Qualitative analysis of PZT (52/48) MPB using different synthesis methods

The current work reports a comparison between the structural and optical attributes of PZT (52/48) powder and thin film prepared via solid-state reaction and sol-gel spin-coating technique, respectively. The two obtained PZT samples, PZT-I corresponding to powder which was calcined at 875°C for 2 h, and PZT-II corresponding to a thin film which was annealed at 650°C for 2 h, were investigated via X-Ray Diffraction, Raman Spectroscopy, UV–Vis Spectroscopy, and SEM analysis. The diffraction spectra suggested the creation of a polycrystalline perovskite structure in both the samples. The optical band gap was evaluated using Tauc's relation. The bandgap values were found to be 3.2 eV for PZT-I and 3.87 eV for PZT-II. The bandgap values are significantly different for the PZT materials prepared by the two different methods.     

UV curing-assisted 3D plotting of ceramic feedstock containing thermo-regulated phase-separable,photocurable vehicle for dual-scale porosity structure

We propose a novel approach for manufacturing dual-scale porosity alumina structures by UV curing-assisted 3D plotting of a specially formulated alumina feedstock using a thermo-regulated phase separable, photocurable camphene/triethylene glycol dimethacrylate (TEGDMA) vehicle. In particular, 3D plotting process was conducted at - 5 °C, and thus an alumina suspension prepared using liquid camphene/TEGDMA at room temperature could undergo phase separation, resulting in camphene crystals surrounded by walls comprised of liquid photopolymer enclosing alumina particles. To enhance the shape retention ability of extruded filaments, polystyrene (PS) polymer was used as the tackifier. The phase-separated feedrod could be extruded favorably through a nozzle and rapidly photopolymerized by UV light during the 3D plotting process. Three-dimensionally interconnected macropores were tightly constructed, which were separated by microporous alumina filaments, where micropores were created by the removal of camphene crystals via freeze-dying. The macroporosity of porous alumina ceramics was controlled by adjusting the distance between deposited filaments, while their microporosity was kept constant, leading to tightly tailored overall porosity and mechanical properties.     

UV-enhanced conductive and dielectric properties in KTN crystal

We observe enhancements of both conductive and dielectric properties under UV illumination by using a ferroelectric absorber, potassium tantalate niobate (KTa_1-xNb_xO₃, KTN). The UV-generated electron-hole pairs weaken the intrinsic ferroelectric polarization while enhance the conductive property. The UV-induced heat effect causes the enhancement of the dielectric property. The results are further confirmed by the maximal rectification ratio which shows an opposite trend between the direct heating process and the UV illumination. Our results are useful for better understanding of ferroelectric properties under UV illumination and the development of new optoelectronic devices.     

Synthesis and spectroscopic studies of some new azobenzenesulfonamide

Abstract

Diazotized sulfadiazine derivative (1) was coupled with some nitrogen heterocyclic namely (thiazolone derivatives 2a–c, thiazole derivatives 4a–c and barbituric acid derivatives 6a,b) to give the corresponding azo compounds 3a–c, 5a–c and 7a,b in good yields. The newly synthesized azo benzene sulfonamide dyes were recorded their UV visible spectra in the region 200–600?nm in four different solvents and discussed the effect of solvents, substituent and effect of acid and base on the absorption values of these dyes.     

Solution processed,vertically aligned,AZO nanocolumn array for chemiresistive sensor application with UV-enhanced sensitivity

In this work, a wide and highly sensitive chemiresistive sensor has been developed based on the AZO nanocolumn array film. This is meant for the room detection of H₂O₂ under UV illumination. A cost-effective one step multi-layers growth process was adopted for the synthesis of the AZO nanocolumn array. The experimental studies were done by scanning electron microscopy (SEM), transmission and electron microscopy (TEM).Then X-ray diffraction confirmed that the AZO column array was closely packed, connected, vertically aligned, and polycrystalline, with a high surface area. This structure ensures better electrical conduction over random and separated nanostructures. The hall-effect measurement indicates that the AZO film was n-type, with high conductivity (3.60 × 10³ Ωcm), high carrier density (11.3 × 10²⁰cm⁻³) and with acceptable mobility (0.95 cm²/Vs). The x-ray photoemission spectroscopy suggests that the AZO film consists of a large amount of adsorbed oxygen-related species at the sheath layer of the thin-film, which is vital for sensors. By the UV light activation, sensors based on the AZO nanocolumn array exhibited enhanced H₂O₂ detection properties at room temperature. At a concentration from 15 μM to 30 mM, H₂O₂ sensitivity evaluated by relative response was remarkably increased from 15% to 36%. The operation under ambient conditions and wide range sensing shows that this chemiresistive AZO sensor is adequate for biomedical and environmental applications.