,Na_(2-x)Al_(2-x)Si_xO_4中间相可以溶解于铝酸钠溶液。