Phase and microstructure evolution of Sc2O3–CeO2 –ZrO2ceramics in Na2SO4 + V2O5 molten salts

In this study, the destabilization resistance of Sc₂O₃ and CeO₂ co-stabilized ZrO₂ (SCZ) ceramics was tested in Na₂SO₄ + V₂O₅ molten salts at 750°C–1100 °C. The phase structure and microstructure evolution of the samples during the hot corrosion testing were analyzed with X-ray diffraction (XRD), Raman spectra, scanning electron microscopy (SEM), energy dispersive X-ray spectrum (EDS), and X-ray photoelectron spectroscopy (XPS). Results showed that the destabilization of SCZ ceramics at 750 °C was the result of the chemical reaction with V₂O₅ to produce m-ZrO₂ and CeVO₄, and little ScVO₄ was detected in the Sc₂O₃-rich SCZ ceramics. The primary corrosion products at 900 °C and 1100 °C were CeO₂ and m-ZrO₂ due to the mineralization effect. The Sc₂O₃-rich SCZ ceramics exhibited excellent degradation resistance and phase stability owing to the enhanced bond strength and the decreased size misfit between Zr⁴⁺ and Sc³⁺. The destabilization mechanism of SCZ ceramic under hot corrosion was also discussed.     

Effect of Ge on microstructure and mechanical properties of Ti3SiC2/Al2O3 composites

Owing to the good physicochemical compatibility and complementary mechanical properties of Ti₃SiC₂ and Al₂O₃, Ti₃SiC₂/Al₂O₃ composites are considered as ideal structural materials. However, TiC and TiSi₂ typically coexist during the synthesis of Ti₃SiC₂/Al₂O₃ composites through an in-situ reaction, which adversely affects the mechanical properties of the resulting composites. In this study, Ti₃SiC₂/Al₂O₃ composites were prepared via in-situ hot pressing sintering at 1450 °C. Ge, which was used as a sintering aid, improved the purity and mechanical properties of the Ti₃SiC₂/Al₂O₃ composites. This is because Ge replaced some of the Si atoms to compensate the evaporation loss of Si to form Ti₃(Si_1-xGe_x)C₂, which showed a crystal structure similar to that of Ti₃SiC₂. Furthermore, the molten Ge accelerated the diffusion reaction of the raw materials, increasing the overall density of the Ti₃SiC₂/Al₂O₃ composites. The optimum Ge amount for improving the mechanical properties of the composites was found to be 0.3 mol. The flexural strength, fracture toughness, and microhardness of the composite with the optimum Ge amount were 640.2 MPa, 6.57 MPa m^1/2, and 16.21 GPa, respectively. The formation of Ti₃(Si_1-xGe_x)C₂ was confirmed by carrying out X-ray diffraction, energy dispersive spectroscopy, and transmission electron microscopy analyses. A model crystal structure of Ti₃(Si_1-xGe_x)C₂ doped with 0.3 mol Ge was established by calculating the solid solubility of Ge.     

辊速差对连铸连轧7075铝板显微组织、织构及力学性能的影响

研究辊速差对连铸连轧7075铝板显微组织、织构及力学性能的影响。采用3种不同上辊/下辊转速比(ω/ω0,ω为上辊转速,ω0为下辊转速)1:1、1:1.2及1:1.4进行多次试验。结果显示,在最大辊速差条件下(ω/ω0=1:1.4),7075铝板在轧制方向的屈服强度和极限抗拉强度分别提高41.5%和21.9%。此外,当辊速比ω/ω0为1:1.4时,成品轧制板的平均晶粒尺寸减小36%,横剖面平均硬度增加约9.2%。织构研究结果显示,辊速差越大,成品各向同性及硬度越大。然而,采用不同辊速度的连铸连轧会导致变形板伸长率降低约6%。     

Application of artificial neural network method to predict the breakage properties of PGE bearing chromite ore

In the present investigation, systematic grinding experiments were conducted in a laboratory ball mill to determine the breakage properties of low-grade PGE bearing chromite ore. The population balance modeling technique was used to study the breakage parameters such as primary breakage distribution (B_{i, j}) and the specific rates of breakage (S_i). The breakage and selection function values were determined for six feed sizes. The results stated that the breakage follows the first-order grinding kinetics for all the feed sizes. It was observed that the coarser feed sizes exhibit higher selection function values than the finer feed size. Further, an artificial neural network was used to predict breakage characteristics of low-grade PGE bearing chromite ore. The predicted results obtained from the neural network modeling were close to the experimental results with a correlation of determination R² = 0.99 for both product size and selection function.     

