聚酰亚胺摩擦学性能的研究

对热模压成型的聚酰亚胺(PI)试样在MHK-500型环-块摩擦试验机上测试了不同载荷P(N)、摩擦速度V(m·s-1)情况下,摩擦系数μ与摩擦持续时间t(min)的关系,并探讨了μ值随t,P,V变化的摩擦规律.结果表明V值增加,使第一阶段的μ峰值降低,峰值到来时间加快,峰宽变窄,第二阶段到来时间提前.而P值增加除了使μ峰值降低外,对第一、二阶段的其他参数的影响却相反.摩擦系数μ的表征值分别与P,V没有单值关系,而与单位面积所受的载荷P(MPa)和速度V的乘积pV值(MPa·m·s-1)具有指数关系.     

肉类加工用国产刀具的选材及其规范化

在调研、分析肉类加工用刀具市场供应品种中,发现国内目前制造肉刀所用材料很不规范,也不科学.讨论了肉类加工用斩拌机刀具材料选择时,不仅应考虑刀具的成本,还应考虑刀具磨损、腐蚀产物对肉质的影响.认为采用不锈工具钢制造斩拌机刀是合理的,并建议规范肉刀市场,以推动肉刀制造与使用的规范化与标准化.     

电铸铜微观组织与织构的研究

采用扫描电镜、透射电镜和电子背散射衍射技术,研究了不锈钢上厚度约2.2 mm的电铸铜层的微观组织、晶粒取向和晶界特征.实验表明,其组织主要由柱状晶构成,靠近基体50～100 μm处的铸层由细小等轴晶和细小柱状晶构成.对于所有晶区,小角度晶界(<15°)的分布频率较小,大角度(>15°)晶界为电铸铜组织的主要晶界,在大角度晶界中,CSL晶界占有很大比例,其中∑3的分布频率较大.柱状晶由平行分布的层状孪晶构成,近似垂直于柱状晶长轴,层间孪晶界为∑3类型.铸层存在较显著的铜型织构,即<111>择优取向,并且随铸层厚度的增加而加强.     

前处理工艺对Al-Zn-Mg-Cu合金ECAP的影响

研究了退火、固溶、双级时效以及回归（RRA）热处理4种前处理工艺对Al-Zn-Mg-Cu系铝合金多道次等径通道挤压（ECAP）变形过程的影响。试验结果表明,退火态试样在常温下只能进行2道次ECAP变形,而其余3种状态常温下经1次ECAP变形后便发生严重的开裂现象。退火处理后的试样采用523K温度加热可进行多次ECAP变形,挤压后晶粒明显细化且逐渐向等轴状演化。8道次之后晶粒细化趋于缓和,10道次后等效真应变达到了6．2,晶粒为0．8μm左右的等轴状。随着挤压道次的增加,试样显微硬度不断增大,且存在定量关系。     

前处理T艺对Al-Zn-Mg-Cu合金ECAP的影响

研究了退火、固溶、双级时效以及回归(RRA)热处理4种前处理工艺对Al-Zn-Mg-Cu系铝合金多道次等径通道挤压(ECAP)变形过程的影响.试验结果表明,退火态试样在常温下只能进行2道次ECAP变形,而其余3种状态常温下经1次ECAP变形后便发生严重的开裂现象.退火处理后的试样采用523 K温度加热可进行多次ECAP变形,挤压后晶粒明显细化且逐渐向等轴状演化.8道次之后晶粒细化趋于缓和,10道次后等效真应变达到了6.2,晶粒为O.8 μm左右的等轴状.随着挤压道次的增加,试样显微硬度不断增大,且存在定量关系.     

高强铝合金的化学镀镍镀层性能研究

对高强铝合金进行了化学镀镍,观察了镀层形貌,对镀后试样进行了不同温度的热处理以及耐热性能试验,研究结果表明:经该工艺处理后镀层胞状形貌明显,结构致密均匀,孔隙少,镀层光亮,结合力好。400℃以下化学镀层的硬度随热处理温度的升高而增大,400℃处理后,镀层与基体的界面元素扩散现象明显。镀层在一定温度下具有保护铝基体的作用,尤其在瞬时高温的条件下镀层的保护作用更加明显。     

Effects of heat treatment process on stress corrosion cracking and microstructures of 7A05 A1 alloy plate

In order to improve the stress corrosion cmcking（SCC） resistance of 7A05Al alloy, four different heat treatment processes were performed. After the heat treatments, the stress corrosion cracking resistance, mechanical properties and microstructures of 7A05Al alloys were studied. The results show that the retrogression and reaging（RRA） treated specimens possess the highest SCC resistance with slightly reduced strength compared with the other specimens. Thus RRA is the best process in terms of the optimal combination of SCC resistance and strength. Further TEM observation reveals that the RRA treated specimens are characterized by the fine equiaxed grains, dispersed second phase and wide PFZ. The pre-aging treated specimens show lower SCC resistance but higher strength as compared with the RRA treated ones. Equiaxed grains are also observed in the pre-aging treated samples by TEM, indicating that the anisotropy is eliminated. However, the dual aging and deformation plus aging treated specimens are demonstrated by large anisotropy.     

Si、Mn含量对中碳Cr-Ni-Mo钢力学性能的影响

研究了不同Si、Mn含量的2个炉号的中碳Cr-Ni-Mo钢淬火、高温回火后的显微组织和力学性能，提出了力学性能与化学成分的关系。找出了σ0.1与冲击吸收功Akv值的关系曲线。结果表明：较高Mn含量虽可使Akv值有所提高，但Akv值分布范围较大。     

超声波对聚氨酯泡沫塑料化学镀铜的影响

为了研究超声波对泡沫塑料化学镀铜的影响,比较了聚氨酯泡沫塑料在以Sn-Pd活化后直接加超声波进行化学镀铜以及在形成连续铜层的基础上施加超声波进行化学镀铜的效果.结果表明:直接在连续铜层上施加超声波不但可缩短镀铜诱导期,而且使镀速加快、施镀深度加大,并随超声波功率增加,铜层增重加快变缓.而在聚氨酯上未形成连续铜层前,在预处理以PdCl2敏化的基础上施加超声波,早期可将钯核震掉影响镀速,从而确定了施加超声波的时间至少在预镀5min后进行.     

含有纳米金刚石粉的化学复合镀层工艺研究

采用纳米金刚石分散混合液，制成的碱性化学复合镀Ni—P-纳米金刚石镀液。研究了镀液中纳米金刚石粉的含量对镀层组织、形貌的影响。结果表明，在采用的纳米佥刚石分散混合溶液，可使镀层中金刚石的含量高达12％～24％，每小时可获得11μm的镀层厚度。同时获得纳米金刚石含量较高、分布均匀的镀层，且镀层与基体的结合力良好。镀层结合力与镀液中全刚石的添加量关系影响不大。