Melting process and melt structure of fly ash/magnesium slag blends for the production of inorganic fibers

Fiber production from inorganic industrial solid wastes is an effective waste management strategy. Because of cost considerations, most enterprises generally use local solid wastes as raw materials to produce fibers. In this study, we explored the feasibility of producing fibers using fly ash and magnesium slag. The results show that the melting temperature of the blends composed of fly ash, magnesium slag, and a small amount of calcined dolomite first decreased and then increased with an increase in acidity coefficient (M_k) from 1.0 to 2.4_. The samples could form a eutectic system in the M_k range of 1.4–1.8, and therefore have a relatively low melting temperature in this M_k range. Fly ash could react with magnesium slag and calcined dolomite to form akermanite, gehlenite-magnesium, and anorthite at temperatures close to the melting temperature; therefore, these crystalline phases were the main reaction products formed in the samples with M_k values lower than 1.80. Anorthite reacted further with some Na-containing and Si-containing spieces to produce labradorite. Thus, the content of anorthite and labradorite rapidly increased and they became the major crystal phases in the blend samples with M_k values greater than 1.80. MAS-NMR spectroscopic analysis revealed that the network structure of the melts depended on the ratio of bridging oxygen to non-bridging oxygen; a high ratio of bridging oxygen to non-bridging oxygen could lead to the formation of a dense network structure in the melt. The blends of fly ash and magnesium slag can be used to produce wool fibers and continuous fibers. In addition, the suitable temperature ranges for the production of both types of fibers were determined. The drawing temperature for continuous fiber production depended on the degree of polymerization and structure of the melt.     

虚实结合的可穿戴产品适合性检验研究

目的 为了更科学地研究和检验可穿戴产品的适合性,提出一种适合性检验方法,能够精确保留现实环境中的产品佩戴关系,并能将现实与虚拟的适合性检验研究相结合,得到合理的适合性检验结果.方法 以虚拟现实眼镜的适合性检验为例,通过高精度的三维测量技术将现实环境中的人、产品以及人—产品佩戴关系转化为三维虚拟信息,并以人—产品佩戴三维模型为参考基准对齐人和产品的虚拟模型,得到保留现实佩戴关系的人—产品佩戴模型组,再应用偏差分析法得出人—机佩戴区域的可视化适合性结果和统计数据,结合主观评价方法进一步分析产品的适合性.结论 虚实结合的产品适合性检验方法可在虚拟环境中高精度地保留现实环境中的人—产品佩戴关系,并能得到可视化的适合性检验结果,为检验和指导产品的适合性提供依据.     

Influence of temperature on acoustic emission source location accuracy in underground structure

An acoustic emission (AE) experiment was carried out to explore the AE location accuracy influenced by temperature. A hollow hemispherical specimen was used to simulate common underground structures. In the process of heating with the flame, the pulse signal of constant frequency was stimulated as an AE source. Then AE signals received by each sensor were collected and used for comparing localization accuracy at different temperatures. Results show that location errors of AE keep the same phenomenon in the early and middle heating stages. In the later stage of heating, location errors of AE increase sharply due to the appearance of cracks. This provides some beneficial suggestions on decreasing location errors of structural cracks caused by temperature and improves the ability of underground structure disaster prevention and control.     

不同盐沼湿地类型脱氮除磷效能及影响因素分析

采用沉水植物表面流湿地(沉水组)、挺水植物表面流湿地(挺水组)和浮床湿地(浮床组)3种盐沼湿地对长江口近岸低污染水体进行脱氮除磷效能的研究。结果表明,HRT为3 d时,水组、挺水组、浮床组对NO3^--N的去除率在高温时段分别为79.9%±13.2%、71.8%±15.2%、77.2%±13.2%,中温时段分别为39.4%±13.7%、31.5%±8.5%、18.4%±16.6%,低温时段分别为15.6%±14.6%、19.7%±8.6%、2.%5±8.6%。沉水组和挺水组对TP的去除率受温度影响较小,分别为66.4%±32.4%、55.5%±29.4%;而浮床组除磷效果受温度影响较大。当HRT缩短为1.5 d时,3组湿地系统在高温时段仍可达到相近的脱氮除磷效果,在中低温时段脱氮除磷效果都有不同程度的下降。     