基于滚动摩擦作用下玉米颗粒在模拟筒仓卸料中的力链分析（网络首发、推荐阅读）

针对颗粒滚动摩擦作用对筒仓中玉米颗粒的力链空间分布进行研究，通过EDEM离散元软件建立筒仓模型与仿真玉米颗粒模型进行卸粮仿真模拟，并与筒仓卸料实验作流态对比，验证模型与仿真结果的准确性。通过对模拟仓进行切片观察和数据处理，对比分析了不同摩擦情况下力链的细观参数随时间演化规律。模拟结果表明：颗粒间摩擦系数越大，卸粮完成的最终时间越长；颗粒间滚动摩擦系数越小，颗粒由整体流转变为管状流的时间越早。对于有漏斗的筒仓来说，减小颗粒间摩擦会改变整体流和管状流之间的极限，从而增加产生管状流的面积。标准滚动摩擦系数下玉米颗粒在卸料过程中会出现起拱-塌陷效应；减小滚动摩擦，玉米颗粒卸料较稳定，未出现起拱的应力突增、以及拱塌陷的应力衰减；增大颗粒间滚动摩擦不但会增加拱效应，且出现成拱高度距离漏斗口更高。     

离线式带钢双面翻转检查站方案设计及实践

针对某酸轧机组检查站穿带困难、检查效率低、产生废品多、故障率高的问题,开发了一种离线式带钢双面检查站。该检查站新增了带钢翻转装置,将在入口分切剪处完成定尺剪切的带钢试样由两侧压板夹紧,中间可升降皮带机落下,翻转装置将带钢试样张紧,并翻转90°或者180°,实现带钢的双面检查。皮带机两侧布置有可升降、可横移的活动操作平台,检测人员站在平台上对带钢进行打磨检查,可同时对带钢上下表面进行检测。由于缩短了带钢的传输距离,有效减少了其他擦划伤的影响,提高了带钢表面质量检测准确性。     

Effect of spheroidized microstructure on the impact toughness and electrochemical performance of a high-carbon steel

The influence of cementite spheroidization on the impact toughness and electrochemical properties of a high-carbon steel has been thoroughly investigated in this study. Heavy warm rolling, followed by 2 h of annealing, has resulted in near-complete spheroidization, leading to a microstructure consisting of nano-cementite globules dispersed in the ultrafine-grained ferritic matrix. The Charpy impact test exhibited superior impact toughness with increased spheroidization. It is validated by the presence of abundant dimples in the fractographs of spheroidized specimens, in contrast to the as-received one that experienced a brittle failure due to its lamellar pearlitic structure. Potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) carried out in a 3.5% NaCl solution revealed that the corrosion resistance of the alloy gets improved with the increase in the degree of spheroidization. This is attributed to the lower susceptibility of the spheroidized specimen to microgalvanic corrosion owing to the minimum area of contact between nano-spheroidized cementite and ferrite, as elucidated with the help of EIS results aided by equivalent electrical circuit model.     

Non-additive sintering of Si2N2O ceramic with enhanced high-temperature strength,oxidation resistance,and dielectric properties

The high-temperature mechanical and dielectric properties of Si₂N₂O ceramics are often limited by the introduction of a sintering aid. Herein, dense Si₂N₂O was prepared at 1700 °C by hot-pressing oxidized amorphous Si₃N₄ powder without sintering additives. A homogeneous network with short-range order and a SiN₃O structure was formed in the oxidized amorphous Si₃N₄ powder during the hot-pressing process. Si₂N₂O crystals preferentially nucleated at positions within the SiN₃O structure and grew into rod-like and plate-like grains. Fully dense ceramics with mainly crystalline Si₂N₂O and some residual amorphous phases were obtained. The as-prepared Si₂N₂O possessed a good flexural strength of 311 ± 14.9 MPa at 1400 °C, oxidation resistance at 1500 °C, and a low dielectric loss tangent of less than 5 × 10⁻³ at 1000 °C.     

Densification and joining of a (HfTaZrNbTi)C high-entropy ceramic by hot pressing

A bulk (Hf_0.2Ta_0.2Zr_0.2Nb_0.2Ti_0.2)C high-entropy ceramic (HEC) with a high density was prepared by hot pressing (HP), and through a robust joining technique, large-sized piece was fabricated. A hot-pressed carbide HEC with a single-phase and homogeneous composition was obtained at the sintering temperatures from 1800 to 1950 °C for 30 min under a pressure of 30 MPa. The influence of sintering temperature on the mechanical properties of the HEC was investigated, and the flexural and compressive strengths were reported. Additionally, the feasibility of active brazing of this HEC was studied and solid joints with high shear strength were obtained by atomic diffusion and chemical reaction at the interface, providing a key approach to fabricate complex components of HECs.     

Improvement in the properties of low carbon MgO-C refractories through the addition of graphite-SiC micro-composite

Graphite–SiC micro-composites have been prepared in–house by carbothermal reduction process. Controlling the process parameters including the weight ratio of SiO₂ to graphite as well as carbothermal reduction temperature during the micro-composite preparation favors the homogeneous formation of SiC with preferred morphologies like ribbons and whiskers/fibers. The micro-composite modified low carbon MgO-C refractories have exhibited significantly improved bulk properties over the standard composition. To understand the beneficial role of SiC reinforcement on hot strength performance under air oxidizing conditions, we propose a scaling parameter known as strength factor (fs) based on the ratio of hot strength (HMOR) to cold strength (CCS). Correlating the strength factor data (fs) with oxidative damage provides new insights into the reinforcing effects of distinct SiC morphologies in this new class of micro-composite fortified refractory systems over the standard compositions.