Microstructural evolution and densification behavior of porous kaolin-based mullite ceramic added with MoO3

Microstructural evolution and densification behavior of porous kaolin-based mullite ceramic added with MoO₃ were investigated. The results indicated that MoO₃ addition not only lowered the secondary mullitization temperature to below 950?°C, but also facilitated effectively the anisotropic growth of mullite grains. Fine mullite whiskers grew and interlocked with one another in the pre-existing pore regions, in-situ forming a stiff 3D skeleton structure of mullite whiskers, which arrested further densification of the sample. On the other hand, due to the great capillary attraction of small pores, the liquid phase tended to spread over small grains, which favored the growth from small mullite grains into whiskers at the expense of the liquid phase. Consequently, competitive mechanisms of sintering and crystal growth of mullite functioned, which further limited the sample densification. As a result, the total linear shrinkage of the sample added with MoO₃ after firing at 1400?°C was only ??2.75%, and its porosity was retained at as high as 67%.     

Synthesis and properties of (Hf1-xTax)C solid solution carbides

Thermodynamically stable (Hf_1–xTa_x)C (x?=?0.1–0.3) compositions were selected by First Principle Calculation and synthesized in nanopowders via high-energy ball milling and carbothermal reduction of commercial oxides at 1450?°C. The formation of a solid solution during powder synthesis was investigated. The solid solution carbide powders were sintered at 1900?°C by spark plasma sintering without a sintering aid. As a result, the (Hf_1–xTa_x)C solid solution carbides exhibited high densities, excellent hardness and fracture toughness (ρ: 98.7–100.0%, HVN: 19.69–19.98?GPa, K_IC: 5.09–5.15?MPa?m^1/2) compared with previously reported HfC and HfC–TaC solid solution carbides.     

Hydrogen production through dry reforming of biogas using a porous electrochemical cell: Effects of a cobalt catalyst in the electrode and mixing of air with biogas

This paper reports the performance of porous Gd-doped ceria (GDC) electrochemical cells with Co metal in both electrodes (cell No. 1) and with Ni metal in the cathode and Co metal in the anode (cell No. 2) for CO₂ decomposition, CH₄ decomposition, and the dry reforming reaction of a biogas with CO₂ gas (CH₄ + CO₂ → 2H₂ + 2CO) or with O₂ gas in air (3CH₄ +?1.875CO₂ +?1.314O₂ → 6H₂ +?4.875CO +?0.7515O₂). GDC cell No. 1 produced H₂ gas at formation rates of 0.055 and 0.33?mL-H₂/(min?m²-electrode) per 1?mL-supplied gas/(min?m²-electrode) at 600?°C and 800?°C, respectively, by the reforming of the biogas with CO₂ gas. Similarly, cell No. 2 produced H₂ gas at formation rates of 0.40?mL-H₂/(min?m²) per 1?mL-supplied gas/(min?m²) at 800?°C from a mixture of biogas and CO₂ gas. The dry reforming of a real biogas with CO₂ or O₂ gas at 800?°C proceeded thermodynamically over the Co or Ni metal catalyst in the cathode of the porous GDC cell. Faraday's law controlled the dry reforming rate of the biogas at 600?°C in cell No. 2. This paper also clarifies the influence of carbon deposition, which originates from CH₄ pyrolysis (CH₄ → C + 2H₂) and disproportionation of CO gas (2CO → C + CO₂), on the cell performance during dry reforming. The dry reforming of a biogas with O₂ molecules from air exhibits high durability because of the oxidation of the deposited carbon by supplied air.     

In-situ formation of Al2O3/Al core-shell from waste material: Production of porous composite improved by graphene

