Accelerating the decarbonization of carbonaceous gold ore by suspension oxidation roasting towards the improvement of gold leaching efficiency

Eliminating the gold preg-robbing effect of carbonaceous matter in carbonaceous gold ores is crucial for gold leaching. In this study, suspension oxidation roasting was proposed to accelerate the decarbonization of carbonaceous gold ore. The characteristics of oxidation reaction process and gas release were analyzed by TG-DTA-FTIR. The phase transformation and microstructure evolution of samples during roasting were analyzed by XRD, SEM and BET. The results show that the gold preg-robbing effect was eliminated after the gasification of carbonaceous matter, and the CaO generated by decomposition of carbonates can effectively capture the SO₂. After roasting for 75 min at 650 °C in a 20% O₂ atmosphere, the total carbon removal rate reached 99.42%, the distribution of exposed gold increased from 28.85% to 77.10% and the gold leaching efficiency increased from 4.55% to 84.83%. In addition, about 70% sulfur was mainly fixed in the roasted products in the form of sulfate. Therefore, the suspension oxidation roasting process is an efficient and clean pretreatment method for carbonaceous gold ores.     

井下硐室大爆破实践

酒钢镜铁山矿运用硐室大爆破处理山头岩体，以便为２号（中）矿体的开采形成良好的覆盖层。由于爆破设计合理，工程质量较好，达到了预期的目的。     

Ceramics composites from iron ore tailings and blast furnace slag

The search for materials and methods capable of reducing human impacts on the environment is of utmost importance nowadays. This study's primary purpose was to analyze the technical feasibility of ceramic composites production utilizing Fundão Dam's Iron Ore Tailings (IOT), Blast Furnace Slag (BFS) from charcoal, and Foundry Sand (FS) as partial substitutes for the traditional raw materials – sand and clay – for application in building industry materials. The composites were molded in rectangular specimens and fired at temperatures of 900, 950, 1000, 1050, and 1200 °C. The developed materials were analyzed and characterized by X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Energy Dispersive Spectroscopy (EDS), Thermogravimetry (TGA), and Differential Thermal Analysis (DTA). The obtained materials had flexural strength modulus of up to 12.19 MPa, water absorption ranging from 2 to 22%, linear shrinkage ranging from 0.02 to 6.50%, and apparent density ranging from 2.03 to 1.63 g/cm³. The study of the internal structure formation process revealed the formation of amorphous structures in the composites. The results demonstrated that these waste materials may be jointly used in construction materials, contributing to the reduction of natural resource extraction, besides enabling their correct disposal, minimizing environmental impacts, and improving the life quality of the surrounding communities.     

Nonlinearity in regulating the metal to insulator transition of ReNiO3 towards low temperature range

Among the existing material family of the correlated oxides, the rare earth nickelates (ReNiO₃) exhibit broadly adjustable metal to insulator transition (MIT) properties that enables correlated electronic applications, such as thermistors, thermochromics, and logical devices. Nevertheless, how to accurately control the critical temperature (T_MIT) of ReNiO₃ via the co-occupation of the rare-earth elements is yet worthy to be further explored. Herein, we demonstrate the non-linearity in adjusting the T_MIT of ReNiO₃ towards lower temperatures via introducing Pr co-occupation within ReNiO₃ (e.g., Pr_xNd_1-xNiO₃ and Pr_xSm_1-xNiO₃) as synthesized by KCl molten-salt assisted high oxygen pressure reaction approach. Although the T_MIT is effectively reduced via Pr substitution, it does not strictly follow a linear relationship, in particular, when there is large difference in the ionic radius of the co-occupation rare-earth elements. Furthermore, the most significant deviation in T_MIT from the expected linear relationship appears at an equal co-occupation ratio of the two different rare-earth elements, while the abruption in the variation of resistivity across T_MIT is also reduced. The present work highlights the importance to use adjacent rare-earth elements with co-occupation ratio away from 1:1 for achieving more linear adjustment in designing the metal to insulator transition properties for ReNiO₃.     

