Ceramics composites from iron ore tailings and blast furnace slag

The search for materials and methods capable of reducing human impacts on the environment is of utmost importance nowadays. This study's primary purpose was to analyze the technical feasibility of ceramic composites production utilizing Fundão Dam's Iron Ore Tailings (IOT), Blast Furnace Slag (BFS) from charcoal, and Foundry Sand (FS) as partial substitutes for the traditional raw materials – sand and clay – for application in building industry materials. The composites were molded in rectangular specimens and fired at temperatures of 900, 950, 1000, 1050, and 1200 °C. The developed materials were analyzed and characterized by X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Energy Dispersive Spectroscopy (EDS), Thermogravimetry (TGA), and Differential Thermal Analysis (DTA). The obtained materials had flexural strength modulus of up to 12.19 MPa, water absorption ranging from 2 to 22%, linear shrinkage ranging from 0.02 to 6.50%, and apparent density ranging from 2.03 to 1.63 g/cm³. The study of the internal structure formation process revealed the formation of amorphous structures in the composites. The results demonstrated that these waste materials may be jointly used in construction materials, contributing to the reduction of natural resource extraction, besides enabling their correct disposal, minimizing environmental impacts, and improving the life quality of the surrounding communities.     

钢混结构大型厂房整体式爆破拆除

采用整体式控制爆破拆除方案对华电扬州电厂钢筋混凝土框-排架结构厂房进行了爆破拆除。爆破前,对汽机房、厂房外墙和楼梯进行了预处理。将厂房划分为3个爆区,采用非电多回路网格式爆破网路,依靠东侧锅炉房倒塌施加在西侧锅炉房上的倾覆力矩,有效地克服了西侧锅炉房向西倒的难题,可为同类工程提供一定的参考。     

C105管桩混凝土设计参数取值的探讨

通过试验得出了C105混凝土100 mm×100 mm×100 mm立方体非标准试件抗压强度换算系数以及C105混凝土的标准方差和强度变异系数。采用理论计算,得到了棱柱体抗压强度与立方体抗压强度的比值α_c1,并与试验实测平均值进行了比较,验证了理论计算方法的可行性。此外,通过对比分析,探讨了直接外延法和引用公式法两种C105混凝土设计参数计算方法的正确性,研究结果可为C105管桩混凝土的设计和应用提供参考。     

Evaluation of back-calculated elastic moduli of unreinforced and geocell-reinforced unbound granular material from full-scale field tests

This paper presents a field-scale experimental track over a poor subgrade with an unreinforced section and a geocell-reinforced section subjected to in-situ performance tests. Plate load tests and Benkelman beam tests were carried out distributed in several unreinforced and reinforced layers. The objective was to: (1) examine the variability of the elastic modulus of unbound granular material (UGM) due the influence of its thickness and the presence of poor subgrade in its base, (2) evaluate the modulus improvement factor (MIF) generated by the geocell reinforcement in the UGM and (3) verify the most appropriate condition to apply the MIF to transport infrastructure design. The results showed that there is a significant influence of the thickness of the UGM layer on its elastic modulus when the layer is supported directly over a soft subgrade. The MIF values obtained in field suggest that its determination is mostly related to the UGM maximum elastic modulus rather than its decreased values (by virtue of poor subgrade or reduced thicknesses), and that the analytical formulation presented for MIF calculation has good predictive capability to be applied to pavement design.     

混凝土结构的压电声波检测分析

本文介绍了混凝土结构的压电体波和表面波检测的主要进展,对两种压电声波检测的优缺点进行了总结。体波检测设备一般埋入混凝土内部,需要选择合理的检测部位,检测结果较为精确;声表面波检测无需选择特定的部位,但是检测深度有限。在实际检测工作过程中,可以联合两种方法相互验证。     

Chromium-promoted preparation of forsterite refractory materials from ferronickel slag by microwave sintering

The chromium-promoted preparation of forsterite refractory materials from ferronickel slag was investigated by microwave sintering of the slag with the additions of sintered magnesia and 0–10 wt% chromium oxide (Cr₂O₃). The thermodynamic calculations revealed that the addition of Cr₂O₃ can promote the formations of spinel and liquid phase and maintain high content of forsterite below 1500 °C. The experimental results showed that there existed a stronger promoting effect of Cr₂O₃ additive on the properties of refractory materials in the microwave field than that in conventional sintering. It was attributed to the preferential formation and growth of spinel with stronger microwave absorption than other phases (e.g., enstatite), the existence of more forsterite, and the enhanced densification in association with the presence of more liquid phase at the same temperature. By microwave sintering of the mixture of ferronickel slag, 25 wt% sintered magnesia, and 4 wt% Cr₂O₃ at 1350 °C for 20 min, a superior refractory material with refractoriness of 1801 °C, thermal shock resistance of 6 times, bulk density of 2.97 g/cm³, apparent porosity of 1.4%, and compressive strength of 197 MPa was obtained. Compared with that prepared by conventional sintering at 1350 °C for 2 h, the refractoriness and thermal shock resistance were increased by 175 °C and 100%, respectively. The present study provided a novel method for preparing high-quality refractory materials from ferronickel slag and relevant industrial wastes.     