Aluminum dross produced from aluminum industry was used to fabricate Al₂O₃/Al porous composites. The dross was milled for 20?h to obtain nano powder. The milled material was examined by TEM and XRD. Graphene (up to 4?wt%) was mixed with the dross and utilized to reinforce sintered composites. The milled powders were compacted then fired at various temperatures up to 700?°C. Physical properties in terms of bulk density and apparent porosity for sintered composites were tested using Archimedes method. SEM attached by energy dispersive spectrometer (EDS) was used to inspect microstructure and elemental analysis of sintered composites. Microhardness and compressive strength were also measured. Ultrasonic nondestructive technique was utilized to examine the elastic moduli. Electrical conductivity of sintered composite was also studied. During milling up to 20?h, Al₂O₃/Al core-shell was in-situ formed with size of 65.9 and 23.8?nm, respectively. The apparent porosity of sintered composites was improved with rising graphene percent while it decreased with increasing sintering temperature. Increasing of graphene mass percent and firing temperature led to remarkable increase in all mechanical properties and electrical conductivity. The maximum compressive strength, hardness, elastic modulus and electrical conductivity were 200?MPa, 1200?MPa, 215?GPa and 1.42?×?10^?5 S/m, respectively, obtained for composite sintered at 700?°C having 4?wt% graphene.     

Structure and electrical properties of Ca2+-doped (Na0.47Bi0.47Ba0.06)TiO3 lead-free piezoelectric ceramics

The lead-free piezoelectric ceramics (Na_.47Bi_.47Ba_.06)_1-xCa_xTiO₃ (x?=?0, 0.01, 0.02, 0.03, 0.05, and 0.08, abbreviated as BNBTC/0, BNBTC/1, BNBTC/2, BNBTC/3, BNBTC/5, and BNBTC/8, respectively) were obtained using the solid-state reaction method. The structure, electric conductivity, and dielectric, ferroelectric, and piezoelectric properties of the Ca²⁺-doped (Na_.47Bi_.47Ba_.06)TiO₃ ceramics were thoroughly investigated. The ceramics sintered at 1200?°C exhibit dense microstructures, having relative densities higher than 96%. The X-ray diffraction results demonstrate that all ceramics have a pure perovskite structure. The mean grain sizes of the ceramics are related to the Ca²⁺ quantity. A small quantity of Ca²⁺ ions (x?≤?0.03) improves the piezoelectric and ferroelectric properties of the samples. The dielectric behavior of the samples is sensitive to the Ca²⁺ content and electric poling. The results demonstrate that the electrical properties of the (Na_.47Bi_.47Ba_.06)TiO₃ lead-free ceramics can be well tuned by varying the Ca²⁺ quantity.     

Effects of structural characteristics on microwave dielectric properties of low-loss (Zn1-xNix)ZrNbTaO8 ceramics

Low-loss (Zn_1-xNi_x)ZrNbTaO₈ (0.02?≤?x?≤?0.10) ceramics possessing single wolframite structure are initiatively synthesized by solid-state route. Based on the results of Rietveld refinement, complex chemical bond theory is used to establish the correlation between structural characteristics and microwave performance in this ceramic system. A small amount of Ni²⁺ (x?=?0.06) in A-site with the fixed substitution of Ta⁵⁺ in B-site can effectually raise the Q?×?f value of ZnZrNb₂O₈ ceramic, embodying a dense microstructure and high lattice energy. The dielectric constant and τ_f are mainly affected by bond ionicity and the average octahedral distortion. The (Zn_0.94Ni_0.06)ZrNbTaO₈ ceramic sample sintered at 1150?°C for 3?h exhibits an outstanding combination of microwave dielectric properties: ε_r =?27.88, Q?×?f?=?128,951?GHz, τ_f =?–39.9?ppm/°C. Thus, it is considered to be a candidate material for the communication device applications at high frequency.     

Synthesis and characterization of calcium aluminate compounds from gehlenite by high-temperature solid-state reaction

The mineral transition mechanism and self-pulverization property of the sintered products in the Ca₂Al₂SiO₇-CaO system were systematically studied using pre-synthesized gehlenite determined by XRD, SEM, FTIR and particle size analyses. The minerals of Ca₁₂Al₁₄O₃₃, CaAl₂O₄, Ca₃SiO₅ and Ca₂SiO₄ are formed by the direct reactions of Ca₂Al₂SiO₇ with CaO. CaAl₂O₄ reacts with CaO to form Ca₁₂Al₁₄O₃₃ or Ca₃Al₂O₆, while Ca₃SiO₅ reacts with Ca₂Al₂SiO₇ to form Ca₂SiO₄ and calcium aluminate compounds. The sintered products mainly contain CaAl₂O₄, Ca₁₂Al₁₄O₃₃ and Ca₂SiO₄ at 1350?°C or above 1500?°C when the molar ratio of CaO to Al₂O₃ is 1.0. Increasing the sintering duration or the CaO consumption promotes the transition of Ca₂Al₂SiO₇ to Ca₂SiO₄ and calcium aluminate compounds when sintered at 1350?°C, which accordingly improves the self-pulverization property of the sintered products. The formed minerals of Ca₁₂Al₁₄O₃₃, CaAl₂O₄ and Ca₂SiO₄ transform into Ca₂Al₂SiO₇ again when the sintering temperature is between 1400?°C and 1450?°C, and the corresponding self-pulverization property of the sintered products deteriorates sharply.     

