NMMO法竹纤维拉伸强度的影响因素探讨

以竹浆粕为原料,N-甲基吗啉-N-氧化物(NMMO)水溶液为溶剂,没食子酸正丙酯为抗氧剂,采用湿法纺丝工艺制备竹纤维,讨论了竹浆粕的聚合度、纺丝原液的竹纤维素含量以及抗氧化剂添加量等因素对竹纤维拉伸强度的影响,并通过场发射扫描电子显微镜(FE-SEM)对竹纤维的表面微观形貌进行观察。结果表明:在竹纤维素质量分数为11%～15%、竹浆粕聚合度为450～950、抗氧剂质量分数0～0.5%的条件下,随着竹纤维素含量的增加、竹浆粕聚合度的增大和抗氧化剂添加量的增加,竹纤维的拉伸强度均呈上升趋势;FE-SEM观察发现竹纤维原纤化明显,表面出现明显的表面缺陷。     

Oxidation of Hastelloy-XR Alloy for Corrosion-Resistant Glass-Coating

The oxidation behavior of Hastelloy-XR alloy was investigated to obtain the optimum surface condition for corrosion-resistant glass-coatings. The surface morphology of oxide scales changed significantly with variation of temperatureand oxygen partial pressure (po2 ). The oxidation kinetics was mainly parabolic independent of oxidation conditions.The oxide scales were consisted of inner Cr2O3 and outer spinel layers. The phase component of spinel layers wereMn1.5Cr1.5O4 and (Mn,Ni)(Cr,Fe)2O4 for the oxygen partial pressures po2<10 kPa and po2>10 kPa, respectively.The optimum oxidation condition to obtain an oxide scale for well-adhered glass-coating to the substrate was 1248 Kand po2 =0.01 kPa for the oxidation time of 43 ks.     

循环伏安法在润滑油检测中的应用

介绍了循环伏安法的产生背景、原理。应用该技术可以快速、方便地对润滑油中抗氧剂、总酸（碱）值进行测定，并且可以对不同厂家润滑油的抗氧剂包进行区别。该技术还可以有效地评价润滑油的使用寿命和设备工作状况。     

几种酚类抗氧剂在润滑油中的应用

采用旋转氧弹法、高压差示扫描量热法等方法研究了5种酚类抗氧剂对6种润滑油基础油氧化安定性的改善效果。结果表明:向加氢基础油中加入0.25%(质量分数)抗氧剂2246-S和RHY510(含硫酚类抗氧剂),可使HVIWH125,HVIWH150,HVIWH500,KN4006,KN40105种润滑油基础油的诱导期由27～88min提高到226～397min;使HVIWH125,HVIWH150,HVIWH300,HVIWH500,KN4006,KN40106种润滑油基础油的起始氧化温度由193.34～198.90℃提高到205.48～230.27℃。     

阻尼胶囊的生产工艺研究

通过对胶料配方、工艺规程、模具结构的试验研究，成功地解决了胶囊制造过程中的难点问题。     

高性能大尺寸永磁体粘合强度的测定

介绍了一种用三点弯曲试验法测定高性能大尺寸粘接永磁体粘合强度的方法，及利用布氏硬度计的加载系统，实现100％检验粘接质量的方法。     

高性能粘合树脂

软性复合包装材料在食品、药品包装及其它领域中的应用已经有了50年的历史。除了共挤出复合工艺外,挤出复合工艺和干法复合工艺是生产这种材料的主要方法。但任何事情总有两重性,这两种工艺在某些方面存在明显的不足。例如,在挤出复合工艺中,LDPE与铝箔往往粘结不牢;而在干法复合工     

布帮鞋无浆贴合工艺技术

本工艺是对原有工艺的改进，突破了原有布帮鞋不能采用无浆贴合的局限性，对原有工艺中的不足有了很大的改进，提高了生产效率，改善了鞋子外观质量，增加了鞋子的美观性。