一种新型的室温快速固化胶黏剂的研制

本文开发了一种新型的方舱夹芯板用室温固化高强度环氧结构胶黏剂,验证了其物化特性、相关力学性能和环境适应性。结果表明此胶黏剂具有优良性能,可以满足方舱用大板胶黏剂的使用需求。     

Thiol-Functionalized Covalent Organic Frameworks as Thermal History Indictor for Temperature and Time History Monitoring

Various products, including foods and pharmaceuticals, are sensitive to temperature fluctuations. Thus, temperature monitoring during production, transportation, and storage is critical. Facile indicators are required to monitor temperature conditions via color changes in real time. This study aimed to prepare and apply thiol-functionalized covalent organic frameworks (COFs) as a novel indicator for monitoring thermal history and temperature abuse. The COFs underwent obvious color changes from bright yellow to purple after exposure to different temperatures for varying durations. The reaction kinetics are analyzed under isothermal conditions, which reveal that the order of reaction rates is k_−20°C < k_4°C < k_20°C < k_35°C < k_55°C. The activation energy (E_a) of the COFs is calculated using the Arrhenius equation as 50.71 kJ moL⁻¹. The COFs are capable of sensitive color changes and offer a broad temperature tracking range, thereby demonstrating their application potential for the monitoring of temperature and time exposure history during production, transportation, and storage. This excellent performance thermal history indicator also shows promise for expanding the application field of COFs.     

Superior Low-Temperature Reversible Adhesion Based on Bio-Inspired Microfibrillar Adhesives Fabricated by Phenyl Containing Polydimethylsiloxane Elastomers

Gecko-inspired microfibrillar adhesives have achieved great progress in microstructure design and adhesion improvement over the past two decades. Space applications nowadays show great interest in this material for the characteristics of reversible adhesion and universal van der Waals interactions. However, the impact of harsh environment of space on the performance of microfibrillar adhesives, especially the extreme low temperature, is rarely addressed. Herein, microfibrillar adhesives fabricated by phenyl containing polydimethylsiloxane (p-PDMS) elastomers with superior low-temperature reversible adhesion is proposed. p-PDMS elastomers are synthesized through one-pot anionic ring-opening copolymerization, and the resulting elastomers become non-crystallizable with excellent low-temperature elasticity. Low-temperature adhesion tests demonstrate that the adhesion strength of microfibrillar adhesives fabricated by p-PDMS elastomers can be well maintained to as low as −120 °C. In contrast, the adhesion strength of pure PDMS microfibrillar adhesive reduces more than 50% below its crystallization temperature. The low-temperature cyclic adhesion tests further demonstrate that p-PDMS microfibrillar adhesives exhibit superior reversible adhesion compared to that of PDMS microfibrillar adhesives, owing to the sustainable conformal contact and even distribution of loads over repeated cycles. This study provides a new fabrication strategy for microfibrillar adhesives, and is beneficial for the practical application of microfibrillar adhesives.     

New insight into subcritical rupture of SiC-based filaments at intermediate temperatures (400–900 °C) under air

The delayed failure of SiC fibrous reinforcement has continuously been investigated to warrant the long term performances of Ceramic Matrix Composite (CMC). Chiefly assessed on multifilament tow samples to alleviate some handling difficulties, subcritical crack growth (SCG) parameters are however ruled by structural artifacts which hinder the identification of intrinsic filament behavior. In this paper, we propose to estimate the true filament parameters for 5 fiber types from bundle behavior using a recently communicated Monte Carlo algorithm integrating flaw and stress distributions through a deterministic fracture mechanics law under Paris’ formulation. So computed tow lifetime are broadly dispersed, encompassing raw data, and show a structure-dependent scale effect, revealed by n_filament>n_tow where n is the stress exponent. The relationship between SCG coefficient and chemical composition of the substrate is discussed and highlights the major effect of doping elements (Ti or Zr), oxygen or hydrogen content.