采用实验观察和理论计算相结合研究经多向锻造后AZ80A镁合金等温退火过程中的显微组织演变与再结晶动力学。结果表明:经多向锻造后的AZ80A镁合金在150℃退火处理时,随着退火时间的延长,再结晶晶粒逐渐增多,退火时间为3600 s时,发生再结晶的体积分数约为88%;175℃退火时,合金在1800 s时已经发生了完全再结晶,且有部分晶粒发生长大;200℃退火时,合金在360 s时的再结晶体积分数约为70%,900 s时再结晶晶粒发生长大;250℃退火时,退火360 s后,再结晶晶粒已经发生了部分长大。利用Avrami再结晶动力学方程计算可得到多向锻造态AZ80A镁合金的再结晶激活能为71.48 kJ/mol,合金在150、175、200和250℃退火时再结晶完成的时间分别为4160、1387、485和85.6 s;计算结果与实验结果一致。     

润滑剂对高纯铝形变织构的影响

采用ODF法研究和分析了润滑剂对高纯铝冷轧形变织构的影响,揭示了两种润滑条件下形变织构的演变规律.结果表明大冷轧变形程度下,采用机油润滑,形变织构为典型的面心立方金属的轧制织构,即由强的B-、Cu-及S-织构组分构成,而且取向分布的密度峰值处在S-取向位置;煤油润滑时轧制织构相对较弱,但Cu织构最强,同时产生了明显的剪切织构{001}〈110〉(Rot.Cube-织构).采用机油润滑时,轧制变形比较均匀.低变形轧制时晶粒取向聚集于α线,随变形量增加,向β线取向聚集,最终形成铜型轧制织构;而煤油粘度小,轧制过程中接触表面摩擦系数较大,不均匀变形严重,低轧制程度时发现有表面剪切Rot.Cube-织构,随着塑性变形增加,Rot.Cube-织构逐渐向Cu-取向转化;变形至95%后,随着变形程度增加,S-织构减弱.     

Evolution of recrystallization textures in high voltage aluminum capacitor foils

1　ＩＮＴＲＯＤＵＣＴＩＯＮＴｈｅｃａｐａｃｉｔａｎｃｅｏｆｅｌｅｃｔｒｏｌｙｔｉｃｃａｐａｃｉｔｏｒｓｄｅｐｅｎｄｓｏｎｔｈｅｅｆｆｅｃｔｉｖｅｓｕｒｆａｃｅｏｆａｌｕｍｉｎｕｍｆｏｉｌｓｆｒｏｍｗｈｉｃｈｔｈｅｙａｒｅｍａｄｅ[1] .Ｔｈｅｅｆｆｅｃｔｉｖｅｓｕｒｆａｃｅｃａｎｂｅｇｒｅａｔｌｙｉｎｃｒｅａｓｅｄｂｙｕｐｔｏｔｗｏｏｒｄｅｒｓｏｆｍａｇｎｉｔｕｄｅｔｈｒｏｕｇｈａｎｅｔｃｈｉｎｇｐｒｏｃｅｓｓｔｈａｔｆｏｒｍｓｎａｒｒｏｗｃｈａｎｎｅｌｓａｌｏｎｇｔｈｅｃｒｙｓｔａｌｌｏｇｒａｐ…     

紫杂铜连铸连轧生产光亮铜杆工艺设计中熔炼设备的比选（续）

原风眼浸入需要的熔体深度,有利于氧化还原风在铜液内的扩散,氧化、还原充分;氧化还原介质的总流量及每个风眼的介质流量都是事先经过计算并精确控制的,避免象固定式反射炉的盲目性;炉底设有多套用于吹氮的透气砖,对熔体进行搅动和净化,使沉入熔池底部的大密度杂质上浮，提高精炼效率，避免扒渣死区集渣。     

挤压及时效对Mg-8Gd-4.8Y-0.4Zr合金显微组织及力学特性的影响

对Mg-8Gd-4.8Y-0.4Zr合金在不同挤压比下进行挤压,并在不同温度对挤压制得合金进行时效处理,通过透射电子显微镜(TEM)分析了挤压及时效后合金的微观组织。结果表明:合金在挤压过程中发生完全动态再结晶,合金内部分解出β″相,在峰时效时合金内部同时含有β′相与β″相;合金在380℃挤压时,挤压比增大,合金的强度与塑性均提高,在220℃时效21 h,合金的屈服强度最高。     

Continuous dynamic recrystallization and discontinuous dynamic recrystallization in 99.99% polycrystalline aluminum during hot compression

The dynamic restoration behavior of 99.99% polycrystalline aluminum was investigated. The deformation was carried out by compression test at 533 - 773 K and initial strain rate of 0. 002 - 2 s^-1 to a true strain of 1.0 followed by water quench. Polarized optical microscopy and transmission electron microscopy were applied to observe the deformation microstructure. It‘s found that discontinuous dynamic recrystallization, which is commonly observed in lower stacking fault energy metals or ultra-high purity aluminum(≥99.999%), occurs when Zenner-Hollomon parameter(Z parameter) is low, but the true stress strain curve doesn‘t accompany stress oscillation.Continuous dynamic recrystallization occurs when Z parameter is intermediate, and only dynamic recovery takes place if Z parameter is high.     

高应变率下纯钛动态压缩力学性能各向异性

利用Instron电子拉伸机和分离式霍普金生（SHPB）压杠实验装置,研究了准静态和动态压缩条件下织构多晶纯钛板TA2的力学性能,对织构多晶纯钛板法向ND、轧向RD、横向TD等三个方向进行了压缩实验,得到了不同应变率下的应力-应变曲线。结果表明对于轧制和退火纯钛板,准静态和动态压缩力学性能均表现出明显的各向异性,且规律一致：均为ND方向屈服强度最大,TD次之,RD方向最小。     

镁及镁合金阻尼特性的研究进展

综述了镁及镁合金阻尼特性的研究进展及阻尼镁合金材料的研究现状,介绍了其阻尼性能的评价方法,阐明了其阻尼机制符合G-L位错钉扎模型、基面(0001)上的位错脱钉运动是造成镁合金在室温具有高应变振幅阻尼性能的主要原因,概述了应变振幅、温度、变形工艺、热处理、晶粒尺寸和取向以及合金元素对镁合金阻尼性能的影响.     

影响双零铝箔力学性能因素的研究

采用化学分析、X射线衍射仪、光学显微镜、扫描电镜等手段研究了影响双零铝箔(0.006～0.007 mm厚)力学性能的各种因素.结果表明,当铝箔中Fe/Si比大于3.0时,随着Fe/Si比的增加,剩余的θ(FeAl3)相增加,这种针片状化合物对铝箔力学性能极为不利,铝箔的抗拉强度因此而下降;要提高铝箔的强度应使铝箔的组织均匀性提高,避免大颗粒化合物聚集,减小第二相化合物的尺寸,提高小尺寸化合物在化合物总体积中所占的体积分数.