Effect of microwave sintering on the properties of copper oxide doped Y-TZP ceramics

The effect of various amounts of copper oxide (CuO) up to 1?wt% on the densification behaviour and mechanical properties of 3?mol% yttria-tetragonal zirconia polycrystal (Y-TZP) were studied by using microwave (MW) sintering method. The MW sintering was performed at temperatures between 1100?°C and 1400?°C, with a heating rate of 30?°C/min. and holding time of 5?min. The beneficial effect of MW in enhancing densification was also compared for the undoped and 0.2?wt% CuO-doped Y-TZP when subjected to conventional sintering (CS) method. The results showed that significant enhancement in the relative density and Vickers hardness were observed for the undoped Y-TZP when MW-sintered between 1100?°C and 1250?°C. It was revealed that the 0.2?wt% CuO-doped Y-TZP and MW sintered at 1250–1300?°C could attain ≥?99.8% of theoretical density, Vickers hardness of about 14.4?GPa, fracture toughness of 7.8 MPam^1/2 and exhibited fine equiaxed tetragonal grain size of below 0.25?µm. In contrast, the addition of 1?wt% CuO was detrimental and the samples exhibited about 50% monoclinic phase upon sintering coupled with poor bulk density and mechanical properties. The study also revealed that the addition of 0.2?wt% CuO and subjected to conventional sintering produced similar densification as that obtained for microwave sintering, thus indicating that the dopant played a more significant role than the sintering method.     

Preparation of nanocrystalline nickel oxide from nickel hydroxide using spark plasma sintering and inverse Hall-Petch related densification

Nanocrystalline nickel oxide (NiO) was prepared from nickel hydroxide by Spark plasma sintering (SPS) and the mechanisms involved in the densification of NiO were studied. Reverse precipitated nickel hydroxide powders were SPS processed at 400, 600 and 700?°C with 70?MPa pressure. Pure NiO with 12?nm crystallite size formed after 400?°C sintering process. However NiO grains had grown to 18 and 38?nm after 600 and 700?°C sintering respectively. NiO pellets prepared using 600 and 700?°C SPS sintering schedules had relative densities of 83% and 94% respectively. Two displacement rate regimes were observed during densification of NiO in both 600 and 700?°C sintering processes. Decomposition of nickel hydroxide and particle sliding of NiO led to first displacement rate maximum while inverse Hall-Petch based plastic deformation facilitated densification during the constant second displacement rate regime. No densification occurred during sintering holding times indicating the limited role that diffusion played during densification.     

Densification mechanism during reactive hot pressing of B4C-ZrO2 mixtures

The densification behaviors of pure B₄C and B₄C-ZrO₂ mixtures were compared during hot pressing. The results showed that in-situ formed ZrB₂ effectively enhanced the densification process of B₄C-ZrO₂ mixtures, more significantly during the intermediate stage. Within the relative density ranging from 0.75 to 0.90, the B₄C-15?wt%ZrO₂ mixture (B15Z) achieved the maximum densification rate as twice much as that of pure B₄C. The stress exponent n>3 indicated plastic deformation was the dominant densification mechanism of B15Z. The viscosities of plastic flow were evaluated using Murray-Rodger-William equation and the viscosity of B15Z was only a quarter of that in pure B₄C. The sintering activation energy was calculated to be 305.9?kJ/mol for pure B₄C and 197?kJ/mol for B15Z, respectively. It was proposed that the lower viscosity of plastic flow and activation energy accelerated the sliding and propagating motions of plastic flow, by which underlain the enhanced densification behaviors of B₄C-ZrO₂ mixtures.