Environmentally Friendly Graphene Inks for Touch Screen Sensors

Graphene-based materials have attracted significant attention in many technological fields, but scaling up graphene-based technologies still faces substantial challenges. High-throughput top-down methods generally require hazardous, toxic, and high-boiling-point solvents. Here, an efficient and inexpensive strategy is proposed to produce graphene dispersions by liquid-phase exfoliation (LPE) through a combination of shear-mixing (SM) and tip sonication (TS) techniques, yielding highly concentrated graphene inks compatible with spray coating. The quality of graphene flakes (e.g., lateral size and thickness) and their concentration in the dispersions are compared using different spectroscopic and microscopy techniques. Several approaches (individual SM and TS, and their combination) are tested in three solvents (N-methyl-2-pyrrolidone, dimethylformamide, and cyrene). Interestingly, the combination of SM and TS in cyrene yields high-quality graphene dispersions, overcoming the environmental issues linked to the other two solvents. Starting from the cyrene dispersion, a graphene-based ink is prepared to spray-coat flexible electrodes and assemble a touch screen prototype. The electrodes feature a low sheet resistance (290 Ω □⁻¹) and high optical transmittance (78%), which provide the prototype with a high signal-to-noise ratio (14 dB) and multi-touch functionality (up to four simultaneous touches). These results illustrate a potential pathway toward the integration of LPE-graphene in commercial flexible electronics.     

Degradation mechanism of high alumina refractory bricks by reaction with deposits in a rotary kiln for fluxed iron ore pellets production

The formed deposits wear out of refractory wall linings in the rotary kiln and may cause production disturbances. This study describes the chemical composition and mineralogical phase components at the deposit/refractory interface in the rotary kiln for fluxed iron ore pellets production. The main phases of refractory bricks are corundum and mullite, while the deposits mainly contain hematite and silicates. The main phases in the deposit/refractory brick contact zone are hematite, anorthite (CaAl₂Si₂O₈), mullite, corundum, and silicates. Moreover, the hematite phases in the deposit/brick interface averagely contain 6.98 wt% Al and 1.38 wt% Ti. The silicates in the contact zone contain higher aluminium content and lower iron content than the silicates in the deposits. Finally, the thermodynamic analysis indicates that the main phases in the deposits can react with the refractory to form Al₂Fe₂O₆, CaAl₂Si₂O₈, feldspar, and liquid phases lead to the degradation of bricks in the kiln during the iron ore pellets production.     

蒸压建材生产过程中钢渣安定性处理与活性化利用

钢渣安定性处理过程常常造成胶凝活性的损失。为此，本文利用改性助剂消除钢渣水化过程中产生的氢氧化物并生成胶凝产物，在蒸压建材的生产过程中实现钢渣安定性处理和游离氧化物的活性化利用，并避免单独处置钢渣造成的活性物质损失。研究表明，8%秸秆灰和3%磷酸二氢铵作为复合助剂制备的尾矿-钢渣蒸压试块体积稳定，抗压强度达24.0MPa。通过对蒸压样品游离氧化物消解率、化学结合水量及热重、XRD分析，得出钢渣安定性处理与活性化利用机制：硅质材料与钢渣中f-CaO水化生成的Ca(OH)₂结合迅速生成对体系力学强度有益的水化硅酸钙，避免因大量Ca(OH)₂积累造成体积膨胀；磷酸盐中的NH₄⁺、H₂PO₄^-与f-MgO结合生成磷酸铵镁及其他低溶度积复盐类矿物，进而消除因f-MgO水化生成Mg(OH)₂造成体积膨胀的隐患。试样在180℃蒸压4h后，f-CaO及f-MgO消解率分别可达86.28%、89.73%。本文将为利用钢渣大比例取代水泥和石灰生产蒸压建筑材料提供理论基础，对于提高钢渣利用率、减少碳排放具有重要价值。     

安徽省铜陵市铁山头铜矿床地质特征及找矿潜力

铁山头铜矿床处于铜陵矿集区的中东部，属于扬子陆块下扬子凹陷中的铜陵隆起。矿床位于凤凰山矿田北侧，成矿潜力较大。综合研究分析认为：①接触交代作用使得岩体接触带及附近变质形成矽卡岩矿化带；②区内凤凰山岩体（花岗闪长岩）系成矿母岩；③矿体主要赋存于花岗闪长岩与三叠系下统南陵湖组石灰岩接触带上；④矿床成因类型为高—中温热液交代矽卡岩型矿床。     

臭氧氧化-循环喷淋法处理钨钼选矿废水

采用臭氧氧化-循环喷淋法去除钨钼选矿废水中COD,研究了pH值、臭氧流量、循环频率对COD去除效果的影响。结果表明: 废水COD去除率随pH值、臭氧流量、循环频率增大而增加,在pH值为10、臭氧流量3.0 L/min、循环频率4.0次/min条件下,氧化120 min后废水COD含量由131 mg/L降至11.5 mg/L,COD去除率达91.2%,满足《污水综合排放标准》(GB 8978-1996)一级标准。与O₂、NaClO处理废水COD的对比试验结果表明,循环喷淋法结合O₃表现出较好的COD去除效果。