Lithiophilic MXene-Guided Lithium Metal Nucleation and Growth Behavior

The positive effects of a lithiophilic substrate on the electrochemical performance of lithium metal anodes are confirmed in several reports, while the understanding of lithiophilic substrate-guided lithium metal nucleation and growth behavior is still insufficient. In this study, the effect of a lithiophilic surface on lithium metal nucleation and growth behaviors is investigated using a large-area Ti₃C₂T_x MXene substrate with a large number of oxygen and fluorine dual heteroatoms. The use of the MXene substrate results in a high lithium-ion concentration as well as the formation of uniform solid–electrolyte-interface (SEI) layers on the lithiophilic surface. The solid–solid interface (MXene-SEI layer) significantly affects the surface tension of the deposited lithium metal nuclei as well as the nucleation overpotential, resulting in the formation of uniformly dispersed lithium nanoparticles ( ≈ 10–20 nm in diameter) over the entire MXene surface. The primary lithium nanoparticles preferentially coalesce and agglomerate into larger secondary particles while retaining their primary particle shapes. Subsequently, they form close-packed structures, resulting in a dense metal layer composed of particle-by-particle microstructures. This distinctive lithium metal deposition behavior leads to highly reversible cycling performance with high Columbic efficiencies >  99.0% and long cycle lives of over 1000 cycles.     

Direct View on the Origin of High Li+ Transfer Impedance in All-Solid-State Battery

Large interfacial resistance plays a dominant role in the performance of all-solid-state lithium-ion batteries. However, the mechanism of interfacial resistance has been under debate. Here, the Li⁺ transport at the interfacial region is investigated to reveal the origin of the high Li⁺ transfer impedance in a LiCoO₂(LCO)/LiPON/Pt all-solid-state battery. Both an unexpected nanocrystalline layer and a structurally disordered transition layer are discovered to be inherent to the LCO/LiPON interface. Under electrochemical conditions, the nanocrystalline layer with insufficient electrochemical stability leads to the introduction of voids during electrochemical cycles, which is the origin of the high Li⁺ transfer impedance at solid electrolyte-electrode interfaces. In addition, at relatively low temperatures, the oxygen vacancies migration in the transition layer results in the formation of Co₃O₄ nanocrystalline layer with nanovoids, which contributes to the high Li⁺ transfer impedance. This work sheds light on the mechanism for the high interfacial resistance and promotes overcoming the interfacial issues in all-solid-state batteries.     

Nido-Hydroborate-Based Electrolytes for All-Solid-State Lithium Batteries

Hydroborate-based solid electrolytes have recently been successfully employed in high voltage, room temperature all-solid-state sodium batteries. The transfer to analogous lithium systems has failed up to now due to the lower conductivity of the corresponding lithium compounds and their high cost. Here LiB₁₁H₁₄ nido-hydroborate as a cost-effective building block and its high-purity synthesis is introduced. The crystal structures of anhydrous LiB₁₁H₁₄ as well as of LiB₁₁H₁₄-based mixed-anion solid electrolytes are solved and high ionic conductivities of 1.1 × 10⁻⁴ S cm⁻¹ for Li₂(B₁₁H₁₄)(CB₁₁H₁₂) and 1.1 × 10⁻³ S cm⁻¹ for Li₃(B₁₁H₁₄)(CB₉H₁₀)₂ are obtained, respectively. LiB₁₁H₁₄ exhibits an oxidative stability limit of 2.6 V versus Li⁺/Li and the proposed decomposition products are discussed based on density functional theory calculations. Strategies are discussed to improve the stability of these compounds by modifying the chemical structure of the nido-hydroborate cage. Galvanostatic cycling in symmetric cells with two lithium metal electrodes shows a small overpotential increase from 22.5 to 30 mV after 620 h (up to 0.5 mAh cm⁻²), demonstrating that the electrolyte is compatible with metallic anodes. Finally, the Li₂(B₁₁H₁₄)(CB₁₁H₁₂)  electrolyte is employed in a proof-of-concept half cell with a TiS₂ cathode with a capacity retention of 82% after 150 cycles at C/5.